应变速率对增强成形性双相钢性能影响分析

doi:10.13228/j.boyuan.issn0449-749x.20210619

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (3669 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The microstructure of dual phase steel with high formability increases retained austenite compared with traditional dual phase steel, which shows a certain TRIP effect and better formability, so it is widely used for safety structural parts of vehicle body with complex shape. In order to study the effect of strain rate on the mechanical characteristics and microstructure changes of dual phase steel with high formability HC440/780DHD+Z, the strain rate properties of 7 different strain rates of 0.001, 0.1, 1, 10, 100, 200 and 500 s^-1 were tested universal testing machine and hydraulic servo high-speed tensile testing equipment to obtain the variation laws of strength, elongation and plastic product. The fracture morphology of the sample under different strain rates was observed and analyzed, and the variation law of dimple morphology and size affected by strain rate was obtained. The content of retained austenite at the fracture of samples with different strain rates was measured quantitatively, and the relationship between retained austenite and strain rate was obtained. Based on the above analysis, the effects of strain rate on material properties and microstructure were analyzed. The results show that, HC440/780DHD+Z has a certain strain rate sensitivity. The strength, elongation after fracture and strong plastic product of the material show positive strain rate sensitivity, which increases with the increase of strain rate. With the increase of strain rate, the dimple size of the material increases obviously, and the energy absorption ability of the material also increases gradually. Due to the transformation of retained austenite, plastic strengthening occurs in the deformation area, which promotes the deformation of other areas, and then increases the deformation uniformity in the process of plastic deformation, so that the material has better elongation. Therefore, with the increase of strain rate, the transformation amount of retained austenite increases, and the material shows better ductility.

Key words： strain rate dual phase steel with high formability fracture morphology retained austenite susceptibility

Received: 10 October 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Wei
	PAN Yue
	LIU Hua-sai
	LI Chun-guang
	CHEN Hong-sheng

Cite this article:

ZHANG Wei,PAN Yue,LIU Hua-sai等. Effect of strain rate on properties of dual phase steel with high formability[J]. Iron and Steel, 2022, 57(4): 123-129.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210619 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I4/123

[1] 王卫卫, 刘浏, 李光瀛. 冷轧双相钢中残余奥氏体稳定性的研究[J]. 轧钢, 2019, 36(2):31.(WANG Wei-wei, LIU Liu, LI Guang-ying. Study on the stability of retained austenite in cold rolled dual-phase steel[J]. Steel Rolling, 2019, 36(2):31.)
[2] 李靖, 关军, 任志超, 等. 高强双相钢DP1180的平整轧制[J]. 中国冶金, 2020, 30(8): 74. (LI Jing, GUAN Jun, REN Zhi-chao, et al. Skin pass rolling of high strength steel DP1180[J]. China Metallurgy, 2020, 30(8): 74.)
[3] 李润昌,张环宇,夏银峰,等. 980 MPa级双相钢边裂致断带原因分析[J]. 中国冶金, 2018, 28(9): 37. (LI Run-chang, ZHANG Huan-yu, XIA Yin-feng, et al. Reasons analysis of edge cracks on 980 MPa level dual-phase steel strip leading to stripbreak[J]. China Metallurgy, 2018, 28(9): 37.)
[4] 罗小兵, 朱飞, 杨才福, 等. 纳米粒子强化含铜双相钢的组织性能关系[J]. 钢铁, 2021, 56(9): 118. (LUO Xiao-bing, ZHU Fei, YANG Cai-fu, et al. Relationships between microstructure and mechanical properties in dual-phase Cu-bearing steel strengthened by nano sized precipitates[J]. Iron and Steel, 2021, 56(9): 118.)
[5] 杨杰, 姚海明, 吕浩, 等. 汽车用双相钢铸坯成分偏析的研究[J]. 连铸, 2021 (1): 1. (YANG Jie, YAO Hai-ming, LÜ Hao, et al. Research of slab segregation of dual phase steel for automobiles[J]. Continuous Casting, 2021 (1): 1.)
[6] 董丹阳, 刘杨, 王磊,等. 应变速率对DP780钢动态拉伸变形行为的影响[J]. 金属学报, 2013, 49(2):159.(DONG Dan-yang, LIU Yang, WANG Lei, et al. Effect of strain rate on dynamic deformation behavior of DP780 steel[J]. Acta Metallurgica Sinica, 2013, 49(2):159.)
[7] 王云瞾. 应变方式及速率对TRIP780钢板组织与力学性能影响的研究[D]. 长春:吉林大学, 2016.(WANG Yun-zhao. Research on the effect of strain modes and strain rates on microstructures and mechanical properties of TRIP780 steel sheet[D].Changchun: Jilin University,2016.)
[8] Madivala M, Schwedt A, Prahl U, et al. Anisotropy and strain rate effects on the failure behavior of TWIP steel: A multiscale experimental study[J]. International Journal of Plasticity, 2019, 115(4): 178.
[9] 王文平, 万敏, 吴向东,等. 典型汽车用钢板应变速率敏感性实验[J]. 塑性工程学报, 2012, 19(6):84.(WANG Wen-ping, WAN Min, WU Xiang-dong, et al. Experimental research on strain rate sensitivity of automotive steel sheet[J]. Journal of Plasticity Engineering, 2012, 19(6):84.)
[10] 王俊峰, 何煜天. DH780钢的热变形行为及热加工图[J]. 金属热处理, 2020, 45(6): 114.(WANG Jun-feng, HE Yü-tian. Hot deformation behavior and hot processing map of DH780 steel[J]. Heat Treatment of Metals, 2020, 45(6): 114.)
[11] 全国钢标准化技术委员会.GB/T 30069.2—2016 金属材料高应变速率拉伸试验第2部分:液压伺服型与其他类型试验系统[S].北京:中国标准出版社, 2016.(National Technical Committee on Steel of Standardization Administration. GB/T 30069.2—2016 Metallic Material-Tensile Testing at High Strain Rates—Part 2: Servo-Hydraulic and Other test Systems[S].Beijing: Standards Press of China, 2016.)
[12] 孟宪明, 谢书港, 方锐,等. B340-590DP双相高强钢板的动态变形行为[J]. 钢铁研究学报, 2015, 27(6):51.(MENG Xian-ming, XIE Shu-gang, FANG Rui, et al. Dy-namic deformation behavior of B340-590DP steel sheet[J]. Journal of Iron and Steel Research, 2015, 27(6):51.)
[13] 高永亮, 胡士廉, 陈巍,等. 高应变速率拉伸条件下TWIP钢动态力学性能与组织演变规律的研究[J]. 热加工工艺, 2019, 48(16):56.(GAO Yong-liang, HU Shi-lian, CHEN Wei, et al. Research on dynamic mechanical behavior and microstructure evolution rule of TWIP steel under high strain rate tensile condition[J]. Hot Working Technology, 2019, 48(16):56.)
[14] 王鑫,李彬周,王军生,等.化学成分对Bi系易切削钢低温冲击韧性的影响[J].上海金属,2021,43(6):25.(WANG Xin,LI Bin-zhou,WANG Jun-sheng, et al. Effect of chemical composition on low temperature impact toughness of Bi-series free-cutting steels[J].Shanghai Metals, 2021,43(6):25.)
[15] 钦祥斗, 刘铮, 李建宾, 等. 30MnVS非调质汽车用钢高温塑性研究[J]. 连铸, 2020 (1): 56. (QIN Xiang-dou, LIU Zheng, LI Jian-bin, et al. High temperature plasticity study of 30MnVS non-tempered automotive steel[J]. Continuous Casting, 2020 (1): 56.)
[16] 方少华. 中温卷取工艺下热轧双相钢组织性能研究[J]. 轧钢, 2020, 37(3): 18. (FANG Shao-hua. Study on the microstructure and properties of hot rolled dual-phase steel under medium temperature coiling process[J]. Steel Rolling, 2020, 37(3): 18.)
[17] 李春光, 张伟, 刘立现,等. 不同应变速率双相高强钢动态力学行为微观机理分析[J]. 锻压技术, 2018, 43(6):166.(LI Chun-guang, ZHANG Wei, LIU Li-xian, et al. Analysis on micro-mechanism of dynamic mechanical behavior for high-strength steel with dual-phase under different strain rates[J]. Forging and Stamping Technology, 2018, 43(6):166.)
[18] 于鸿垚, 刘珍君, 王凯, 等. 金属拉伸试验引起的应变速率脆性[J]. 钢铁研究学报, 2015, 27(3):45.(YU Hong-yao, LIU Zhen-jun, WANG Kai, et al. Strain rate embrittlement of metal induced by tensile test[J]. Journal of Iron and Steel Research, 2015, 27(3):45.)
[19] 苏崇涛, 郭晓静, 左海霞,等. 冷轧双相钢显微组织检测与分析[J]. 物理测试, 2020, 38(2):20.(SU Chong-tao, GUO Xiao-jing, ZUO Hai-xia, et al. Detection and analysis of microstructure of cold rolled dual phase steel[J]. Physics Examination and Testing, 2020, 38(2):20.)
[20] 罗兴壮, 罗庆革, 杨剑洪, 等. 低镍奥氏体不锈钢冷轧边裂原因分析[J]. 轧钢, 2021, 38(4): 89. (LUO Xing-zhuang, LUO Qing-ge, YANG Jian-hong, et al. Cause analysis of edge crack of low nickel austenitic stainless steel strip during cold rolling[J].China Rolling,2021, 38(4): 89.)
[21] 郑宏光, 刘华松. 铸态奥氏体晶粒粗化与热装再加热中晶粒的演化[J]. 连铸, 2020 (2): 45. (ZHENG Hong-guang, LIU Hua-song. Grain coarsening of As-cast austenite and evolution of grain structure during hot charging reheating[J]. Continuous Casting, 2020 (2): 45.)
[22] 沈世雕,黄福祥,陈书浩,等.堆垛缓冷对连铸坯中心偏析的影响[J].钢铁,2010,45(10):47.(SHEN Shi-diao, HUANG FU-xiang, CHEN Shu-hao,et sl. Study on the effect of stacking slow-cooling before rolling on the center-segregation of continuous casting slab[J].Iron and Steel,2010,45(10):47.)
[23] 李静,尚成嘉,贺信莱,等.碳含量对高性能桥梁钢组织结构和性能的影响[J].钢铁,2006,41(12):64. (LI Jing, SHANG Cheng-jia, HE Xin-lai, et al. Effect of carbon content on microstrcture and properties of high performance bridge steel[J]. Iron and Steel,2006,41(12):64.)
[24] 王宇,彭翔飞,李俊,等,高氮奥氏体不锈钢强韧化及抗弹性能研究进展[J].钢铁,2022,57(1):28. (WANG Yu, PENG Xiang-fei, LI Jun, et al. Research progress on strengthening mechanism and ballistic performance of high nitrogen austenitic stainless steels[J]. Iron and Steel,2022,57(1):28.)
[25] 王凤权,孙挺,王毛球,等.Fe-Mn-Al-C系奥氏体基低密度钢的研究进展[J].钢铁,2021,56(6):89.(WANG Feng-quan, SUN Ting, WANG Mao-qiu,et al. Research progress of Fe-Mn-Al-C system austenitic low density steel[J].Iron and Steel,2021, 56(6):89.)