巴润精矿配比对球团矿强度的影响

doi:10.13228/j.boyuan.issn0449-749x.20210647

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (7341 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to give full play to the characteristics of Barun iron concentrate with high iron grade, concentrated particle size distribution and excellent pellet-forming performance, while suppress the weakness of high content of K₂O, Na₂O and F, how to improve the utilization rate of Barun ore on the basis of ensuring the strength of finished oxidized pellets by reasonably matching it with the ore in the region with low content of harmful elements was studied. In the research process, the influencing factors on strength of finished ball under different ratios of Barun iron concentrate were analyzed by FactSage7.3 thermodynamic software calculation, oxidation roasting, compressive strength detection, chemical composition detection, mineral phase analysis, SEM-EDS analysis and other experimental research methods. The results show that the iron concentrate in the area has a wider particle size range than the Barun iron concentrate, with the average particle size of 53.21 μm and 32.01 μm, respectively. The mineral powder particles smaller than 0.043 mm(<300 mesh) of iron concentrate in the area is accounting for 78.65%, while the mineral powder particles of Barun iron concentrate is accounting for 84.70%. The strength of finished ball with 40% ratio of Barun iron concentrate is the highest, which is 4 602.2 N /P. Thermodynamic calculation shows that with the increase of Barun iron concentrate ratio, the slag phase in the finished ball increases. In the process of oxidizing roasting and cooling, pyroxene and quartz are the main precipitates of finished ball slag phase for 40% Barun iron concentrate, while calcium iron olivine is the main precipitates of 100% Barun iron concentrate. In terms of mineral phase structure, with the increase of Barun iron concentrate ratio, the hematite intercrystal effect decreases, but the slag phase distribution is uniform at 40% ratio, which plays a good role of bonding phase. One of the reasons for low compressive strength of magnesium-bearing magnetite particles formed by MgO content of 1.05% in 100% Barun finished ball is its poor intercrystal.

Key words： Barun iron concentrate pellets finished ball slag phase compressive strength

Received: 24 October 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHU Rui-zong
	ZHANG Fang
	PENG Jun
	WANG Yong-bin
	CHANG Hong-tao

Cite this article:

ZHU Rui-zong,ZHANG Fang,PENG Jun等. Effect of Barun concentrate ratio on strength of finished pellets[J]. Iron and Steel, 2022, 57(6): 32-41.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210647 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I6/32

[1] 阳诚平, 周晓军, 钟洋. 程潮球团配加毛粉的生产试验[J]. 烧结球团, 2018, 43(6): 74.(YANG Cheng-ping, ZHOU Xiao-jun, ZHONG Yang. Production test of Cheng Chao pellet with wool powder[J]. Sintering and Pelletizing, 2018, 43(6): 74.)
[2] 周明顺, 王义栋, 赵东明, 等.高硫铁精矿配比对球团工艺参数及性能的影响[J]. 钢铁, 2018, 53(5): 11.(ZHOU Ming-shun, WANG Yi-dong, ZHAO Dong-ming, et al. Effect of high sulfur iron concentrate ratio on pelletizing process parameters and performance[J]. Iron and Steel, 2018, 53(5): 11.)
[3] 赵连达, 刘迎立, 苏鸿, 等. 添加赤铁矿对碱性球团性能的影响[J]. 中国冶金, 2021, 31(3): 11.(ZHAO Lian-da, LIU Ying-li, SU Hong, et al. Effect of hematite on properties of alkaline pellets[J]. China Metallurgy, 2021, 31(3): 11.)
[4] 黄柱成, 张元波, 朱尚朴, 等.以赤铁矿为主配加磁铁矿制备氧化球团的研究[J].钢铁, 2004, 39(4): 9.(HUANG Zhu-cheng, ZHANG Yuan-bo, ZHU Shang-pu, et al. Preparation of oxidized pellets from Hematite with magnetite[J]. Iron and Steel, 2004, 39(4): 9.)
[5] 余正伟, 向爱平, 刘山平, 等.低铁高硅赤铁精矿对氧化球团性能的影响[J].中国冶金, 2020, 30(6): 8.(YU Zheng-wei, XIANG Ai-ping, LIU Shan-ping, et al. Study on the oxidation pellet performance of low iron and high silicon red iron concentrate[J]. China Metallurgy, 2020, 30(6): 8.)
[6] 马丽, 青格勒, 田筠清, 等.球团配加细磨麦克粉的试验研究[J].烧结球团,2019, 44(2): 39.(MA Li, QING Ge-le, TIAN Jun-qing, et al. Experimental study on pellet adding finely ground mac powder[J]. Sintering and Pelletizing, 2019, 44(2): 39.)
[7] 朱德庆, 黄铮静, 杨聪聪, GF88赤铁精矿制备氧化球团的试验研究[J].烧结球团, 2020, 45(6): 61.(ZHU De-qing, HUANG Zheng-jing, YANG Cong-cong, Experimental study on preparation of oxidized pellets from GF88 red iron concentrate[J]. Sintering and Pelletizing, 2020, 45(6): 61.)
[8] 田筠清, 青格勒, 张彦, 等.含硼矿粉制备球团矿的特点及应用方法[J].中国冶金, 2020, 30(6): 18.(TIAN Yun-qing, QING Ge-le, ZHANG Yan, et al. Characteristics and application of boron bearing ore powder for pellet preparation[J]. China Metallurgy, 2020, 30(6): 18.)
[9] 刘然, 薛向欣, 姜涛, 等.硼铁矿综合利用概况与展望[J].矿山综合利用, 2006,4(2): 33.(LIU Ran, XUE Xiang-xin, JIANG Tao, et al. Review and prospect of comprehensive utilization of pyrite[J]. Comprehensive Utilization of Mine, 2006,4(2): 33.)
[10] 丁信珍, 衣守志, 孙苒荻, 等.硼铁精矿焙烧过程反应活性研究[J].化工矿物与加工, 2017(2): 23.(DING Xin-zhen, YI Shou-zhi, SUN Ran-di, et al. Study on the reactivity of boron iron concentrate during roasting[J]. Industrial Minerals and Processing, 2017(2): 23.)
[11] 黄桂香, 甄彩铃, 张举成, 等.配加硼镁铁矿生产镁质球团矿的工业试验研究[J].烧结球团, 2016, 41(6): 48.(HUANG Gui-xiang, ZHEN Cai-ling, ZHANG Ju-cheng, et al. Study on the production of magnesium pellets by adding bormaite [J]. Sintering and Pelletizing, 2016, 41(6): 48.)
[12] 刘然, 薛向欣, 黄大威.硼铁矿氧化焙烧失重及机理探讨[J].钢铁, 2007, 42(9): 9.(LIU Ran, XUE Xiang-xin, HUANG Da-wei. Study on weight loss of pyrite by oxidation roasting [J]. Iron and Steel, 2007, 42(9): 9.)
[13] 李杰, 郭学东, 姜涛.钙化焙烧对富硼渣活性的影响研究[J].化工矿物与加工, 2015(3): 20.(LI Jie, GUO Xue-dong, JIANG Tao. Effect of calcification calcination on the activity of boron rich slag[J]. Industrial Minerals and Processing, 2015(3):20.)
[14] 余建文, 韩跃新, 高鹏.含硼铁精矿还原过程中硼矿物的热力学行为[J]. 中国有色金属学报, 2015, 25(7): 1969.(YU Jian-wen, HAN Yue-xin, GAO Peng. Thermodynamic behavior of boron minerals during reduction of boron-bearing iron concentrate[J]. The Chinese Journal of Nonferrous Metals, 2015, 25(7): 1969.)
[15] 沈茂森, 吕志义, 康文革, 等. 白云鄂博铁球团矿异常还原膨胀的机理[J]. 中国冶金, 2021, 31(3): 17.(SHEN Mao-sen, LÜ Zhi-yi, KANG Wen-ge, et al. Mechanism of abnormal reduction expansion of Bayan Obo iron pellets[J]. China Metallurgy, 2021, 31(3): 17.)
[16] 张芳,聂东娥,霍明鹤,等. 钾长石对CO还原过程铁氧化物过程还原膨胀性的影响[J]. 钢铁研究学报, 2020,32(11): 958.(ZHANG Fang, NIE Dong-e, HUO Ming-he, et al. Effect of potassium feldspar on dilatancy of iron oxide during CO reduction[J]. Journal of Iron and Steel Research, 2020,32(11): 958.)
[17] 蔡皓宇, 青格勒, 张卫东, 等. 细磨对矿粉特性和造球性能的影响[J]. 钢铁, 2015, 50 (8): 16.(CAI Hao-yu, QING Ge-le, ZHANG Wei-dong, et al. Effect of fine grinding on characteristics of ore powder and pelletizing performance[J]. Iron and Steel, 2015, 50 (8): 16.)
[18] 范晓慧,袁晓丽,姜涛, 等铁精矿粒度对球团强度的影响[J].中国有色金属学报,2006(11):1965. (FAN Xiao-hui, YUAN Xiao-li, JIANG Tao, et al. Effect of particle size of iron concentrate on pellet strength[J]. The Chinese Journal of Nonferrous Metals, 2006 (11): 1965.)
[19] 范建军, 杨礼元. 高压辊磨预处理对超细粒度磁铁精矿粉球团性能的影响[J]. 钢铁, 2012, 47(9): 9.(FAN Jian-jun, YANG Li-yuan. Effect of high pressure roller mill pretreatment on performance of ultrafine magnetite concentrate pellets[J]. Iron and Steel, 2012, 47(9): 9.)
[20] 董杰吉, 王广, 李华, 等. 三水铝石型高铝褐铁矿粉烧结液相生成特性[J]. 钢铁, 2014, 49(11): 25.(DONG Jie-ji, WANG Guang, LI Hua, et al. Formation characteristics of high alumina limonite trihydrate powders in sintering phase [J]. Iron and Steel, 2014, 49(11): 25.)
[21] 潘建, 田宏宇, 朱德庆, 等. 超微细铁精矿的粒度特性和润湿性对其成球性能的交互影响[J]. 工程科学学报, 2017, 39(6): 830.(PAN Jian, TIAN Hong-yu, ZHU De-qing, et al. Effect of particle size and wettability on pelleforming performance of ultrafine iron concentrate[J]. Journal of Engineering Science, 2017, 39(6): 830.)
[22] 朱德庆, 徐梦杰, 潘建, 等. 改善超细铁精矿成球性能的实验研究[J]. 钢铁研究学报, 2017, 29(9): 704.(ZHU De-qing, XU Meng-jie, PAN Jian, et al. Experimental study on improving pelletizing performance of ultrafine iron concentrate[J]. Journal of Iron and Steel Research, 2017, 29(9):704.)
[23] 朱德庆, 虎训, 潘建, 等. 优化配矿强化西澳超细粒磁铁精矿球团焙烧研究[J]. 工程科学学报, 2017, 39(5): 683.(ZHU De-qing, HU Xun, PAN Jian, et al. Study on pellet roasting of west Australia ultrafine magnetite concentrate by optimizing ore blending[J]. Journal of Engineering Science, 2017, 39(5): 683.)
[24] 张汉泉.膨润土在铁矿氧化球团中的应用[J]. 中国矿业, 2009, 18(8): 99.(ZHANG Han-quan. Application of bentonite to iron ore oxidation pellets[J]. China Mining Magazine, 2009, 18(8): 99.)
[25] 张淑会, 严照照, 刘小杰, 等. 化学成分对球团矿抗压强度影响的研究现状[J]. 烧结球团, 2017, 42(6): 57.(ZHANG Shu-hui, YAN Zhao-zhao, LIU Xiao-jie, et al. Research status of influence of chemical composition on compressive strength of pellets[J]. Sintering and Pelletizing 2017, 42(6): 57.)
[26] Dwarapudi S, Ghosh K, Shankar A, et al. Effect of pellet basicity and MgO content onthe quality and microstructure of hematite pellets[J]. International Journal of Mineral Processing, 2011, 99(6): 43.
[27] Pal J, Arunkumar C, Rajshekhar Y, et al. Development on iron ore pelletization using calcined lime and MgO combined flux replacing limestone and bentonite[J]. ISIJ International,2014, 54(2): 2169.
[28] WANG R, ZHANG J, LIU Z, et al. Interaction between iron ore and magnesium additives during induration process of pellets[J]. Powder Technology, 2020, 361(1): 894.
[29] ZHU D, CHUN T, PAN J, et al. Influence of basicity and MgO content on metallurgical performances of Brazilian specularite pellets[J]. International Journal of Mineral Processing, 2013, 125(9): 51.
[30] Kemppainen A, Ohno K, Iljana M, et al. Softening behaviors of acid and olivine fluxed iron ore pellets in the cohesive zone of a blast furnace[J]. ISIJ International, 2015, 55(2):2039.