回火温度对700 MPa级大梁钢组织和性能的影响

doi:10.13228/j.boyuan.issn0449-749x.20230090

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract It is common that microalloying elements are not precipitated completely in hot rolled steel. When there are oversaturated solid solution microalloying elements in steel,tempering can precipitate them in the matrix and affect the mechanical properties. The effect of tempering temperature on microstructure and properties of Nb-Ti microalloying hot rolled 700 MPa automobile beam steel was studied by means of SEM,EBSD,TEM and tensile test. The results show that when tempering at 450 ℃ to 600 ℃,the matrix structure of the experimental steel is almost identical to the hot-rolled experimental steel,and it is mainly quasi-polygonal ferrite with slightly larger size. When tempering at 700 ℃,the microstructure of the experimental steel transforms to polygonal ferrite,the grain size increases rapidly,the grain boundary density decreases,and partial recrystallization occurs. When tempering,the oversaturated solid solution Ti and Nb in the hot rolling stage will precipitate in the form of (Ti,Nb)C. The higher the tempering temperature,the shorter the precipitation incubation period of (Ti,Nb)C and the larger the precipitation content. The average particle size will first decrease and then increase. When the tempering temperature is 600 ℃,the average particle size of (Ti,Nb)C is the smallest,only 5.47 nm. The tensile strength,yield strength and elongation increase with the increase of temperature when the experimental steel is tempered in the range of 450 ℃ to 600 ℃. When the tempering temperature rises to 700 ℃,the yield strength and tensile strength of the experimental steel decrease significantly and the elongation increases. When the tempering temperature is 600 ℃,the mechanical properties of the experimental steel are optimal. The tensile strength,yield strength and elongation are 803 MPa,755 MPa and 24.6%,respectively. The strengthening mechanism analysis shows that the yield strength improvement of the experimental steel is mainly caused by the precipitation strengthening of microalloying elements Ti and Nb during the tempering process.

Key words： automobile bean steel Nb-Ti microalloying tempering temperature mechanical property strengthening mechanism

Received: 28 February 2023

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHOU Qiang
	CAO Yanguang
	YANG Gengwei
	LI Zhaodong
	WAN Guoxi
	WANG Wenjun

Cite this article:

ZHOU Qiang,CAO Yanguang,YANG Gengwei等. Effect of tempering temperature on microstructure and mechanical properties of 700 MPa grade beam steel[J]. Iron and Steel, 2023, 58(10): 102-110.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20230090 OR http://www.chinamet.cn/Jweb_gt/EN/Y2023/V58/I10/102

[1] 张继永,李红俊,申震,等. 700 MPa级汽车大梁钢混晶组织问题研究[J]. 轧钢,2021,38(1):84.(ZHANG J Y,LI H J,SHEN Z,et al. Research of mixed crystal structure of 700 MPa grade plate for automobile beam[J]. Steel Rolling,2021,38(1):84. )
[2] 杜海明,李静宇,杜亚伟,等. AG700L钢亚动态再结晶行为研究[J]. 轧钢,2022,39(5):47.(DU H M,LI J Y,DU Y W,LIU et al. Research on sub-dynamic recrystallization behavior of AG700L steel[J]. Steel Rolling,2022,39(5):47. )
[3] 杨庚蔚,毛新平,赵刚,等. Ti微合金化高强度热轧带钢组织性能及强化机理[J]. 钢铁研究学报,2016,28(12):75.(YANG G W,MAO X P,ZHAO G,et al. Microstructure,mechanical properties and strengthening mechanisms of Ti microalloyed high strength hot strip steel[J]. Journal of Iron and Steel Research,2016,28(12):75.)
[4] FU Z X,YANG G W,HAN R Y,et al. Influence of coiling temperature on microstructure and mechanical properties of a hot-rolled high-strength steel microalloyed with Ti,Mo and V[J]. Journal of Iron and Steel Research International,2022,29(3):484.
[5] 杨庚蔚,陆佳伟,孙辉,等. Ti-V微合金化热轧高强钢的相变规律及组织性能[J]. 钢铁研究学报,2019,31(8):726.(YANG G W,LU J W,SUN H,et al. Microstructure,mechanical properties and phase transformation behavior of Ti-V microalloyed high-strength hot-strip steel[J]. Journal of Iron and Steel Research,2019,31(8):726.)
[6] HAN R Y,YANG G W,XU D M,et al. Effect of V on the precipitation behavior of Ti-Mo microalloyed high-strength steel[J]. Materials,2022,15(17): 5965.
[7] 何仙灵,杨庚蔚,毛新平,等. Nb对Ti-Mo微合金钢连续冷却相变规律及组织性能的影响[J]. 金属学报,2017,53(6):648.(HE X L,YANG G W,MAO X P,et al. Effect of Nb on the continuous cooling transformation rule and microstructure,mechanical properties of Ti-Mo bearing microalloyed steel[J]. Acta Metallurgica Sinica,2017,53(6):648.)
[8] HUANG H H,YANG G W,ZHAO G,et al. Effect of Nb on the microstructure and properties of Ti-Mo microalloyed high-strength ferritic steel[J]. Materials Science and Engineering A,2018,736:148.
[9] 杨洪波,王豪,赵旭,等. 微合金高强钢纳米相间析出行为研究进展[J]. 钢铁,2021,56(12):10.(YANG H B,WANG H,ZHAO X,et al. Research progress on nano-scale interphase precipitation behavior of microalloyed high-strength steel[J]. Iron and Steel,2021,56(12):10.)
[10] 张亮亮,于洋,李晓军,等. 600 MPa级高强钢热轧卷取工艺研究及应用[J]. 中国冶金,2022,32(12):106.(ZHANG L L,YU Y,LI X J,et al. Research and application of hot rolling coiling process for 600 MPa high strength steel[J]. China Metallurgy,2022,32(12):106.)
[11] 韩荣,刘洪喜,尉文超,等. Ti-V-Mo微合金化22MnB5钢中析出相及其强化作用[J]. 钢铁,2022,57(2):127.(HAN R,LIU H X,YU W C,et al. Precipitates and their strengthening in Ti-V-Mo microalloyed 22MnB5 steel[J]. Iron and Steel,2022,57(2):127.)
[12] 李成刚,周晓光,蒋小冬,等. 冷却工艺对Ti微合金化高强钢组织和硬度的影响[J]. 钢铁研究学报,2021,33(9):987.(LI C G,ZHOU X G,JIANG X D,et al. Influence of cooling processes on microstructure and hardness of Ti micro-alloyed high strength steel[J]. Journal of Iron and Steel Research,2021,33(9):987.)
[13] 宋丽英,王明明,邢俊芳,等. 钛微合金化700 MPa级高强耐候钢组织和性能研究[J]. 钢铁研究学报,2022,34(12):1447.(SONG L Y,WANG M M,XING J F,et al. Study on microstructures and properties of 700 MPa Ti-microalloyed high strength weathering steels[J]. Journal of Iron and Steel Research,2022,34(12):1447.)
[14] 胡学文,彭欢,王海波,等. 1 200 MPa级热轧超高强钢组织及性能[J]. 轧钢,2021,38(6):87.(HU X W,PENG H,WANG H B,et al. Research on microstructure and mechanical properties of 1 200 MPa grade hot rolled ultra-high strength steel[J]. Steel Rolling,2021,38(6):87. )
[15] 刘怡私,梁亮,宫成,等. 变形和冷却工艺对含Ti-Nb高强汽车用钢组织性能的影响[J]. 轧钢,2023,40(2):39.(LIU Y S,LIANG L,GONG C,et al. Effect of deformation and cooling process on microstructure and mechanical properties of Ti-Nb microalloyed high strength automotive steel[J]. Steel Rolling,2023,40(2):39. )
[16] 蔡易辰,吴昊,梁亮,等. 屈服强度1 400 MPa级超高强钢的研发及应用[J]. 轧钢,2022,39(6):145.(CAI Y C,WU H,LIANG L,et al. Development of yield strength 1 400 MPa grade ultra-high strength steel and itsapplication[J]. Steel Rolling,2022,39(6):145. )
[17] FUNAKAWA Y,SHIOZAKI T,TOMITA K,et al. Development of high strength hot-rolled sheet steel consisting of ferrite and nanometer-sized carbides[J]. ISIJ International,2004,44(11):1945.
[18] 惠亚军,陈斌,崔阳,等. 600 MPa级Nb-Ti微合金化高成形性元宝梁用钢的开发[J]. 钢铁研究学报,2018,30(5):6.(HUI Y J,CHEN B,CUI Y,et al. Development of 600 MPa grade Nb-Ti microalloyed high formability crossbeam steel[J]. Journal of Iron and Steel Research,2018,30(5):6.)
[19] 张可,雍岐龙,孙新军,等. 卷取温度对Ti-V-Mo复合微合金化超高强度钢组织及力学性能的影响[J]. 金属学报,2016,52(5):529.(ZHANG K,YONG Q L,SUN X J,et al. Effect of coiling temperature on microstructure and mechanical properties of Ti-V-Mo complex microalloyed ultra-high strength steel[J]. Acta Metallurgica Sinica,2016,52(5):529.)
[20] 田星,朱国明,康永林,等. CSP流程钛微合金化高强钢的第二相粒子析出行为[J]. 工程科学学报,2015,37(1):42.(TIAN X,ZHU G M,KANG Y L,et al. Precipitation behavior of Ti-microalloyed high-strength steel by CSP process[J]. Chinese Journal of Engineering,2015,37(1):42.)
[21] 贺彤,王海建,李花兵,等. 含氮热作模具钢的研究现状与发展[J]. 钢铁研究学报,2022,34(12):1334.(HE T,WANG H J,LI H B,et al. Current research status and development of nitrogen-containing hot-work die steel[J]. Journal of Iron and Steel Research,2022,34(12):1334.)
[22] 付至祥. 回火工艺对Ti-Mo-V微合金化热轧超高强钢析出行为及组织性能的影响[D]. 武汉:武汉科技大学,2021.(FU Z X. Effect of Tempering Process on the Precipitation Behavior,Microstructure and Mechanical Properties of Ti-Mo-V Microalloying Hot-Rolled Ultra-High Strength Steel[D]. Wuhan:Wuhan University of Science and Technology,2021.)
[23] 卜凡征,王玉斌,郑连辉,等. Ti-Mo微合金钢回火过程中纳米碳化物析出行为[J]. 钢铁研究学报,2018,30(11):928.(BU F Z,WANG Y B,ZHENG L H,et al. Precipitation of nanoscale carbides in Ti-Mo microalloyed steel during tempering process[J]. Journal of Iron and Steel Research,2018,30(11):928.)
[24] WU Z R,YU J M,ZHANG Z W,et al. Static recrystallization behavior of Mg-Gd-Y-Zn-Zr alloy during annealing treatment[J]. The Journal of The Minerals,Metals and Materials Society,2022,74(7):2566.
[25] ZHENG Y X,WANG Q,ZHU L G,et al. Microstructure evolution and carbide precipitation behavior of microalloyed TS800TB steel during hot rolling and coiling processes[J]. Materials Science and Engineering A,2022,840:142902.
[26] ZHOU Q,LI Z,WEI Z S,et al. Microstructural features and precipitation behavior of Ti,Nb and V microalloyed steel during isothermal processing[J]. Journal of Iron and Steel Research International,2019,26:102.
[27] 李冠楠,商志强,李红俊. 调质工艺对汽车大梁钢700L组织性能的影响[J]. 中国冶金,2022,32(4):41.(LI G N,SHANG Z Q,LI H J. Effect of quenching and tempering process on microstructure and properties of automobile large beam steel 700L[J]. China Metallurgy,2022,32(4):41.)
[28] 刘旭辉,曾斌,梁亮,等. 回火工艺对900 MPa级热轧卷板组织与性能的影响[J]. 钢铁,2018,53(10):74.(LIU X H,ZENG B,LIANG L,et al. Effect of tempering process on microstructure and mechanical properties of 900 MPa grade hot rolled steel[J]. Iron and Steel,2018,53(10):74.)
[29] 董纪,杨晓斌,刘晨曦,等. 超高强度钢热处理组织中碳化物演化行为研究进展[J]. 钢铁研究学报,2021,33(10):105.(DONG J,YANG X B,LIU C X,et al. Research progress of carbide evolution behavior in heat treated structure of ultra-high strength steel[J]. Journal of Iron and Steel Research,2021,33(10):1052.)
[30] 雍岐龙. 钢铁材料中的第二相[M]. 北京:冶金工业出版社,2006.(YONG Q L. Second Phase in Structural Steels[M]. Beijing:Metallurgical Industry Press,2006.)
[31] LI X L,JIN C,LI H Z,et al. Influence of cooling rate on phase transformation and precipitation behavior of Ti-bearing steel in continuous cooling process[J]. Journal of Iron and Steel Research International,2022,29:165.
[32] LI X L,YANG J W,LI Y T,et al. A systematical evaluation of the crystallographic orientation relationship between MC precipitates and ferrite matrix in HSLA steels[J]. Materials,2022,15(11):3967.
[33] HANSEN N. Hall-Petch relation and boundary strengthening[J]. Scripta Materialia,2004,51(8):801.
[34] HESLOP J,PETCH N J. The ductile-brittle transition in the fracture of α-iron: II[J]. Philosophical Magazine,1958,3(34):1128.
[35] 易航. Ti-Mo-V复合微合金钢中第二相析出行为及组织性能研究[D]. 武汉:武汉科技大学,2020.(YI H. Study on the Precipitation Behavior,Microstructure and Mechanical Properties of Ti-Mo-V Complex Microalloyed Steel[D]. Wuhan: Wuhan University of Science and Technology,2020.)