| Numerical simulation and experimental verification of interrupted quenching (IRQ) for heavy-haul railway wheels |
| YAO Sancheng1,2, ZHANG Jian1,2, LIU Xuehua1,2, ZHAO Hai1,2, SHI Na1,2, XU Jun3 |
1. Key Parts of Rail Transit Technology Innovation Center of Anhui Province, Maanshan 243003, Anhui, China;
2. Technology Center, Maanshan Iron and Steel Co., Ltd., Maanshan 243003, Anhui, China;
3. School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China |
|
|
|
|
Abstract The non-pearlite mixed microstructure layer containing martensite (M) and bainite (B),which is generated during the heat treatment cooling process of railway wheels,is a potential source of driving faults and hazards. For heavy-haul railway wheels with prominent non-pearlite layer,the finite element numerical model of interrupted quenching (IRQ) was established based on software MSC. Marc and Thermal Prophet,and the influence of IRQ process on temperature field,microstructure and mechanical properties of the wheel was analyzed,and the physical verification was carried out. The simulation results show that during the short quenching interruption period,due to the influence of heat conduction inside the deeper rim,a small temperature platform or temperature return phenomenon occurs near the surface of the wheel tread. The return temperature is lower than the critical point Ac1,which can avoid secondary austenitization,but the tread sub-surface and inside of the rim are slightly affected. IRQ process slow down the temperature drop near the tread surface,and avoid most of the M and B transformation areas. The non-pearlitic layer is inhibited,and its thickness is controlled within 6 mm,so the microstructure near the tread is significantly improved. The interior of the rim has a relatively uniform microstructure with fine pearlite and a small amount of ferrite (P-F),but within a depth range of 10-15 mm from the tread surface,the composition of the microstructure may fluctuate locally,and a small amount of B microstructure may be regenerated in the P-F microstructure. The gradient of strength and hardness distribution from the tread surface of the wheel is reasonable and gradually decreased,and the strength and hardness level of most areas inside the rim is not significantly affected. Due to the pre-cooling effect,the IRQ process improves the average effective cooling rate within the depth range of 15-30 mm from the tread surface,forming a local maximum area of strength and hardness,slightly improving the strength and hardness compared with the traditional process wheel. The physical verification results are basically consistent with the simulation results. After comprehensive evaluation,it is basically feasible to apply IRQ process to control the non-pearlitic microstructure layer of heavy-haul railway wheels.
|
|
Received: 20 March 2023
|
|
|
|
[1] 蔡钊.整体辗钢车轮传统热处理工艺分析与展望[J].轧钢,1990,7(6):44.(CAI Z. Analysis and prospect of traditional heat treatment process for integrally rolled steel wheel[J]. Steel Rolling,1990,7(6):44.)
[2] 张关震,任瑞铭,吴斯,等.不均匀组织ER8车轮滚动接触疲劳性能研究[J].摩擦学学报,2021,41(4):553. (ZHANG G Z,REN R M,WU S,et al. Rolling contact fatigue performance of ER8 wheel steel with non-uniform microstructure [J]. Tribology,2021,41(4):553.)
[3] 张关震,任瑞铭,尹鸿祥,等.动车组车轮异常组织特征及成因[J].中国铁道科学,2020,41(4):108.(ZHANG G Z,REN R M,YIN H X,et al. Characteristics and causes of abnormal microstructure in EMU wheels[J]. China Railway Science,2020,41(4):108.)
[4] 丛韬,韩建民,张关震,等.铁路车轮轮辋疲劳裂纹和踏面剥离掉块的微观伤损因素分析[J].中国铁道科学,2017,38(5):93.(CONG T,HAN J M,ZHANG G Z,et al. Analysis of micro damage factors of shattered rim and tread shelling of railway wheel[J]. China Railway Science,2017,38(5):93.)
[5] LI G,HONG Z Y,YAN Q Z. The influence of microstructure on the rolling contact fatigue of steel for high-speed-train wheel[J]. Wear,2015(342/343):349.
[6] 江波,陈刚,赵海,等.中碳车轮钢复合型裂纹疲劳扩展行为 [J].钢铁,2018,53(12):100.(JIANG B,CHEN G,ZHAO H,et al. Fatigue propagation behavior of mixed mode crack in wheel steel[J]. Iron and Steel,2018,53(12):100.)
[7] SUN J,SAWLEY K J,STONE D H,et al. Progress in the reduction of wheel spalling[C]//Proceeding of the 12th International Wheelset Congress. Qingdao:China Railway Society,1998:18.
[8] 张斌,付秀琴,张弘,等.机车车辆车轮踏面剥离现状及其分析[J].铁道车辆,2005,43(5):1.(ZHANG B,FU X Q,ZHANG H,et al. The present conditions and the analysis of wheel tread peeling on locomotives and rolling stock[J]. Rolling Stock,2005,43(5):1.)
[9] 张弘,张斌,王振刚,等.车轮早期剥离现象及成因初探[J].铁道机车车辆,2006,26(3):18.(ZHANG H,ZHANG B,WANG Z G,et al. Pilot study of early shelling of locomotive and vehicle wheels[J]. Railway Locomotive and Car,2006,26(3):18.)
[10] 付斌,安涛,沈晓辉,等.火车车轮淬火过程中的温度场[J].钢铁研究学报,2007,19(9):46.(FU B,AN T,SHEN X H,et al. Temperature field during quenching process of railway wheel[J]. Journal of Iron and Steel Research,2007,19(9):46.)
[11] 安涛,付斌,沈晓辉,等.火车车轮淬火过程数值模拟 [J].计算机辅助工程,2006,15(s1):388. (AN T,FU B,SHEN X H,et al. Numerical simulation during railway wheel quenching process[J]. Computer Aided Engineering,2006,15(s1):388.)
[12] 冯浩洲,王蓬,李冬玲,等.火车车轮轮辋组织与显微硬度的统计分布表征[J].钢铁研究学报,2022,34(3):280.(FENG H Z,WANG P,LI D L,et al. Statistical distribution characterization of train wheel rim structure and microhardness[J]. Journal of Iron and Steel Research,2022,34(3):280.)
[13] 苏世怀,赵海,江波,等.中国高速车轮产品质量性能研发应用进展[J].钢铁,2018,53(11):1.(SU S H,ZHAO H,JIANG B,et al. Development and application of high-speed wheel product quality performance in China[J]. Iron and Steel,2018,53(11):1.)
[14] 苏世怀,张建平,江波,等.一种改善车削加工性能的火车车轮热处理方法:中国,02113182.1[P]. 2002-06-18.(SU S H,ZHANG J P,JIANG B,et al. Method for Heat Treatment of Train Wheel with Improved Turning Ability:China,02113182.1[P]. 2002-06-18.)
[15] 陈刚,王世付,江波,等.高碳钢火车车轮轮辋表面的热处理方法及热处理装置:中国,200810020421.5 [P]. 2008-03-04.(CHEN G,WANG S F,JIANG B,et al. Thermal Treatment Method for High-Carbon Steel Train Wheel Circular Rim Surface and Heat Treatment Apparatus:China,200810020421.5[P]. 2008-03-04.)
[16] 姚三成,钟斌,邓荣杰,等.一种铁路车轮冷却装置、冷却方法和制备方法:中国,201911154651.5[P]. 2019-11-22.(YAO S C,ZHONG B,DENG R J,et al. Train Wheel Cooling Device and Method and Preparation Method:China,201911154651.5[P]. 2019-11-22.)
[17] 姚三成,宫彦华,陈刚,等.一种铁路车轮的热处理冷却工艺:中国,201910358140.9[P]. 2019-04-30.(YAO S C,GONG Y H,CHEN G,et al. Heat-treatment Cooling Process for Train Wheel:China,201910358140.9[P]. 2019-04-30.)
[18] 姚三成,江波,刘学华,等.高碳钢铁路车轮新型热处理冷却工艺有限元模拟[J].材料热处理学报,2021,42(1):181.(YAO S C,JIANG B,LIU X H,et al. Finite element simulation of new heat treatment cooling process for high carbon steel railway wheel[J]. Transactions of Materials and Heat Treatment,2021,42(1):181.)
[19] 万志健,刘学华,赵海,等.一种用于铁路车轮的间歇淬火方法:中国,202010735022.8[P]. 2020-07-28. (WAN Z J,LIU X H,ZHAO H,et al. Intermittent Quenching Method for Railway Wheel:China,202010735022.8[P]. 2020-07-28.)
[20] 戎咏华,左训伟,陈乃录.清洁的水-空交替控时淬火冷却技术:原理与应用[J].金属热处理,2018,43(4):1.(RONG Y H,ZUO X W,CHEN N L. Clean water-air alternative timed quenching (ATQ) technology:Principle and applications[J]. Heat Treatment of Metals,2018,43(4):1.)
[21] 左训伟,张绵胜,陈乃录,等.U20Mn钢轨水－空交替控时淬火技术的中试研究[J].金属热处理,2020,45(9):50. (ZUO X W,ZHANG M S,CHEN N L,et al. Pilot-scale study of water-air alternative timed quenching technology for U20Mn steel rail[J]. Heat Treatment of Metals,2020,45(9):50.)
[22] 孔祥谦.有限单元法在传热学中的应用[M].3版. 北京:科学出版社,1998.(KONG X Q. Application of Finite Element Method in Heat Transfer[M]. 3rd Edition. Beijing:Science Press,1998.)
[23] 刘庄,吴肇基,吴景之,等.热处理过程的数值模拟[M].北京:科学出版社,1996.(LIU Z,WU Z J,WU J Z,et al. Numerical Simulation of Heat Treatment Processing[M]. Beijing:Science Press,1996.)
[24] 顾剑锋,潘健生,胡明娟,等.9Cr2Mo冷轧辊加热过程的模拟[J].金属学报,1999,35(12):1266.(GU J F,PAN J S,HU M J,et al. Numerical simulation on heating process of 9Cr2Mo cold roller[J]. Acta Metallurgica Sinica,1999,35(12):1266.)
[25] 雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006.(YONG Q L. Secondary Phases in Steels[M]. Beijing:Metallurgical Industry Press,1996.)
[26] KUZIAK R,ZYGMUNT T. A new method of rail head hardening of standard-gauge rails for improved wear and damage resistance[J]. Steel Research International,2013,84(1):13.
[27] 孙邦明.ø1 098 mm车轮热处理工艺的研究[J].钢铁研究,2001(2):28.(SUN B M. Study on heat treatment process for ø1 098 mm wheel[J]. Research on Iron and Steel,2001(2):28.)
[28] 陈明伟,周禾丰.延迟淬火提高淬硬层深度效应的计算传热学分析[J].金属热处理学报,1993,14(4):1.(CHEN M W,ZHOU H F. Numerial heat transfer analysis on the effcet of enhancing hardened depth by delay quenching[J]. Transactions of Metal Heat Treatment,1993,14(4):1.)
[29] 左训伟.水-空交替控时淬火冷却设备的研究与应用[D].上海:上海交通大学,2010.(ZUO X W. Research and Application of Alternately Timed Quenching Equipment by Water and Air[D]. Shanghai:Shanghai Jiao Tong University,2010.)
[30] 马跃.高速车轮钢韧化机理及工艺优化研究[D].北京:钢铁研究总院,2013.(MA Y. Study on Toughening Mechanism and Production Process Optimization of Wheel Steel for High Speed Train[D]. Beijing:Central Iron and Steel Research Institute,2013.)
[31] FUJIMURA T,ANJIKI M,MAKINO T,et al. Railway Wheel and Manufacturing Method of the Railway Wheel:United States,5899516[P]. 1999-05-04. |
|
|
|
2023, Vol. 58 