Microstructure of W18Cr4V High Speed Steel After Cryogenic Treatment

  • DUAN Chunzheng,WANG Minjie
Author information +
文章历史 +

摘要

用X射线衍射和透射电子显微镜研究了W18Cr4V高速钢循环深冷处理前后的显微组织。结果表明,与一次长时间深冷处理相比,多次循环深冷处理后马氏体轴比和碳含量明显下降,奥氏体含量进一步减少,有大量新的超细弥散碳化物颗粒沿马氏体孪晶带和位错线析出,表明高速钢多次循环深冷处理效果好于一次长时间深冷处理。

Abstract

The microstructure of W18Cr4V high speed steel before and after repeated cryogenic treatment was studied using Xray diffraction and transmission electron microscopy. The results show that in comparison with single long cryogenic treatment after repeated cryogenic treatment, the axial ratio and carbon content of martensite decrease significantly, the residual austenite content further lowers, a lot of new ultrafine dispersed carbide particles precipitates on the twin bands and dislocation lines of martensite, therefore, the effect of repeated cryogenic treatment is better than that of the single long cryogenic treatment for high speed steel.

关键词

高速钢 / 深冷处理 / 马氏体 / 残余奥氏体 / 碳化物

Key words

high speed steel / cryogenic treatment / martensite / residual austenite / carbide

引用本文

导出引用
段春争;王敏杰. 深冷处理后W18Cr4V高速钢的显微组织[J]. 钢铁研究学报, 2008, 20(8): 38-0
DUAN Chunzheng;WANG Minjie. Microstructure of W18Cr4V High Speed Steel After Cryogenic Treatment[J]. Journal of Iron and Steel Research, 2008, 20(8): 38-0

0

Accesses

0

Citation

Detail

段落导航
相关文章

/