Effect of .nish rolling temperature on microstructure and mechanical properties of hot rolled high strength steel for container

LI Wen-yuan, LIU Kun, HUI Ya-jun, LIU Xiao-cui, LIU Jie, LI Zheng-quan

Journal of Iron and Steel Research ›› 2015, Vol. 27 ›› Issue (8) : 64-69.

Journal of Iron and Steel Research ›› 2015, Vol. 27 ›› Issue (8) : 64-69. DOI: 10.13228/j.boyuan.issn1001-0963.20150007

Effect of .nish rolling temperature on microstructure and mechanical properties of hot rolled high strength steel for container

  • LI Wen-yuan1, LIU Kun1, HUI Ya-jun1, LIU Xiao-cui2, LIU Jie1, LI Zheng-quan2
Author information +
History +

Abstract

Influence of finish rolling temperature on the metallographic structure, mechanical properties and precipitation behavior of the second phase particles was studied by means of optical microscopy, scanning electron microscopy, transmission electron microscopy and other test equipments. The results show that the metallographic structures of high strength steels for container with different finish rolling temperatures are composed of ferrite and a little pearlite and the grain size grades of ferrite are both 13.0. Compared with the one with finish rolling temperature of 890 ℃, the yield strength and tensile strength of the one with finish rolling temperature of 850 ℃ increase by 32 MPa and 26 MPa respectively. The results of theoretical calculation and observation by TEM show that the higher strength of the one with finish rolling temperature of 850 ℃ mainly is due to the higher nucleation rate of second phase particles, more precipitation amount and smaller particle spacing, which makes precipitation strengthening effect more significant.

Key words

finish rolling temperature / second phase particles / fine crystalline strengthening / precipitation strengthening / nucleation rate

Cite this article

Download Citations
LI Wen-yuan, LIU Kun, HUI Ya-jun, LIU Xiao-cui, LIU Jie, LI Zheng-quan. Effect of .nish rolling temperature on microstructure and mechanical properties of hot rolled high strength steel for container[J]. Journal of Iron and Steel Research, 2015, 27(8): 64-69 https://doi.org/10.13228/j.boyuan.issn1001-0963.20150007

References

[1] 陆匠心.700MPa级高强度微合金钢生产技术研究:博士学位论文[D]. 沈阳:东北大学,2004. [2] 文新理.700MPa级薄规格集装箱成分设计和组织性能控制:硕士学位论文[D]. 北京:北京科技大学,2009. [3] 张永坤.Nb-B复合强化热轧高强集装箱板组织和性能研究:硕士学位论文[D]. 北京:北京科技大学,2010. [4]周建,康永林,毛新平,等.对高强耐候钢力学性能的影响[J].北京科技大学学报, 2006, 28(10):926-930 [5]霍向东,毛新平,吕盛夏,等.生产微合金化高强钢中纳米碳化物[J].北京科技大学学报, 2011, 33(8):941-945 [6]陈庆军,康永林,谷海荣,等.对高强度耐候钢组织和性能的影响[J].特殊钢, 2005, 26(1):30-33 [7]赵培林,孙新军,汤化胜,等.微合金化对热轧超高强耐候钢组织和性能的影响[J].特殊钢, 2012, 33(1):46-50 [8] 雍歧龙, 马明图, 吴宝榕.微合金钢-物理和力学冶金[M]. 北京:机械工业出版社,1989:57. [9]. 雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006. [10]雍岐龙,裴和中,田建国,等.铌在钢中的物理冶金学基础数据[J].钢铁研究学报, 1998, 10(2):66-69 [11]雍岐龙,田建国,杨文勇,等.钛在钢中的物理冶金学基础数据[J].云南工业大学学报, 1999, 15(2):7-10

132

Accesses

0

Citation

Detail

Sections
Recommended

/