| Effects of long term aging on microstructure and properties of a tungsten bearing heat resistant alloy |
| Han‑sheng Bao1, Gang Yang1, Zheng‑zong Chen1, Zheng‑dong Liu1 |
| 1 Institute for Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China |
|
|
|
|
Abstract The effects of long-term aging at 700 and 750 °C on microstructure and mechanical properties of a new developed tungsten bearing heat-resistant alloy used for advanced ultra-supercritical power plant was investigated both experimentally and thermodynamically. Experimental results showed that the mechanical properties maintained excellent stability after long-term aging at 700 °C for 10,000 h, while the impact absorbing energy decreased sharply after 1000-h aging and then kept constant till 10,000?h. The main precipitates after long-term aging at 700 and 750? C were M23C6, MC and homogeneous γ′-phases. The mass fraction of M23C6 carbides increased with increasing aging time, and M23C6 carbides precipitated in shape of chains and lamellas on grain boundaries. The slight decrease in MC carbides during aging may be due to degradation reaction. The weight fraction of γ′-phase increased with the aging time, and then changed little after 5000 h; γ′-phase exhibited excellent microstructure stability and low coarsening rate during long-term aging at 700 °C. However, the coarsening rate of γ′-phase was much higher at 750 °C.
|
|
|
|
|
|
| Cite this article: |
|
Han‑sheng Bao,Gang Yang,Zheng‑zong Chen, et al. Effects of long term aging on microstructure and properties of a tungsten bearing heat resistant alloy[J]. Journal of Iron and Steel Research International, 2020, 27(4): 477-487.
|
|
|
|
| [1] |
Hou-long Liu, Ming-yu Ma, Ling-ling Liu, Liang-liang Wei, Li-qing Chen. Effect of W addition on hot deformation and precipitation behaviors of 19Cr2Mo ferritic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(5): 425-434. |
| [2] |
Yan-jun Xie, Huai-chao Yang, Xue-bing Wang, Lin Zhao, Chun-jiang Kuang, Wei Han. Control of wall thickness and surface morphology of tungsten thin wall parts by adjusting selective laser melting parameters[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(2): 182-190. |
| [3] |
Shan-shan Liu, Hai-yan Chen, Xuan Zhao, Li Fan, Xiao-ming Guo, Yan-sheng Yin. Corrosion behavior of Ni-based coating containing spherical tungsten carbides in hydrochloric acid solution[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(2): 191-199. |
| [4] |
Kai Ding Hui-jun Ji Xia Liu Peng Wang Quan-liang Zhang Xiao-hong Li Yu-lai Gao. Prevention of carbon migration in 9% Cr/CrMoV dissimilar welded joint by adding tungsten inert gas overlaying layer[J]. , 2018, 25(8): 847-853. |
| [5] |
Hong Li · Yuan Qin · Wei Cui · Man Yao · Xu-dong Wang · Hai-xuan Xu · Simon R. Phillpot. Effects of grain boundaries on irradiation-induced defects in tungsten by molecular dynamics simulations[J]. , 2018, 25(2): 200-206. |
| [6] |
Zhong-liang Tian,,Sen-bao Jiang,Zheng-zong Chen,Han-sheng Bao,Zheng-dong Liu,*. Microstructural evolution and mechanical properties of a new Ni-based heat-resistant alloy during aging at 750°C[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 513-519. |
|
|
|
|
2020, Vol. 27 