Effect of magnesium injection process on hot metal desulfurization |
Jian-ming Su1,2, Zhi-he Dou1, Ting-an Zhang1, Yan Liu1 |
1 Key Laboratory of Ecological Metallurgy of Multi-metal Intergrown Ores of Ministry of Education, Northeastern University, Shenyang 110819, Liaoning, China; 2 General Steelmaking Plant, Anshan Iron and Steel Group Co., Ltd., Anshan 114021, Liaoning, China |
|
|
Abstract To solve the technical problems of hot metal desulfurization by injecting magnesium particulate, a new method of hot metal desulfurization by bottom-blowing magnesium vapor combined with mechanical agitation was put forward. The effects of three different desulfurization processes on the desulfurization efficiency were studied in view of thermodynamics and kinetics. It was found that the utilization efficiency of magnesium can reach 82.6% and desulfurization efficiency can reach 86.2% during the first 4 min using the method of magnesium vapor injection combined with mechanical agitation. The gasification of magnesium powder leads to significant splashing and magnesium losses in the process of magnesium powder injection, resulting in a low utilization efficiency of magnesium of 51.8% and a low desulfurization efficiency of 55.76%. Activation energy for a first-order kinetic relationship between magnesium powder and sulfur was measured from the experiments, which was 142.82 kJ/mol in the temperature range of 1573–1723 K. The activation energy of the reaction between magnesium vapor and sulfur was around 54.8–65.0 kJ/mol in the temperature range of 1573–1723 K, which indicates that the desulfurization with magnesium vapor proceeds relatively easier than the desulfurization with magnesium powder.
|
|
|
|
|
Cite this article: |
Jian-ming Su,Zhi-he Dou,Ting-an Zhang, et al. Effect of magnesium injection process on hot metal desulfurization[J]. Journal of Iron and Steel Research International, 2020, 27(12): 1391-1399.
|
|
|
|
[1] |
Jian-ming Su, Zhi-he Dou, Ting-an Zhang, Yan Liu. Kinetics of hot metal desulfurization by bottom blowing magnesium vapor[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(4): 392-401. |
[2] |
Jian‑ming Su, Zhi‑he Dou, Ting‑an Zhang, Yan Liu. Physical simulation of bubble refinement in the bottom blowing process with mechanical agitation[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(10): 1137-1144. |
[3] |
Kang-hui Zhang, Yan-ling Zhang, Tuo Wu. Kinetics of hot metal desulfurization using CaO–SiO2–Al2O3–Na2O–TiO2 slag[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(10): 1041-1051. |
[4] |
Qing-min Meng . Jia-xin Li, . Ru-fei Wei . Hong-ming Long, . Tie-jun Chun . Ping Wan . Zhan-xia Di . Luana Dessbesell . Chunbao Xu. Effects of gangue compositions on reduction process of carbon-bearing iron ore pellets[J]. , 2018, 25(11): 1105-1112. |
[5] |
Jian DING,Qingcai LIU,Lijun JIANG,Guoqing LIU,Shan REN,Jian YANG,Lu YAO,Fei MENG. Thermal Behavior and Kinetics of Raw/Pyrolytic Wood and Coal Blends during Cocombustion Process[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 917-923. |
[6] |
Wen-jie WU , Hui-xiang YU, Xin-hua WANG, Hai-bo LI , Ke LIU. Optimization on Bottom Blowing System of a 210 t Converter[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 80-86. |
|
|
|
|