| Prediction and evaluation of optimum quenching temperature and microstructure in a 1300 MPa ultra-high-strength Q&P steel |
| Peng-fei Gao1,2, Ju-hua Liang1,2,3, Wei-jian Chen1,2, Feng Li1,2, Zheng-zhi Zhao1,2 |
| 1 Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China; 2 Beijing Laboratory of Metallic Materials and Processing for Modern Transportation, Beijing 100083, China; 3 Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031, Anhui, China |
|
|
|
|
Abstract The quenching and partitioning steel is the representative of the third generation of advanced high-strength steel. The effect of quenching temperature on the microstructure and mechanical property of ferrite-containing quenching and partitioning steel was studied by intercritical annealing quenching and partitioning processes. When preparing a test steel with a tensile strength of 1300 MPa and total elongation of 19%, it is found that the actual optimum quenching temperature was lower than that calculated according to the constrained carbon equilibrium. The results indicate that the martensite start temperature of the austenite was overestimated when considering the diffusion of carbon only. Austenite grain size which is affected by low temperature and the existence of ferrite during intercritical annealing influenced the optimum quenching temperature. A scheme considering the diffusion of various alloying elements and austenite grain size was proposed and verified. Using this scheme, the optimum quenching temperature of intercritically annealed quenching and partitioning steel with complex microstructures was well predicted.
|
|
|
|
|
|
| Cite this article: |
|
Peng-fei Gao,Ju-hua Liang,Wei-jian Chen, et al. Prediction and evaluation of optimum quenching temperature and microstructure in a 1300 MPa ultra-high-strength Q&P steel[J]. Journal of Iron and Steel Research International, 2022, 29(2): 307-315.
|
|
|
|
| [1] |
Li-ying Liu, Ping Yang, Dan-dan Ma, Xin-fu Gu. Surface effect induced phase transformation by Mn removal during annealing and its textures in cold-rolled high manganese transformation-induced plasticity steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 494-502. |
| [2] |
R.D. Liu, Y.Z. Li, L. Lin, C.P. Huang, Z.H. Cao, M.X. Huang. Strain rate sensitivity of a 1.5 GPa nanotwinned steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(11): 1352-1356. |
| [3] |
Ming-jie Qin, Xi Jin, Min Zhang, Hui-jun Yang, Jun-wei Qiao. Twinning induced remarkable strain hardening in a novel Fe50Mn20Cr20Ni10 medium entropy alloy[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(11): 1463-1470. |
| [4] |
Qi‑hang Pang, Mei Xu, Zhen‑li Mi, Juan Cui, Jing Guo. Microstructure evolution of ultra-high-strength twinning-induced plasticity (TWIP) steel under dynamic loading[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(1): 66-75. |
| [5] |
Jia-cheng Zhang, Tuo Zhang, Yi-tao Yang. Microstructure and properties evolution of Nb-bearing medium Cr wear-resistant cast steel during heat treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(06): 739-751. |
| [6] |
Chang-sheng Li, Bin-zhou Li, Xin Jin, Yu Wang. Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(03): 360-369. |
|
|
|
|
2022, Vol. 29 