| Precipitation behavior of P550 steel for non-magnetic drill collars during isothermal aging at 650–900 °C |
| Li-wei Xu1, Huai-bei Zheng2, Hua-bing Li1, Zhou-hua Jiang1, Shu-cai Zhang1, Jiang-tao Yu1, Hao Feng1, Yue Lin1 |
| 1 School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China 2 State Key Laboratory of Metal Material for Marine Equipment and Application, Anshan 114002, Liaoning, China |
|
|
|
|
Abstract Precipitation behavior of P550 steel for non-magnetic drill collars was investigated by microstructure characterization as well as thermodynamic calculation. The results demonstrate that the main precipitate formed at 650–900 °C was cellular Cr2N, and its precipitation depended heavily on the aging temperature. The most sensitive precipitation temperature of cellular Cr2N was 750 °C. At 750 °C, the cellular Cr2N exhibited fast-slow precipitation kinetics with the aging time prolonging. The initial precipitation of cellular Cr2N was governed by the short-range intergranular diffusion of Cr. During long-term aging, its growth was controlled by the long-range bulk diffusion of Cr. In addition, cellular Cr2N induced the precipitation of r phase ahead of the cell after long period of aging. Increasing the nitrogen content resulted in the increment of both the nucleation site and the driving force for the cellular Cr2N, which jointly promoted its precipitation.
|
|
|
|
|
|
| Cite this article: |
|
Li-wei Xu,Huai-bei Zheng,Hua-bing Li, et al. Precipitation behavior of P550 steel for non-magnetic drill collars during isothermal aging at 650–900 °C[J]. Journal of Iron and Steel Research International, 2022, 29(4): 636-646.
|
|
|
|
| [1] |
Xiao-lin Li, Chi Jin, Hao-zhe Li, Xiao-xiao Hao, Yi He, Xiang-tao Deng, Zhao-dong Wang. Influence of cooling rate on phase transformation and precipitation behavior of Ti-bearing steel in continuous cooling process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(01): 165-174. |
| [2] |
Ying‑cong Zhou, Yu Wang, Kuo‑chih Chou, Guo‑hua Zhang. Synthesis of high-quality ferrovanadium nitride by carbothermal reduction nitridation method[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(03): 255-262. |
| [3] |
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(7): 849-866. |
| [4] |
Li‑wei Xu, Hua‑bing Li, Huai‑bei Zheng, Peng‑chong Lu, Hao Feng, Shu‑cai Zhang, Wei‑chao Jiao, Zhou‑hua Jiang 1. Effects of nitrogen content on pitting corrosion resistance of non-magnetic drill collar steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(12): 1466-1475. |
| [5] |
Meng-du Peng, Jie Shi, Wen-chao Yu, Bing Cui, Ting Sun, Xiao-yuan Li, Mao-qiu Wang. Hot working process optimization of Fe–20Mn–19Cr–0.5C–0.6N steel by activation energy, power dissipation and microstructural evolution[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 856-865. |
| [6] |
Wen-shu Zhang, Cai-li Zhang, Nan Dong, Jian-guo Li, Pei-de Han, Zhu-xia Zhang, Li-xia Ling. Surface adsorption and diffusion of N on c-Fe–Al (111) using first principles calculations[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(8): 882-887. |
|
|
|
|
2022, Vol. 29 