Erosion–corrosion resistance of Mo–Ti- and Ni–Cr–Mo-alloyed medium-carbon martensitic steels: a critical analysis of synergistic effect of erosion and corrosion |
De-fa Li1, Hang-yu Dong2,3, Cheng-yang Hu2,3, Kai-ming Wu2, Serhii Yershov2, Oleg Isayev2 |
1 School of Mechanical and Vehicle Engineering, West Anhui University, Luan 237012, Anhui, China; 2 The State Key Laboratory of Refractories and Metallurgy, Hubei Province Key Laboratory of Systems Science on Metallurgical Processing, International Research Institute for Steel Technology, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China; 3 Laboratory for Excellence in Advanced Steel Research, Materials Science and Engineering Program, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, El Paso, TX 79968, USA |
|
|
Abstract Grain refinement renders Mo–Ti-alloyed medium-carbon martensitic steel to exhibit high hardness, high strength, and good toughness, but the erosion–corrosion resistance of steel in a corrosive slurry environment is not known. Mo–Ti-alloyed medium-carbon martensitic steel is compared with Ni–Cr–Mo-alloyed medium-carbon martensitic steel, and the erosion– corrosion resistance of those two steels under impingement by NaCl solution with gravels has been investigated. Three components, pure-corrosion rate, pure-erosion rate, and synergistic effect of erosion and corrosion (SEEC) of erosion– corrosion rate, were quantified. The pure-corrosion and pure-erosion rates of Mo–Ti-alloyed steel were higher than those of Ni–Cr–Mo-alloyed one; however, its erosion–corrosion rate was relatively lower because of a weak SEEC. Surface plastic deformation and work hardening due to gravel impingement were the essential reason for SEEC, which could be reduced by grain refinement, and consequently, Mo–Ti-alloyed steel with finer grains had better erosion–corrosion resistance. Grain refinement could be an effective way to improve the erosion–corrosion resistance of martensitic steels.
|
|
|
|
|
Cite this article: |
De-fa Li,Hang-yu Dong,Cheng-yang Hu, et al. Erosion–corrosion resistance of Mo–Ti- and Ni–Cr–Mo-alloyed medium-carbon martensitic steels: a critical analysis of synergistic effect of erosion and corrosion[J]. Journal of Iron and Steel Research International, 2022, 29(08): 1299-1311.
|
|
|
|
[1] |
Xiao-xiao Liu, Zheng Zhang, Jie Zhang, Ran Yang, Cheng-shuang Yu, Jun-wei Qiao, Li-na Han. Enhanced strength and toughness in 40CrNiMo steels by austempering below martensite start temperature[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(5): 810-818. |
[2] |
Xin-pan Yu, Hui-bin Wu, Yang Gu, Rui Yuan, You-you Zhang, Yu-hui Feng. Effect of prior martensite on bainite transformation and microstructure of high-carbon nano-bainitic steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(4): 647-654. |
[3] |
Peng-fei Gao, Ju-hua Liang, Wei-jian Chen, Feng Li, Zheng-zhi Zhao. Prediction and evaluation of optimum quenching temperature and microstructure in a 1300 MPa ultra-high-strength Q&P steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(2): 307-315. |
[4] |
Tian-peng Qu, De-yong Wang, Hui-hua Wang, Dong Hou, Jun Tian, Shao-yan Hu, Li-juan Su. Interface characteristics between TiN and matrix and their effect on solidification structure[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(9): 1149-1158. |
[5] |
Fei Zhu, Feng Chai, Xiao-bing Luo, Zheng-yan Zhang, Cai-fu Yang. Strengthening and toughening mechanism of a Cu-bearing highstrength low-alloy steel with refined tempered martensite/bainite (M/ B) matrix and minor inter-critical ferrite[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(4): 464-478. |
[6] |
Chang-sheng Li, Bin-zhou Li, Xin Jin, Yu Wang. Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(03): 360-369. |
|
|
|
|