Chromium enrichment in different crystalline phases of Cr-containing slag under various basicities and equilibrium temperatures |
Shao-wen Wu1, Yan-ling Zhang1, Shuai Zhang1 |
1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract The effects of basicities and equilibrium temperatures on the enrichment of chromium in different mineral phases of synthesized argon–oxygen decarburization slags were investigated to understand the Cr concentrating behavior into Mg(Cr,Al)2O4 spinel phase and to determine the leaching stability of Cr-containing slag. The results showed that when the basicity decreased from 1.0 to 0.6 and temperatures decreased from 1600 to 800 C, the Cr content of amorphous phase and crystalline phase gradually decreased, with a subsequent increase in the Cr content of spinel phase. The range of Cr enrichment in spinel of slags S1, S2, and S3 is 92.03–96.89, 91.63–96.36, and 90.67–95.42, respectively. The mass fraction and the size of spinel increased with the decreasing equilibrium temperatures, and the Cr leaching values decreased simultaneously. Therefore, the trend of the amount of Cr-related ions in the leachate was consistent with the trend of Cr in the amorphous phase, diopside, and akermanite. The results suggest that the lower basicity and equilibrium temperatures could be conducive to stabilizing Cr into spinel phase to minimize Cr leaching into the environment.
|
|
|
|
|
Cite this article: |
Shao-wen Wu,Yan-ling Zhang,Shuai Zhang. Chromium enrichment in different crystalline phases of Cr-containing slag under various basicities and equilibrium temperatures[J]. Journal of Iron and Steel Research International, 2022, 29(09): 1412-1422.
|
|
|
|
[1] |
Xin-li Song, Chang-hu Huang, Juan Jia, Jing Liu. Effect of strain rate on fracture behaviour of Cr18Ni11Ti stainless steel at high temperatures[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(6): 1004-1011. |
[2] |
Yu-jie Hong, Qing Liu, Jian-ping Yang, Jian Wang, Shan Gao, Hong-hui Li. Genetic optimization of ladle scheduling in empty-ladle operation stage based on temperature drop control[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(4): 563-574. |
[3] |
Shi-sen Li, Wan-ming Li, De-jun Li, Yu-lei Sun, Jun-wei Dong, Xi-tao Yin, Xi-min Zang. Determination of real-time oxygen transfer rate based on an electrochemical method[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 418-424. |
[4] |
Zhi-xiang Fu, Geng-wei Yang, Ru-yang Han, Yao-wen Xu, Xin-ping Mao, Si-qian Bao, Gang Zhao. Influence of coiling temperature on microstructure and mechanical properties of a hot-rolled high-strength steel microalloyed with Ti, Mo and V[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 484-493. |
[5] |
Ting-wei Ma, Xian-chao Hao, Ping Wang. Effect of heat treatments on Charpy impact properties of 15Cr12MoVWN ferritic/martensitic steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(3): 512-518. |
[6] |
Peng-fei Gao, Ju-hua Liang, Wei-jian Chen, Feng Li, Zheng-zhi Zhao. Prediction and evaluation of optimum quenching temperature and microstructure in a 1300 MPa ultra-high-strength Q&P steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(2): 307-315. |
|
|
|
|