| Distribution ratio of sulfur between high alumina slag and carbonsaturated iron |
| Shuai Wang1, Ying Jiang1, Yu-feng Guo1, Feng Chen1, Ling-zhi Yang1, Zhuang Yang1, Guang Li1 |
| 1 School of Minerals Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China |
|
|
|
|
Abstract High alumina slag is widely found in pyrometallurgical extractions of ferronickel, ferrochromium, and platinum group metals. The effects of MgO, Al2O3, and CaO/SiO2 on the sulfur distribution ratio between high-alumina CaO–SiO2–MgO–Al2O3 slag and carbon-saturated iron were investigated. The slag consisted of Al2O3 content in the range of 27.61–40.00 wt.%, CaO/SiO2 ratio of 0.8–1.1, and MgO content of 8–16 wt.%. The theoretical liquid areas of CaO–SiO2–MgO–Al2O3 slag were analyzed through the phase diagrams. The sulfur distribution ratio was measured via the slag–metal equilibrium technique at 1500 ºC. It was observed that the sulfur distribution ratio increased with higher MgO content and higher CaO/SiO2 ratio largely due to the increase in free O2- ions and the decrease in activity coefficient of sulfur ion in slag, but slightly decreased with the increasing Al2O3 content because of the decrease in free O2-.
|
|
|
|
|
|
| Cite this article: |
|
Shuai Wang,Ying Jiang,Yu-feng Guo, et al. Distribution ratio of sulfur between high alumina slag and carbonsaturated iron[J]. Journal of Iron and Steel Research International, 2023, 30(09): 1732-1742.
|
|
|
|
| [1] |
Kang-hui Zhang, Yan-ling Zhang, Tuo Wu. Kinetics of hot metal desulfurization using CaO–SiO2–Al2O3–Na2O–TiO2 slag[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(10): 1041-1051. |
| [2] |
REN Zhong-shan,,HU Xiao-jun,,CHOU Kuo-chih,. Calculation and Analysis of Sulfide Capacities for CaO-Al2O3-SiO2-MgO-TiO2 Slags[J]. Chinese Journal of Iron and Steel, 2013, 20(9): 21-25. |
| [3] |
XU Ji-fang,ZHANG Jie-yu,JIE Chang,TANG Lei,CHOU Kuo-chih,. Measuring and Modeling of Density for Selected CaO-MgO-Al2O3-SiO2 Slag With Low Silica[J]. Chinese Journal of Iron and Steel, 2012, 19(7): 26-32. |
| [4] |
WU Long,PEI Fen,CHEN Yu,LI Shi-qi. Experimental Study on Deep Desulfurizer in LF Process[J]. Chinese Journal of Iron and Steel, 2012, 19(4): 17-21. |
| [5] |
ZHANG Guo-Hua. Model for Evaluating Density of Molten Slag With Optical Basicity[J]. Chinese Journal of Iron and Steel, 2010, 17(4): 1-1. |
|
|
|
|
2023, Vol. 30 