| Mechanism and control of nonuniform phase transformation of microalloyed dual-phase steel during cooling process after hot rolling |
| Wen-quan Sun1, Sheng-yi Yong1, Tie-heng Yuan1, Chao Liu1, San-bao Zhou2, Rui-chun Guo1, Meng-xia Tang2 |
| 1 National Engineering Research Center for Advanced Rolling and Intelligent Manufacturing, University of Science and Technology Beijing, Beijing 100083, China 2 Strip Production Plant, Xichang Steel and Vanadium Corporation of Pangang Group, Xichang 615000, Sichuan, China |
|
|
|
|
Abstract After cooling in the hot rolling process, the metallographic structure of microalloyed dual-phase steel is nonuniform along the rolling direction, while the thickness fluctuation of microalloyed dual-phase steel with a nonuniform metallographic structure will occur during cold rolling. The mechanism of nonuniform phase transformation of microalloyed dual-phase steels was studied during the cooling process after hot rolling, and the nonuniform phase transformation of microalloyed dual-phase steel was regulated during the cooling process after hot rolling through process optimization. First, the empirical equation of phase transformation temperature was measured by a dilatometer considering thermal expansion. Then, the phase field and temperature field of laminar cooling process were calculated to provide initial boundary conditions for the finite element model. After that, the coupling finite element model of the temperature phase transformation of the strip steel in coiling transportation process was established. The simulation results show that the different thermal contact conditions of the microalloyed dual-phase steel during coil transportation lead to uneven cooling of the coil, which leads to nonuniform transformation of the coil along the rolling direction. In addition, by prolonging the time interval from coiling to unloading, the phenomenon of nonuniform phase transformation of microalloyed dual-phase steel can be effectively controlled. The simulation results are applied to industrial production. The application results show that prolonging the time interval from coiling to unloading can effectively improve the nonuniform phase transformation of microalloyed dual-phase steel in the cooling process after hot rolling.
|
|
|
|
|
|
| Cite this article: |
|
Wen-quan Sun1,Sheng-yi Yong1,Tie-heng Yuan1, et al. Mechanism and control of nonuniform phase transformation of microalloyed dual-phase steel during cooling process after hot rolling[J]. Journal of Iron and Steel Research International, 2024, 31(02): 428-441.
|
|
|
|
| [1] |
Wen-quan Sun, Sheng-yi Yong, Tie-heng Yuan, Ting-song Yang, An-rui He, Chao Liu, Rui-chun Guo. Effect of post rolling stress on phase transformation behavior of microalloyed dual phase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2024, 31(3): 688-699. |
| [2] |
Yu-chao Yao, Miao Liu, Zhong-qiu Liu, Bao-kuan Li, Yong Gan. Review on effect of applied internal cooling source and vibration on metal solidification process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1059-1072. |
| [3] |
Rui-song Tan, Wei Liu, Bo Song, Shu-feng Yang, Yong-feng Chen, Xiao-tan Zuo, Yan Huang. Numerical simulation on solidification behavior and structure of 38CrMoAl large round bloom using CAFE model[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(6): 1222-1233. |
| [4] |
Teng-fei Qi, Hai-feng Li, Jun-jie Sun, Guo-jun Chen, Yong-jie Zhang. Simulation of gas–solid flow in sinter vertical cooling furnace[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(11): 2133-2142. |
| [5] |
Wen-feng Gu, Jiang Diao, Rui-xin Hu, Wen-sun Ge, Wen-feng Tan, Hong-yi Li, Bing Xie. Solidification and heat transfer of molten steel slag particles during air quenching process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(09): 1834-1842. |
| [6] |
Xiao-han Wu, Zhi-gang Song, Bao-shun Wang, Ming-hua Wu, Qi-liang Nai, Liang Yao, Han Feng, Wen-jie Zheng. Morphologies of secondary austenite in 2507 duplex stainless steel after heat treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(6): 994-1003. |
|
|
|
|
2024, Vol. 31 