Causes and Improvement Measures on Edge Crack of Casting Blank
LIU Xian-ling1,ZHU Kai-jun1,ZHANG Zhi-wei2,WANG Wen-cai1
1. No.3 Steel Making Plant of Handan Iron and Steel Co., Ltd.,Handan 056015,Hebei, China 2. CSP Plants of Handan Iron and Steel Co., Ltd.,Handan 056015, Hebei, China
Abstract:The causes of edge crack for casting blank was discussed. The results showed that the cracks are connected with gas content of molten steel, mold oscillation parameters and process of secondary cooling system. The surface quality of casting blank is improved by strengthen protection cast process, optimization technological parameters, controlling straightening area temperature so that the edge crack rate of high strength ship plate is reduced from 4.5% to 1.8%.