1. Manufacturing and Management Department of Shanghai Meishan Iron and Steel Co.， LTD.， Nanjing 210039，Jiangsu，China 2. Steel Plant of Shanghai Meishan Iron and Steel Co.， LTD.， Nanjing 210039，Jiangsu， China 3. School of Materials and Metallurgy， Northeastern University， Shenyang 110819， Liaoning， China
Abstract：Low-carbon Al2O3-ZrO2-SiC-C refractories were fabricated via a reaction sintering process， using fused corundum， α-Al2O3， ZrSiO4， active carbon and natural graphite as main starting materials， nickel powder as additive. Phase composition， sintering properties and cold crushing strength were investigated. The research results show that the as-prepared refractories mainly consist of corundum， t-Zr0.92Y0.08O1.96， β-SiC and graphite. The sintering properties and crushing strength can be increased. The crushing strength of the sample doped with 5% nickel powder reaches 26.5 MPa， which is 2.6 times as high as that of the sample without nickel addition.
黄 海，周秀丽，马北越，刘鹏举，于景坤. 添加镍对低碳Al2O3-ZrO2-SiC-C连铸耐火材料制备及性能的影响[J]. 中国钢铁期刊网, 2015, 34(2): 10-14.
HUANG Hai，ZHOU Xiu-li，MA Bei-yue，LIU Peng-ju，YU Jing-kun. Effects of nickel addition on preparation and properties of low-carbon Al2O3-ZrO2-SiC-C refractories in continuous casting. Chinese Journal of Iron and Steel, 2015, 34(2): 10-14.
2015, Vol. 34 