汽车齿轮钢8620RH连铸坯中夹杂物研究

doi:10.13228/j.boyuan.issn1005-4006.20170035

摘要
图/表
参考文献
相关文章 (15)

全文: PDF (0 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要利用扫面电镜分析汽车齿轮钢8620RH连铸坯中氧化物夹杂的形貌和化学成分，结合具体的生产工艺，确定直径尺寸不小于25 μm的球状夹杂物是导致圆材B类夹杂物超标的主要原因，且此类夹杂物来源于炉渣。从提高精炼过程夹杂物去除效果和防止非稳态连铸过程卷渣，提高中包去除夹杂物能力等方面制定改善措施。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	作者相关文章
	安杰

关键词 ：汽车齿轮钢, 8620RH, 夹杂物

Abstract：Morphology and composition of oxide inclusions in gear steel 8620RH continuous cast billet were analyzed by SEM. Combining with specific production process， the main reason of causing overproof B inclusions rate in round steel was spherical inclusions with diameter dimension ≥25 μm， which came from slag. The improvement measures including increasing inclusion removal effect in refining process， preventing unsteady continuous casting process slag entrapment and improving inclusion removal effect of tundish， were made.

Key words： automobile gear steel 8620RH inclusion

收稿日期: 2017-03-06 出版日期: 2017-09-07

PACS:

TF762

引用本文:

李涛，孙大利，安杰. 汽车齿轮钢8620RH连铸坯中夹杂物研究[J]. 中国钢铁期刊网, 2017, 36(03): 39-42. LI Tao，SUN Da-li，AN Jie. Study on Inclusion of Automobile Gear Steel 8620RH in Continuous Cast Billet. Chinese Journal of Iron and Steel, 2017, 36(03): 39-42.

链接本文:

http://www.chinamet.cn/Jweb_lz/CN/10.13228/j.boyuan.issn1005-4006.20170035 或 http://www.chinamet.cn/Jweb_lz/CN/Y2017/V36/I03/39

[1]	张宝景,张朝发.钢的洁净度控制及生产新技术[J].金属材料及冶金工程,2010,38(6):11.
[2]	阿不力克木?亚森,刘洋,单以钢,等. 8620RH非调质钢全流程洁净度研究[J].炼钢,2015,31(6):40.
[3]	张海泉,谢有,成国光,等.含硫齿轮钢SAE8620H热轧棒材夹杂物[J].钢铁,2013,48(7):70.
[4]	李润霞.汽车用含硫齿轮钢洁净度控制研究[D].沈阳:东北大学,2010.
[5]	王琳松.水钢高效率低成本洁净钢生产[J].钢铁,2014,49(6):18.
[6]	赵克文,陈天明,杨素波,等.BOF-BCC流程生产高品质汽车齿轮钢实践[J].钢铁,2009,44(6):38.
[7]	徐匡迪,肖丽俊.特殊钢精炼中的脱氧及夹杂物控制[J].钢铁,2012,47(10):1.
[8]	张立峰,李燕龙,任英.钢中非金属夹杂物的相关基础研究(I)—非稳态浇铸中的大颗粒夹杂物及夹杂物的行核、长大、运动、去除和捕捉[J].钢铁,2013,48(11):1.
[9]	周伟基,魏仁杰,韩志远.高档汽车齿轮钢冶炼工艺研究[J].中国冶金,2013,23(8):5.
[10]	安杰,王哲,李润霞,李涛,丁克振,李如.汽车齿轮钢8620RH的洁净度[J].中国冶金,2016,26(9):33.