异型坯铸坯缺陷分析
高 仲,白居冰,张晓峰,李富帅,刘伟涛,刘洪波,倪赛珍
中冶连铸北京冶金技术研究院,北京 100028
Analysis on quality defect of beam blank
GAO Zhong,BAI Ju-bing,ZHANG Xiao-feng,LI Fu-shuai,LIU Wei-tao,LIU Hong-bo,NI Sai-zhen
Metallurgical technology research institute of CCTEC in Beijing, Beijing 100028, China
摘要 就异型坯铸坯质量较板坯和方坯常规坯型容易出现缺陷的现象,从异型坯连铸设备和异型坯连铸工艺特点方面分析了原因,并总结了解决异型坯相应铸坯缺陷的方向,最后提出在异型坯连铸设计工程中需重点考虑的事项。
关键词 :
异型坯 ,
连铸 ,
铸坯缺陷
Abstract :?According to the beam blank quality defects that easily produced than slab or bloom, this paper analysed the reasons from the beam blank caster and their characteristics, and summarized the methods that solved the cast product defect. Finally some key points that design the beam blank caster were presented.
Key words :
beam blank
continuous casting
quality defect
收稿日期: 2016-12-04
出版日期: 2017-09-07
[1]
钱凡,李化龙,杨文刚,郭海荣,刘国齐,李红霞,马北越. 添加剂对BN-ZrO2 陶瓷抗钢液侵蚀影响研究 [J]. 钢铁研究学报(英文版), 2022, 29(7): 1101-1109.
[2]
张翔,谢清华,倪培远,厉英. 全水口自旋流连铸水口钢水流动行为 [J]. 钢铁研究学报, 2022, 34(7): 629-638.
[3]
赵显久1,2,张捷宇2,3,李传军2,3. 冷轧薄板钙镁铝尖晶石类夹杂物成因分析 [J]. 钢铁研究学报, 2022, 34(7): 664-671.
[4]
商庭瑞, 王卫领, 康吉柏, 朱苗勇, 罗森. 20CrMnTi连铸瞬态与平均冷速条件下凝固原位观察 [J]. 钢铁, 2022, 57(7): 73-85.
[5]
陈斌, 李海波, 季晨曦, 刘国梁, 周海忱. 浇铸参数对结晶器液面波动影响及其工业应用 [J]. 钢铁, 2022, 57(7): 86-94.
[6]
康永林, 朱国明, 姜敏, 王国连, 刘彭涛, 徐海卫,谢翠红, 魏运飞, 沈开照, 刘洋. 板坯连铸大辊径大压下及低压缩比轧制特厚板 [J]. 钢铁, 2022, 57(7): 95-105.
[7]
程瑾琦,张立强,伏凯旋,赵傲南. 钢包长水口吹氩自动控制系统研究与应用 [J]. 钢铁研究学报, 2022, 34(6): 562-570.
[8]
吕迺冰, 高航, 刘珂, 刘斌, 徐士新, 周洁. 冷却强度对超高硫中碳钢方坯凝固过程MnS生长的影响 [J]. 钢铁, 2022, 57(6): 50-56.
[9]
宫佳睿,刘中秋,吴颖东,姚毓超,姜玖华,李宝宽. 连铸结晶器内弥散氩气泡的瞬态运动和捕捉行为 [J]. 钢铁研究学报, 2022, 34(5): 461-469.
[10]
周秋月, 朱坦华, 张立峰, 陈威, 袁天祥, 刘珍童. 非稳态浇铸对结晶器卷渣定量影响的大涡模拟 [J]. 钢铁, 2022, 57(4): 68-78.
[11]
李华刚. 板坯连铸铸流电磁搅拌辊的设计与应用 [J]. 连铸, 2022, 41(3): 56-64.
[12]
王志政, 钟鹏, 王欢. 双流板坯连铸机中间包系统优化 [J]. 连铸, 2022, 41(3): 65-70.
[13]
刘长伟, 邹卓明. 机器人自动加保护渣技术在宁波钢铁的应用 [J]. 连铸, 2022, 41(3): 71-75.
[14]
周干水, 张海洋, 宁曙光, 孙军, 陈阳, 肖海健. 热调宽技术在四台双流板坯连铸上的应用 [J]. 连铸, 2022, 41(3): 76-82.
[15]
谢建府, 隋亚飞, 邓之勋, 梁远栋, 陈佛望. 09CrCuSb热轧卷边部缺陷的成因分析 [J]. 连铸, 2022, 41(3): 89-96.