82B钢凝固传热过程对铸坯缺陷影响分析
田鹏
北京科技大学
the Effect Analysis of Solidification Heat Treatment on Slab Defects of 82B
Peng TIAN
摘要 连铸坯的中心偏析、裂纹、缩孔和疏松等缺陷是铸坯常见的内部缺陷,与钢液自身的性质密切相关。通过对82B钢连铸坯凝固传热过程的研究,分析钢的凝固特性与铸坯缺陷的关系,为改进连铸工艺提供依据。
关键词 :
凝固传热 ,
板坯缺陷 ,
连铸方坯
Abstract :The defects of the center segregation, cracks, shrinkage and loosening are common internal defects of the continuous casting billet and are closely related to the properties of the molten steel. Based on the study of the solidification heat transfer process of 82B continuous casting billet, the relationship between the solidification characteristics of steel and the defects of slab is analyzed, which provides the basis for improving the continuous casting process.
Key words :
solidification heat treatment
slab defect
continuous casting billet
收稿日期: 2017-07-17
出版日期: 2020-04-17
[1]
胡文广, 祭程, 朱苗勇. 重轨钢连铸大方坯凝固末端压下过程的数值模拟 [J]. 连铸, 2021, 40(4): 2-6.
[2]
阳剑,胡振伟,孟红记. 基于表面温度测量的连铸二冷动态控制模型 [J]. , 2019, 31(2): 113-116.
[3]
胡志勇, 陈兴华, 唐 萍, 侯自兵. 过热度对帘线钢连铸方坯碳偏析的影响 [J]. , 2017, 36(5): 12-16.
[4]
李静敏,李新文,安 航,王 睿. 150 mm圆坯连铸机提拉速实践 [J]. 中国钢铁期刊网, 2017, 36(1): 1-7.
[5]
刘 纲,李士琦,李京社,张兴中,张新建,常 进. 基于中间包冶金工艺优化对钢液温度场的研究 [J]. 中国钢铁期刊网, 2016, 35(6): 47-49.
[6]
常 毅, 侯自兵, 王 伟, 徐 云. 高碳钢方坯碳锰元素纵向分布及机理 [J]. 钢铁, 2016, 51(11): 43-48.
[7]
刘 纲,李京社,张兴中,张新建,刘 煜,张东升. 过热度对HRB400凝固传热的数值模拟研究 [J]. 中国钢铁期刊网, 2016, 35(1): 22-25.
[8]
郭 春,岳 峰,孙 涛,马忠存,李 瑛,郭 鑫. 大圆坯连铸传热数值模拟 [J]. 中国钢铁期刊网, 2016, 35(1): 35-39.
[9]
冯辉君 ,陈林根 ,丁泽民 ,孙丰瑞 . 基于热损失率目标的板坯连铸凝固传热过程多目标优化 [J]. 中国钢铁期刊网, 2014, 26(6): 31-37.
[10]
王 涛 , 张炯明 , 赵新凯 . 150 mm×150 mm方坯连铸机末端电磁搅拌及拉速对铸坯内部质量的影响 [J]. 中国钢铁期刊网, 2014, 33(6): 50-59.
[11]
冯辉君,陈林根,丁泽民,孙丰瑞. 基于Matlab的板坯连铸凝固传热过程及热损失研究 [J]. 中国钢铁期刊网, 2013, 32(6): 16-22.
[12]
杨跃标 祭程. 连铸动态二冷控制模型的开发与应用 [J]. 钢铁, 2010, 45(9): 48-48.
[13]
邹达基 邹宗树. 关于连铸凝固传热数值模拟中钢液有效导热系数的探讨 [J]. 中国钢铁期刊网, 2009, 28(6): 5-5.
[14]
刘纲. 应用Fluent对水平连铸40Cr管坯温度场分布及传热的研究 [J]. 中国钢铁期刊网, 2009, 28(3): 4-4.
[15]
阮晓明 阎朝红 梅峰 张炯明. 宝钢3#板坯连铸机凝固与传热模型开发 [J]. 中国钢铁期刊网, 2009, 28(3): 21-25.