Abstract:The metallurgical performances were systematically investigated the heavy reduction technology with the convex rollers for bloom continuous casting process with cross section of 320 mm×425 mm in Baowu Group Guangdong Shaoguan Iron and Steel Co., Ltd. China. It is shown that the strand internal quality including central prosity, shrinkage cavity and composition uniformity has been improved significantly after using the heavy reduction technology. Among these, the width of center segregation region in the strand longitudinal section reduced from 52 mm to 39 mm, the maximum value of carbon segregation in the strand decreased from 1.174 to 1.100. Accordingly, the width of porosity region decreased from 50 mm to 42 mm, and the porosity grade can be reduced by 0.5 for the rolling production with diameter of 90 mm.
刘成斌, 韦乾永, 曾令宇, 程晓文. 重压下工艺下大断面方坯内部质量改善研究[J]. 连铸, 2020, 39(1): 66-70.
Liu Cheng-bin, Wei Qian-yong, Zeng Ling-yu, Cheng Xiao-wen. Research on improvement of internal quality of large section billet under heavy pressing process. CONTINUOUS CASTING, 2020, 39(1): 66-70.
VLudlow, A Normanton, A Anderson,et al. Strategy to minimise central segregation in high carbon steel grades during billet casting[J]. Ironmaking & Steelmaking, 2005, 32(1): 68.
J I Cheng, WU Chen-hui, ZHU Miao-yong, Thermo-mechanical behavior of the continuous casting bloom in the heavy reduction process[J]. JOM, 2016, 68(12): 3107.
[8]
J I Cheng, WANG Zi-lin, WU Chen-hui, et al, Constitutive modeling of the flow stress of GCr15 continuous casting bloom in the heavy reduction process[J]. Metallurgical and Materials Transactions:B, 2018, 49(2): 767.
[9]
GUAN Rui, JI Cheng, ZHU Miaoyong, et al, Numerical simulation of V-shaped segregation in continuous casting blooms based on a microsegregation model[J]. Metallurgical and Materials Transactions:B, 2018, 49(5): 2571.
[10]
J I Cheng, L I Guoliang, WU Chenhui, et al, Design and application of CSC-Roll for heavy reduction of the bloom continuous casting process[J]. Metallurgical and Materials Transactions:B, 2019, 50(1), 110.
WU Chen-hui, JI Cheng, ZHU Miao-yong, Influence of differential roll rotation speed on evolution of internal porosity in continuouscasting bloom during heavy reduction, Journal of Material Processing Technology, 2019, 271: 651.