Formation and prevention of longitudinal surface cracks in peritectic steel slab |
|
|
|
Abstract Longitudinal crack is the most common surface defects arising in as-cast slabs. It is well-known that peritectic steel are particularly vulnerable to longitudinal cracking, this problem has long plagued the metallurgical workers. With the development of hot delivery and hot charging and thin slab continuous casting-continuous rolling technology, no defects casting billet production become even more important. Combined with previous studies and the author’s work, this paper discussed the formation of longitudinal cracks of peritectic steel and reviewed the countermeasures to prevent it. We hope this has some benefit for solve the problem of longitudinal crack on peritectic steel slab.
|
Received: 14 January 2010
|
|
|
|
[1] |
ZHAN Mei-zhu, WANG Sheng-dong, ZHANG Li-feng, CHEN Wei. Effect of casting speed on inclusions in continuous casting slab of peritectic tinplate steel[J]. CONTINUOUS CASTING, 2022, 41(3): 39-44. |
[2] |
MEI Ning, WANG Bao-dong, LIU Yan-qiang, XIAO Hua-sheng, ZHAO Lu-ming, YANG Chun-bao. Analysis on cause of peritectic steel breakout at slab joint in process of quick change of tundish[J]. CONTINUOUS CASTING, 2021, 40(3): 40-44. |
[3] |
ZHANG Chen, CAI De-xiang, XU Guo-dong, FAN Ying-tong. Development and application of mold flux for heavy plate peritectic steel[J]. CONTINUOUS CASTING, 2021, 40(2): 51-56. |
[4] |
LI Yu-di, ZHANG Fa-bin. Analysis of longitudinal cracks and optimization of mold flux for peritectic steel slab[J]. CONTINUOUS CASTING, 2021, 40(2): 57-60. |
[5] |
HONG Gang1, LIU Huasong1, DONG Yannan1, ZHENG Hongguang2, XU Guodong2, ZHANG Jiaquan1. Study on kinetics of austenite grain growth of microalloyed peritectic steels under high temperatures[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(12): 1270-1277. |
[6] |
ZHAI Bing-yu, ZHANG Lei, WANG Wan-lin. Optimization on comprehensive properties of mold fluxes for peritectic steel by CSP[J]. CONTINUOUS CASTING, 2020, 39(5): 30-37. |
|
|
|
|