| Causes and Countermeasures for Mould Copper Plate Cracking in High Speed Caster |
| WEN Weixin,DIAO Chengmin |
| The No.3 Steelmaking Plant of Jinan Iron and Steel Group Co., Jinan 250101,Shandong,China |
|
|
|
|
Abstract Mould copper plate cracking problems in the high speed slab caster at the No.3 Steelmaking Plant of Jinan Iron & Steel Group Co.are introduced and analyzed. Based on production practice, a series of countermeasures have been taken. Good results have been got.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
ZHOU Songbo1，ZHANG Liqin1,2，HU Feng1，YIN Chaochao1，ZHOU Wen1，WU Kaiming1,2,3. Effect of center microstructure on fracture mechanism of ultra-thick high strength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(6): 578-587. |
| [2] |
CHEN Kangyan1，HU Feng1,2，ZHOU Songbo1，ZHOU Wen1，PAN Xianming4，WU Kaiming1,2,3. Effect of strain rate on strength and plasticity of medium carbon lowtemperature bainitic steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(4): 361-370. |
| [3] |
ZHAN Mei-zhu, WANG Sheng-dong, ZHANG Li-feng, CHEN Wei. Effect of casting speed on inclusions in continuous casting slab of peritectic tinplate steel[J]. CONTINUOUS CASTING, 2022, 41(3): 39-44. |
| [4] |
GAO Long-yong. Control measures and formation mechanism about edge-crack of hot-rolling coil of midium carbon steel[J]. CONTINUOUS CASTING, 2022, 41(3): 45-50. |
| [5] |
LIU Liang. Analysis and control over formation cause of surface longitudinal crack for continuous casting bloom of sulfur bearing steel[J]. CONTINUOUS CASTING, 2022, 41(3): 51-55. |
| [6] |
XIE Jian-fu, SUI Ya-fei, DENG Zhi-xun, LIANG Yuan-dong, CHEN Fo-wang. Cause analysis of edge defects of 09CrCuSb hot rolled coil[J]. CONTINUOUS CASTING, 2022, 41(3): 89-96. |
|
|
|
|
2009, Vol. 28 