Analyse and Measures of Surface longitudinal cracks of Steel Sheet in CSP production |
|
|
|
Abstract Surface longitudinal crack were studied and analized for SS400 steel sheet which occurred during CSP manufacture in this paper.The results demonstrated that most of the longitudinal cracks were distributed of 1/4 areas along the width direction of the steel sheet as parallel beam or reticulate form.The length and the depth of the cracks were 0.5-2mm and 0.1-0.2mm and the width was less than 1mm.Complex inclusions which composed of Na、Mg、Al、Si、Cl、K、Ca ets were found along the trench of the cracks, while only ferric oxide was found inside the cracks.Further analysis showed that such surface cracks originally formed in the successive mouldand further enlarged by the following secondary cooling and furnace heating. By controlling of the mould heat transfer and adjusting of secondary water cooling, longitudinal crack of steel sheet was controlled.
|
Received: 25 September 2009
|
|
|
|
[1] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[2] |
FAN Xiaohui, FANG Tianren, HUANG Xiaoxian, CHEN Xuling, WANG Xin. Thermal parameters optimization for gratekiln production process based on soft measurement of pellet temperature[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(6): 514-522. |
[3] |
FU Zhixiang1,2,YANG Gengwei1,2,XU Yaowen1,2,HU Zhuoli1,2,YIN Qilong1,2,ZHAO Gang1,2. Study on dynamic recrystallization behavior of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(6): 596-604. |
[4] |
SONG Mingming1,2, MEN Chaoqi1,2, XIE Yumin1,2, ZHU Hangyu1,2, MA Guojun1,2, XUE Zhengliang1,3. Application of automatic statistics in inclusion analysis[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(4): 334-340. |
[5] |
GAO Long-yong. Control measures and formation mechanism about edge-crack of hot-rolling coil of midium carbon steel[J]. CONTINUOUS CASTING, 2022, 41(3): 45-50. |
[6] |
JIN Xinyan,BI Wenzhen,WANG Li. Application of grain characteristic in analysis of
surface defects on automotive steel sheets [J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(3): 35-44. |
|
|
|
|