Test and Analysis of SS400B Plate Edge Defect |
LI Ji-dong1,XU Qing-tai1,SUN Zhong-qiang1,DOU Wei-xue2,ZHANG Peng-fei2,BAI Jin-en2 |
1. Northeastern University Metallurgical Technology Institute, Shengyang 110004, Liaoning, China 2. Hebei Iron and Steel Group Jingye Iron and Steel Institute, Shijiazhuang 050400, Hebei, China |
|
|
Abstract Abstract:Defect of SS400B plate edge with 45mm in thickness was tested and analyzed by macroscopic observation, metallography, SEM(Scanning Electron Microscope) and EDS(Energy Dispersive Spectrometer).The results showed that there were oxidation, decarburization and non-metallic inclusions near the defect, and some bubbles remained in the matrix after rolling, which indicated that the bubbles on the continuous casting slab surface and pinholes were the main cause of the defect on plate’s edge.
|
Received: 04 November 2011
Published: 24 July 2012
|
|
|
|
[1] |
WEN Xin1,REN Ying1,ZHANG Lifeng2. Cleanliness of GCr15 bearing steel refined by RH and VD vacuum processes[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 613-621. |
[2] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[3] |
YANG Jian, LI Ting-ting. Research progress on inclusion control of non-oriented silicon steel with REM treatment[J]. Iron and Steel, 2022, 57(7): 1-15. |
[4] |
DU Yi-nuo, GUO Lei, YANG Yang, ZHANG Shuai, YU Han-zhang, GUO Zhan-cheng. Numerical simulation of inclusions floating behavior under supergravity field in liquid steel[J]. Iron and Steel, 2022, 57(7): 54-62. |
[5] |
GUO Shuai, ZHU Hang-yu, ZHOU Jie, DONG Shuai, LIANG Yin. Effects of inclusions on stress field in low-density steel under compressive loading[J]. Iron and Steel, 2022, 57(7): 63-72. |
[6] |
LI Jipeng1,2, WANG Liang1, CHENG Shusen1, LIU Zhao1, CHEN Haoyu1, LIU Yong1. Thermodynamic study on calcium treatment of “liquid phase window” and inclusions modification[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(6): 523-533. |
|
|
|
|