Cause Analysis and Improvement Measures on Round Billet Continuous Casting Slab Jitter |
JING Su-dong,HUANG Jian-jun,ZHANG Xin-wen,DU Zhi-ming |
Baoshan Iron and Steel Co., Ltd., Nantong, Nantong 226002, Jiangsu, China |
|
|
Abstract In this investigationcauses for casting billet jitter were analyzed and improvement measures were proposed under the consideration of actual situation. Result shows that, in two strand cold chamber the jitter is due to equipment precision and overlarge taper of the crystallizer copper tube. For the production of No.20, 16Mn, 37Mn5 shell which is relatively soft and ductile, jitter does not occur or only slight jitter occurs; but for the production of 40Mn2, 26CrMo, 27CrMo44 which have higher strength and hardness, severe wobble occurs. The using of low viscosity, low melting slag can increase lubrication performance and reduce billet jitter obviously, but fails to eradicate jitter.
|
Received: 12 November 2012
Published: 25 July 2013
|
|
|
|
[1] |
ZHOU Gan-shui, ZHANG Hai-yang, NING Shu-guang, SUN Jun, CHEN Yang, XIAO Hai-jian. Application of online hot width adjustment in four slab casters at FENGNAN[J]. CONTINUOUS CASTING, 2022, 41(3): 76-82. |
[2] |
LIU Yanjie,YU Tongxin,SHU Jintao,LIU Yi,FAN Liuming,AN Tanglin. Research of high-throughput hardness tester[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(3): 9-12. |
[3] |
YUAN Peng-fei, JIANG Zhao-hui, ZHAO Hai-ming. Cause analysis and control of intermediate crack in Q345B continuous casting slab[J]. CONTINUOUS CASTING, 2021, 40(4): 38-42. |
[4] |
WANG Miao, LI Sheng-li, GAO Chuang, FAN Yue. End-point prediction TSVR model accuracy of 80 t BOF steelmaking[J]. Iron and Steel, 2020, 55(7): 53-57. |
[5] |
HU Jiao, MEI Feng, FENG Chang-bao. Causes and improvement of side crack formation in low carbon boron steel[J]. CONTINUOUS CASTING, 2020, 39(4): 60-65. |
[6] |
SUN Li-gang, JIA Sheng, LI Xin. Causes and control of surface crack on continuous casting billets of wide and thick plates[J]. CONTINUOUS CASTING, 2020, 39(4): 70-73. |
|
|
|
|