| Finite element analysis of soft reduction for round bloom continuous casting |
| CAO Xue-qian，WANG Ying，CHEN Jie |
| （Steelmaking and Continuous Casting Engineering Division， Capital Engineering and Research Inc. Ltd.， Beijing 100176， China） |
|
|
|
|
Abstract Based on the round bloom continuous caster， the finite element model of soft reduction was established， it found that the change for transformation of bloom on the various reduction amount. The results show that： 1） the reduction can be passed to the bloom core when solid fraction is above 0.35 and reduction amount of the single roll has to be greater than 10mm. 2）According to the design standard of the continuous caster， when the surface strain value of the slab exceeds 0.015， the surface of the slab is incline to appear cracks， so the maximum reduction of single roll should not exceed 8mm. Therefore， round bloom that be produced in a conventional manner is not suitable for the implementation of the soft reduction process. By adjusting the technological means or adding equipment to facilitate the soft reduction of round billets， it is necessary to study in subsequent work.
|
|
Received: 03 April 2018
Published: 29 September 2018
|
|
|
|
|
|
| [1] |
Tooru MATSUMIYA. Recent Topics of Research and Development in Continuous Casting [J], ISIJ International, 2006; 46: 1800-1804．
|
| [2] |
Ralf THOME and Klaus HARSTE. Principles of Billet Soft-reduction and Consequences for Continuous Casting [J], ISIJ International, 2006; 46: 1839-1844．
|
| [3] |
Chang Hee YIM, et al. The Effect of Soft Reduction on Center Segregation in C.C. Slab [J], ISIJ International, 1996; 36: S231-S234．
|
| [4] |
方文勇, 吴迪平, 秦勤. 方坯连铸动态轻压下的研究[J], 冶金设备, 2005, 12(6): 18-21．
|
| [5] |
曹学欠. 280mm×325mm大方坯连铸动态轻压下压下模型的研究与应用[D], 沈阳: 东北大学, 2009．
|
| [1] |
Fan Qian, Hua-long Li, Wen-gang Yang, Hai-rong Guo, Guo-qi Liu, Hong-xia Li, Bei-yue Ma. Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1101-1109. |
| [2] |
ZHANG Xiang，XIE Qinghua，NI Peiyuan，LI Ying. Flow behavior of molten steel in SEN during fullnozzle selfswirling flow continuous casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 629-638. |
| [3] |
ZHAO Xianjiu1,2，ZHANG Jieyu2,3，LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
| [4] |
GUO Shuai, ZHU Hang-yu, ZHOU Jie, DONG Shuai, LIANG Yin. Effects of inclusions on stress field in low-density steel under compressive loading[J]. Iron and Steel, 2022, 57(7): 63-72. |
| [5] |
SHANG Ting-rui, WANG Wei-ling, KANG Ji-bai, ZHU Miao-yong, LUO Sen. In situ observation of solidification under transient and average cooling rate of 20CrMnTi continuous casting[J]. Iron and Steel, 2022, 57(7): 73-85. |
| [6] |
CHEN Bin, LI Hai-bo, JI Chen-xi, LIU Guo-liang, ZHOU Hai-chen. Influence of casting parameters on level fluctuations and its industrial application[J]. Iron and Steel, 2022, 57(7): 86-94. |
|
|
|
|
2018, Vol. 37 