Practical study on control of corner crack breakout of Malaysia stander C12D steel billet |
CHEN Rong-kai,LIU Kun |
(Alliance Steel (M) Sdn. Bhd., peheng 26150, Malaysia) |
|
|
Abstract The standard C12D steel in Malaysia belongs to the peritectic steel. The 7 machine and 7 flow 8 m arc square billet caster is used to produce the continuous casting billet of C12D steel (165 mm×165 mm) in United Steel. The main problem in the production is the longitudinal crack in the inner arc, which directly causes the leakage of steel and affects the smooth production of the normal production. In order to solve the problem of longitudinal cracks in continuous casting billets, the mechanism of crack morphology, microstructure and crack formation in continuous casting C12D steel was studied. By adjusting the composition of molten steel, the overheat of molten steel, the selection of the slag, the adjustment of the cooling water and the speed of drawing, the goals of controlling the longitudinal crack in the corner of the casting billet and stabilizing the production are achieved.
|
Received: 30 July 2018
Published: 29 January 2019
|
|
|
|
[1] |
Fan Qian, Hua-long Li, Wen-gang Yang, Hai-rong Guo, Guo-qi Liu, Hong-xia Li, Bei-yue Ma. Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2022, 29(7): 1101-1109. |
[2] |
ZHANG Xiang,XIE Qinghua,NI Peiyuan,LI Ying. Flow behavior of molten steel in SEN during fullnozzle selfswirling flow continuous casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 629-638. |
[3] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[4] |
SHANG Ting-rui, WANG Wei-ling, KANG Ji-bai, ZHU Miao-yong, LUO Sen. In situ observation of solidification under transient and average cooling rate of 20CrMnTi continuous casting[J]. Iron and Steel, 2022, 57(7): 73-85. |
[5] |
CHEN Bin, LI Hai-bo, JI Chen-xi, LIU Guo-liang, ZHOU Hai-chen. Influence of casting parameters on level fluctuations and its industrial application[J]. Iron and Steel, 2022, 57(7): 86-94. |
[6] |
KANG Yong-lin, ZHU Guo-ming, JIANG Min, WANG Guo-lian, LIU Peng-tao, XU Hai-wei, XIE Cui-hong, WEI Yun-fei, SHEN Kai-zhao, LIU Yang. Slab continuous casting by big roll heavy reduction and extra thick plate rolled by low compression ratio[J]. Iron and Steel, 2022, 57(7): 95-105. |
|
|
|
|