Research and practice on corner scarring defect of continuous casting slabs |
XU Li-ping1,WANG Hong-feng2 |
(1. China Iron and Steel research institute group, Beijing 100081,China 2. Baosteel Meishan Iron and SteelCo., Ltd., Nanjing 210039, Jiangsu, China) |
|
|
Abstract In this paper, the formation procedure and mechanism of scarring defects at the corners of slabs produced by Baosteel Meishan Steelmaking plant were systematically investigated. It preliminarily found that the scarring defects formed at the mold meniscus through analysis to macroscopic morphology with field tracking. And it was ascribed to the overflow of solidification furrow at the corner of shell caused by the rupture, overflow and condensation of the primary shell of the meniscus. According to the analysis, the following measures are suggested to diminish the defects: the sinterability of mold powder should be reduced. While the deviation of crystallizer vibration as well as the cooling homogeneity should also be strictly controlled. Thus, the quality of the mold copper plate and the functional accuracy of the equipment related to the forces of the primary shell in the mold must be guaranteed. The corner scarring defects of slabs then will be diminished
|
Received: 04 September 2018
Published: 28 February 2019
|
|
|
|
[1] |
蔡开科.《连铸结晶器振动与铸坯表面质量》.冶金工业出版社,2016年
|
[2] |
迟景灏.《连珠保护渣》. 东北大学出版社, 1993年
|
[1] |
CHEN Bin, LI Hai-bo, JI Chen-xi, LIU Guo-liang, ZHOU Hai-chen. Influence of casting parameters on level fluctuations and its industrial application[J]. Iron and Steel, 2022, 57(7): 86-94. |
[2] |
GONG Jiarui,LIU Zhongqiu,WU Yingdong,YAO Yuchao,JIANG Jiuhua,LI Baokuan. Transient movement and capture behavior of dispersed argon bubbles in continuous casting mold [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 461-469. |
[3] |
ZHOU Qiu-yue, ZHU Tan-hua, ZHANG Li-feng, CHEN Wei, YUAN Tian-xiang, LIU Zhen-tong. Large eddy simulation on quantitative influence of unsteady casting on mold slag entrainment[J]. Iron and Steel, 2022, 57(4): 68-78. |
[4] |
LIU Yan-bin, TANG Hai-yan, WANG Kai-min, MA Yu, SHANG Guang-hao, ZHANG Li-ping, ZHANG Jia-quan. Effect of submerged entry nozzle structures on liquid surface flow behavior of slab continuous casting mold[J]. CONTINUOUS CASTING, 2022, 41(3): 1-10. |
[5] |
LIU Tong-wei, ZHANG Yan-chao, ZHANG Cai-jun, ZHAI Jin-jun. Study on fluctuation behavior of mold steel slag surface under blowing conditions[J]. CONTINUOUS CASTING, 2022, 41(3): 18-24. |
[6] |
LIU Chang-wei, ZOU Zhuo-ming. Application of robot automatic mould fluxes adding technology in Ningbo Iron and Steel Works[J]. CONTINUOUS CASTING, 2022, 41(3): 71-75. |
|
|
|
|