Research of slab segregation of dual phase steel for automobiles |
YANG Jie1, YAO Hai-ming2, LÜ Hao1, MA De-gang1, LI Jing-zhe1 |
1. HBIS Group Tanggang Company, Tangshan 063016, Hebei, China;
2. Department of Mechanical Engineering, Tangshan Industry and Profession Technology Academy, Tangshan 063299, Hebei, China |
|
|
Abstract The research of slab internal segregation of DP780 was carried out for finding the influence of process conditions of continuous casting and the cause of banded structure. Test equipments and test methods of original pisition analysis, drilling cutting composition testing, optical microscope and scanning electron microscopy (SEM) were used, the influence of tundish superheat, casting speed on slab macrosegregation was analyzed, the influence of secondary cooling ratio and tundish superheat on primary and secondary dendrite spacing was analyzed, and the influence of slab dendrite segregation on banded structure of hot rolled plate was studied, mechanism and countermeasures has been clear about banded structure happening of dual phase steel. The results showed that the degree of superheat was less than 30 ℃, the level of slab center segregation of dual phase steel could be controlled under C1.0, center equiaxial grain ratio could reach 12.25%. Casting speed had little influence on the center equiaxial grain ratio of slab. Primary and secondary dendrite spacing of dual phase steel slab were reduced by reducing superheat and improving secondary cooling ratio.
|
Received: 02 July 2020
Published: 23 February 2021
|
|
|
|
[1] |
康永林,邝霜,尹显东,等. 汽车用双相钢板的开发与研究进展[J].汽车工艺与材料,2006 (5):1.
|
[2] |
周晓光,田壵,郝紫勋,等. 热轧双相钢生产现状、存在问题及发展趋势浅析[J].轧钢,2020,37(1):61.
|
[3] |
王健,房锦超,张玉文. 热轧双相钢DP600关键工艺技术[J].中国冶金,2014,24(11):42.
|
[4] |
黄群飞,何燕霖,李麟. 高性能双相钢的研究进展[J].热处理技术与装备,2007,28(3):11.
|
[5] |
利成宁,袁国,周晓光,等. 汽车结构用热轧双相钢的生产现状及发展趋势[J].轧钢,2012,29(5):38.
|
[6] |
田志强,唐荻,江海涛,等. 汽车用双相钢的研究与生产现状[J].机械工程材料,2009,33(4):1.
|
[7] |
柳得橹,邵伟然,孙贤文,等. 钢的表面带状组织及其引起的冷弯裂纹[J].北京科技大学学报,2005,27(1):40.
|
[8] |
张迎晖,赖泓州,赵鸿金. 钢中带状组织的研究现状[J].轧钢,2014,31(3):45.
|
[9] |
龙明建,王自荣,张丽琴,等. 低碳高锰热轧带钢带状组织控制实践[J]. 轧钢,2015,32(4):84.
|
[10] |
汪洪峰,陶林,王勇. 高强钢连铸板坯中心偏析的分析及改善措施[J]. 连铸,2017 (5):34.
|
[11] |
陈亮,宋波,陈天明,等. 320 mm×410 mm断面重轨钢连铸坯宏观偏析控制关键技术[J]. 连铸,2017 (4):43.
|
[12] |
段永卿,王建锋,郭朝军. 重轨钢连铸坯中心偏析的分析和工艺改进[J]. 特殊钢,2016,37(1):27.
|
[13] |
刘洋,王新华,张开钧. 含铌钒钛微合金化钢连铸板坯中心偏析的影响因素[J]. 北京科技大学学报,2007,29(9):898.
|
[14] |
李论.浅析连铸坯的中心偏析[J]. 连铸,2009 (2):39.
|
[15] |
王臻明,赵晶,王玉龙,等. 400 mm特厚板坯中心偏析控制的研究[J]. 连铸,2019 (6):47.
|
[16] |
钟晓丹,刘军,邹宗树. 改善350 mm×470 mm矩形坯宏观偏析研究与实践[J]. 连铸,2016 (2):62.
|
[17] |
唐恩,许中波,王海涛,等. 高碳钢小方坯中成分偏析情况的研究[J]. 连铸,2004(6):34.
|
[18] |
李荣祥,范建通. 用金属原位分析仪研究42CrMo钢连铸坯的偏析[J]. 河北冶金,2013(5):7.
|
[19] |
左小坦,陈永峰,张洪彪,等. 连铸工艺参数对40Cr圆坯碳偏析的影响[J]. 中国冶金,2020,30(6):97.
|
[20] |
杨恩蛟,姜敏,侯泽旺,等. 连铸板坯凝固末端大压下改善铸坯内部质量[J]. 中国冶金,2020,30(5):23.
|
[21] |
李京社,汪庆国,唐海燕,等. 82B铸坯碳硫偏析和低倍缺陷控制的试验研究[J]. 连铸,2011(增刊1):341.
|
[22] |
周景龙,齐力军. 高碳钢小方坯二次枝晶间距与P偏析的关系[J].重型机械,2013 (4):33.
|
[23] |
张延玲,刘海英,阮小江,等. 中低碳齿轮钢中合金元素的偏析行为及其对带状组织的影响[J].北京科技大学学报,2009,31(增刊1):204.
|
[24] |
田亚强,宋进英,魏英立,等. 控轧控冷工艺对J55石油套管用钢带状组织影响[J].塑性工程学报,2011,18(6):111.
|
[25] |
纪元,闵云峰,李鹏善,等. 钢中带状组织及其研究现状[J].中国冶金,2016,26(4):7.
|
[1] |
ZHANG Wei, PAN Yue, LIU Hua-sai, LI Chun-guang, CHEN Hong-sheng. Effect of strain rate on properties of dual phase steel with high formability[J]. Iron and Steel, 2022, 57(4): 123-129. |
[2] |
LIU Liang. Analysis and control over formation cause of surface longitudinal crack for continuous casting bloom of sulfur bearing steel[J]. CONTINUOUS CASTING, 2022, 41(3): 51-55. |
[3] |
ZOU Lei-lei, HUANG Jun-xiong, LI Quan-hui, ZHANG Jiang-shan, LIU Qing. Research progress on the crack and segregation prediction of continuous casting strand[J]. CONTINUOUS CASTING, 2022, 41(2): 2-9. |
[4] |
DENG Xiao-xuan, LI Hai-bo, JI Chen-xi, CHEN Bin, ZHU Guo-sen. Three-dimensional distribution on macro inclusions in surface layer of IF steel slabs[J]. CONTINUOUS CASTING, 2022, 41(2): 35-40. |
[5] |
WU Xu-feng, ZHANG Cai-gui, WANG De-yong. Effect slag modification on vortex entrapment in ladle[J]. CONTINUOUS CASTING, 2022, 41(2): 41-46. |
[6] |
ZHANG Hao-hao, WU Jia-lu, LONG Mu-jun, GUO Wei, YANG Xiao-dong, CHEN Deng-fu. Evolution of micron Ti(Cx,N1-x) in TSCR process of ultra-high strength hot stamping steel[J]. CONTINUOUS CASTING, 2022, 41(2): 47-54. |
|
|
|
|