Analysis and control of longitudinal crack on hot rolled coil in CSP plant of Baotou Steel |
MA Chao, SUN Li-gang, ZHANG Wei, GUAN Sheng, JIA Gui-jun |
CSP Plant, Baotou Iron and Steel Group Co., Ltd., Baotou 014010, Nei Mongol, China |
|
|
Abstract In order to study the cause of longitudinal crack defect of hot rolled coil in CSP production line of thin plate factory, continuous casting process and operating parameters of equipment were investigated and analyzed. The results show that the poor vibration accuracy of vibrating table of continuous casting machine and scaling of the copper plate in the mould are the main reasons for the longitudinal crack of hot rolling.After adjusting the vibration parameters, improving the alignment accuracy of the shaking table and controlling the scale formation of the copper plate, the longitudinal crack defect on the surface of the hot rolled coil plate was reduced, and the longitudinal crack rate decreased from the highest 1.15% to less than 0.10%.In view of CSP casting machine, on the premise of ensuring good thermal conductivity of the mould copper plate, the joint bearing clearance of the four-link mechanism of the mould vibrator should be strictly controlled within 0.02 mm.Elevation deviation of shaking table should be strictly controlled within 0.05 mm.Horizontal displacement of mould vibration is suggested to be controlled within 0.1 mm.
|
Received: 08 April 2020
|
|
|
|
[1] |
张剑君,毛新平,王春峰,等.薄板坯连铸连轧炼钢高效生产技术进步与展望[J].钢铁,2019,54(5):1.
|
[2] |
郭海峰,张志克,唐章印.邯钢CSP连铸机常见漏钢形式以及预防措施[J].冶金管理,2019(11):60.
|
[3] |
隋亚飞,徐刚军,周军军,等.CSP含铝电工钢水口堵塞问题的研究和解决[J].连铸,2019,44(4):1.
|
[4] |
谭文,韩斌,蔡珍,等.武钢CSP短流程优质中高碳钢的开发及应用[J].轧钢,2017,34(6):10.
|
[5] |
肖尊湖,隋亚飞,刘彭,等.CSP工艺含铝无取向电工钢中夹杂物的演变和控制[J].钢铁,2019,54(7):42.
|
[6] |
韩玉龙,高军,乔继强.CSP流程无取向硅钢中间品处理方案[J].轧钢,2019,36(2):67.
|
[7] |
李瑞生,赵艳良,罗北平,等.连铸二级系统升级及拓展的探讨与实践[J].中国冶金,2018,28(12):60.
|
[8] |
杨婷. 薄板坯连铸-连轧技术的发展[J]. 世界金属导报,2017-01-24(B03).
|
[9] |
George Gurley. 水处理对CSP钢厂产品质量和产能的影响[C]//第十七届(2013年)全国炼钢学术会议论文集:B卷.杭州:中国金属学会,2013:807.
|
[10] |
蔡开科. 连铸坯质量控制[M].北京:冶金工业出版社,2010.
|
[1] |
FU Zhixiang1,2,YANG Gengwei1,2,XU Yaowen1,2,HU Zhuoli1,2,YIN Qilong1,2,ZHAO Gang1,2. Study on dynamic recrystallization behavior of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(6): 596-604. |
[2] |
LIU Liang. Analysis and control over formation cause of surface longitudinal crack for continuous casting bloom of sulfur bearing steel[J]. CONTINUOUS CASTING, 2022, 41(3): 51-55. |
[3] |
XIE Jian-fu, SUI Ya-fei, DENG Zhi-xun, LIANG Yuan-dong, CHEN Fo-wang. Cause analysis of edge defects of 09CrCuSb hot rolled coil[J]. CONTINUOUS CASTING, 2022, 41(3): 89-96. |
[4] |
GONG Bin. Control and application on R-angle longitudinal crack of microalloyed near-net-shape bream blank[J]. CONTINUOUS CASTING, 2022, 41(1): 62-66. |
[5] |
QIAO Tong,HUANG Yu,CHENG Guoguang,BAO Daohua,DAI Weixing. Characteristics and causes of surface peeling defects on hotrolled sheet of 2507 duplex stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(8): 851-861. |
[6] |
YANG Zhi-gang, XU Zi-qian, HUANG Wei-li, DONG Gen-lai, HUO Li-qiao. Research and control of longitudinal corner cracks in continuous casting slab[J]. CONTINUOUS CASTING, 2021, 40(6): 71-75. |
|
|
|
|