Causes and improvement of side crack formation in low carbon boron steel |
HU Jiao1, MEI Feng2, FENG Chang-bao1 |
1. Baosteel Zhanjiang Iron and Steel Company, Zhanjiang 524072, Guangdong, China; 2. Baoshan Iron and Steel Company, Shanghai 200941, China |
|
|
Abstract In order to solve the problem of side crack of low carbon boron steel, industrial experiments were carried out. The results show that the poor performance of the mold power can easily lead to the uneven shell and the stress concentration, resulting in the formation of slab side cracks; The condition of casting machine, such as mold oscillate, the arc state of mold and bending, has a great influence on the crack sensitive side crack of low carbon boron steel; Components N and B further aggravate the side crack of low carbon boron steel.After adopting measures such as mold power optimization, equipment state adjustment, composition control, the steel block rate of edge warping in the hot rolling plant decreased by 2.35%.
|
Received: 20 April 2020
|
|
|
|
[1] |
邹长东,麻晗,周青峰,等.低碳含硼钢盘条表面缺陷产生原因的分析[J].连铸,2018,43(6):55.
|
[2] |
王小燕,肖丽俊,仇圣桃,等.硼微合金化对CSP生产低碳铝镇静钢带性能的影响[J].中国冶金,2006,16(7):27.
|
[3] |
李昆昆. 钢坯表面裂纹在轧制过程中的演变和遗传性研究[D].唐山:华北理工大学,2018.
|
[4] |
Suzuki H G, Nishimura S, Imamura J, et al. Embrittlement of steels occurring in the temperature range from 1 000 to 600 ℃[J]. Transactions of the Iron and Steel Institute of Japan, 1984, 24(3):169.
|
[5] |
王新华,朱国森,于会香,等.高碳钢连铸板坯高温力学性能[J].北京科技大学学报,2005,27(5):545.
|
[6] |
朱国森,朱志远,王彦锋,等.含铌钢板坯角横裂纹的控制[J].钢铁,2006,41(12):30.
|
[7] |
Meahara Y.Constitution and properties of steels[J].Materials Science and Technology,1990,10(6):93.
|
[8] |
Mintz B.The influence of composition on the hot ductility of steel and to the problem of transverse cracking[J].International Materials Reviews,1991,36(9):18.
|
[9] |
赵建平,王帅,冯帅,等.低碳低硅铝镇静钢铸坯表面凹陷的成因及控制[J].连铸,2020,45(2):31.
|
[10] |
朱立光,张利民,肖鹏程,等.低碳钢板坯夹渣缺陷分析及控制[J].连铸,2020,45(2):36.
|
[11] |
艾克南,张盼盼,赵梦豪,等.1215易切削钢拉拔表面裂纹形成机制分析[J].钢铁,2020,55(2):88.
|
[12] |
刘辉,温维新.厚板连铸坯角部横裂纹缺陷的成因分析及控制[J].连铸,2014,39(2):34.
|
[13] |
屈天鹏,韩志伟,冯科.连铸板坯角部横裂纹产生机理与预防[J].连铸,2011,36(增刊1):385.
|
[14] |
苏笃星,周青峰,邹长东.BN析出行为对低碳含硼钢高温塑性的影响[J].钢铁研究学报,2018,30(6):476.
|
[1] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[2] |
WANG Xu-feng, WANG Qiang-qiang, ZHANG Xu-bin, WANG Qian, HE Sheng-ping. Effect of AlN on properties of CaO-SiO2 based mold fluxes for high-Al steel[J]. Iron and Steel, 2022, 57(5): 64-71. |
[3] |
YAN Xiao-peng, LIU Lei, HAN Xiu-li, WANG Yin-hui, ZHANG Di. Effect of boron on microstructure of fluorine-free mold fluxes[J]. Iron and Steel, 2022, 57(5): 72-80. |
[4] |
LIU Chang-wei, ZOU Zhuo-ming. Application of robot automatic mould fluxes adding technology in Ningbo Iron and Steel Works[J]. CONTINUOUS CASTING, 2022, 41(3): 71-75. |
[5] |
PIAO Zhan-long, WANG Xing-juan, ZHANG Cai-jun, ZHU Li-guang, LI Shao-ying, WANG Bo. Steel-slag interface reaction behavior in continuous casting mold of high titanium steel[J]. Iron and Steel, 2022, 57(3): 61-70. |
[6] |
PAN Wei-jie, LI Min, ZHU Li-long, HE Sheng-ping. Effect of Na2O on properties of ultra-high basicity continuous casting mold fluxes[J]. Iron and Steel, 2022, 57(1): 93-101. |
|
|
|
|