Causes and control of surface crack on continuous casting billets of wide and thick plates |
SUN Li-gang, JIA Sheng, LI Xin |
CSP Plant, Baotou Iron and Steel Group Co., Ltd., Baotou 014010, Nei Mongol, China |
|
|
Abstract In view of the surface cracks in batch in the thin slab continuous casting and rolling mill of CSP Plant of Baotou Steel. main causes of surface cracks on the slab were analyzed by investigating the types of surface defects, crack morphologies and characteristics, combined with the continuous casting process conditions, molten steel quality and equipment conditions.The measures of optimizing the vibration parameters, controlling the nitrogen content of molten steel, improving the vibration accuracy, adjusting the performance of protective slag and improving the quality of secondary cooling water were put forward to improve the surface defects of the casting billet, and the obvious results were obtained, and the surface cracks of the casting billet were effectively controlled.
|
Received: 07 April 2020
|
|
|
|
[1] |
何建中.采用微合金化技术实现产品结构升级[J].包钢科技,2005(6):1.
|
[2] |
李强,张凯,沈长华.辊式电磁搅拌器在包钢电工钢上的应用[J].连铸,2020,45(2):68.
|
[3] |
勤牧,杨雄,杨维宇.包钢含稀土Q690CF高强钢的研制[J].包钢科技,2020,46(2):52.
|
[4] |
王智峰,任慧平,方琪.GCR15轴承钢工艺改进及性能研究[J].包钢科技,2018,44(3):50.
|
[5] |
董丽丽,卢晓禹,杨源远,等.短流程CSP和2250 MM轧制生产50W600无取向硅钢组织及性能对比[J].金属热处理,2020,45(3):119.
|
[6] |
卢晓禹,董丽丽,王少炳,等.稀土CE对取向硅钢铸坯及热轧态组织的影响[J].包钢科技,2020,46(1):39.
|
[7] |
李殿明,邵明天,杨宪礼,等.连铸结晶器保护渣应用技术[M].北京:冶金工业出版社,2008.
|
[8] |
刘军.微合金钢铸坯角部横裂纹控制技术的应用[J].连铸,2019,44(3):34.
|
[9] |
张锦文,王文先,李建军,等.S355NL连铸圆坯表面横裂纹形成原因分析及改进[J].连铸,2016,41(6):63.
|
[10] |
蔡开科.连续铸钢原理与工艺[M].北京:冶金工业出版社,1994.
|
[11] |
赵晶,甄新刚,朱志远,等.倒角连铸坯角部纵向裂纹形成机制及控制[J].钢铁,2015,50(7):43.
|
[1] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[2] |
WANG Xu-feng, WANG Qiang-qiang, ZHANG Xu-bin, WANG Qian, HE Sheng-ping. Effect of AlN on properties of CaO-SiO2 based mold fluxes for high-Al steel[J]. Iron and Steel, 2022, 57(5): 64-71. |
[3] |
YAN Xiao-peng, LIU Lei, HAN Xiu-li, WANG Yin-hui, ZHANG Di. Effect of boron on microstructure of fluorine-free mold fluxes[J]. Iron and Steel, 2022, 57(5): 72-80. |
[4] |
LIU Chang-wei, ZOU Zhuo-ming. Application of robot automatic mould fluxes adding technology in Ningbo Iron and Steel Works[J]. CONTINUOUS CASTING, 2022, 41(3): 71-75. |
[5] |
PIAO Zhan-long, WANG Xing-juan, ZHANG Cai-jun, ZHU Li-guang, LI Shao-ying, WANG Bo. Steel-slag interface reaction behavior in continuous casting mold of high titanium steel[J]. Iron and Steel, 2022, 57(3): 61-70. |
[6] |
PAN Wei-jie, LI Min, ZHU Li-long, HE Sheng-ping. Effect of Na2O on properties of ultra-high basicity continuous casting mold fluxes[J]. Iron and Steel, 2022, 57(1): 93-101. |
|
|
|
|