Research on secondary cooling spray structure of billet continuous casting machine based on uniform cooling |
LIU Tao, CHEN Yong-feng, JIAO Kui-ming, ZHANG Hong-biao, ZUO Xiao-tan, ZHAO Li |
Iron and Steel Research Institute, Wuhu Xinxing Ductile Iron Pipes Co., Ltd., Wuhu 241002,Anhui,China |
|
|
Abstract The billet produced by the 180 mm billet continuous caster in a certain factory has serious corner subcutaneous cracks. Through modeling and numerical simulation of the casting machine, the surface center and corner temperature of the casting slab solidification process are obtained. Based on the principle of uniform cooling of the secondary cooling, the simulation evaluation and optimization of the secondary cooling spray structure of the cast slab, including the cooling uniformity analysis of the cast slab in the longitudinal and circumferential directions. According to the optimized structure plan, the 10th stream and second cold spray structure of the casting machine was actually modified and the production test was carried out. Comparing the low-magnification morphology of cast slabs produced without modification (other streams) and after modification (10 streams), it is found that the subcutaneous cracks at the corners of the slab produced by 10 streams have been significantly improved.
|
Received: 20 August 2021
|
|
|
|
[1] |
靳星,陈登福,龙木军. 连铸二冷区喷嘴布置方式优化方法[J]. 重庆大学学报,2011,34(1):53.
|
[2] |
朱苗勇. 高拉速连铸过程传输行为特征及关键技术探析[J]. 钢铁,2021,56(7): 1.
|
[3] |
康吉柏,王卫领,罗腾飞,等. 20CrMnTi钢160 mm×160 mm方坯内部质量控制[J]. 钢铁,2021,56(2): 82.
|
[4] |
左帅,张学慧,石晓钘.Q345R钢板探伤不合的原因分析与改进[J].河北冶金,2021(9):62.
|
[5] |
Petrus B,Kai Z,Zhou X. Model-based spray-cooling control system for steel continuous casting[J]. Metallurgical and Materials Transactions B,2011,42(1):87.
|
[6] |
刘青,王良周,曹立国,等. 连铸二次冷却研究的进展[J]. 钢铁研究学报,2005(6):6.
|
[7] |
朱苗勇. 新一代高效连铸技术发展思考[J]. 钢铁,2019,54(8):21.
|
[8] |
朱国森,季晨曦,刘洋,等. 首钢板坯连铸技术进步[J]. 中国冶金,2019,29(8):1.
|
[9] |
陈登福,徐佩,龙木军,等. 钢液连铸二次冷却先进工艺模型的发展与研究[J]. 钢铁,2020,55(3):40.
|
[10] |
何文杰. 180 mm方坯连铸二次冷却工艺模型研究[D]. 重庆:重庆大学,2019.
|
[11] |
陈登福,冯科,廖建云,等. 方坯高效连铸凝固冷却的研究[J]. 炼钢,2001 (4):49.
|
[12] |
史进强,丁剑,颜慧成,等.200 mm×200 mm方坯连铸机二冷区喷嘴冷态特性研究[J].河北冶金,2019(11):36.
|
[13] |
潘文峰,蔡兆镇,王少波,等. 连铸板坯二冷高温区传热均匀性研究与优化[J]. 中国冶金,2021,31(8): 23.
|
[14] |
朱立光,郭志红.高速连铸技术研究[J].河北冶金,2021(6):1.
|
[15] |
刘增勋,张朝阳,肖鹏程,等. 冷却工艺对高速连铸结晶器传热的影响[J]. 钢铁,2021,56(5): 41.
|
[16] |
Tsubakihara O,Kameyama K,Takahama H,et al. Method for cooling continuous casting:US,US4424855A[P].1984-10-01.
|
[17] |
陈亮,宋波,陈天明,等. 45钢连铸大方坯中心疏松与缩孔控制[J]. 钢铁,2018,53(8):49.
|
[18] |
刘亮. 奥钢联板坯铸机驱动力报警问题的分析及改进[J]. 中国冶金,2019,29(1):52.
|
[19] |
王璐,孙彦辉,焦帅,等. 轴承钢大方坯二次枝晶臂间距数值模拟[J]. 钢铁,2018,53(7):56.
|
[20] |
郭剑波,梁爱生,荣亮,等. 带液芯控制的板坯连铸二冷区动态控制模型[J]. 钢铁,1997(6):29.
|
[21] |
Inazaki K,Takahashi M,Chi Da Y,et al. Computer control system for CC-DR process[J]. ISIJ International,2006,24(1):75.
|
[22] |
KONG Y,CHEN D,QIANG L,et al. Research on the on-line simulation of a three-dimensional temperature field model of slab continuous casting[J]. Steel Research International,2018,89(8):1800091.
|
[1] |
BAI Xiao-lu, ZHANG Xiao-wei, LI Meng-fei, ZHANG Li-qiang. Corner crack controlling of niobium microalloyed steel billet for construction[J]. CONTINUOUS CASTING, 2022, 41(2): 61-65. |
[2] |
LI Wei, TAN Zheng-jun, CHENG Jin-jun, LIN Qian, ZHANG Li-qiang. Quality improvement and practice of high speed continuous casting of billet based on secondary cooling optimization[J]. CONTINUOUS CASTING, 2022, 41(2): 95-99. |
[3] |
CHEN Changhua,CHEN Xinhua,ZHANG Wencheng,ZHOU Yue,WU Lian,LI Zhumao. Numerical simulation and ultrasonic testing analysis of solidification field of 42CrMo ingot[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(2): 8-12. |
[4] |
MA Fei-yue. Development and prosperity of macrostructure etching process of continuous casting billet[J]. CONTINUOUS CASTING, 2022, 41(1): 9-13. |
[5] |
DENG Yong, YANG Li-bin, WANG Cheng-yi. Application of high-speed continuous casting technology for low carbon steel slab in Masteel[J]. CONTINUOUS CASTING, 2022, 41(1): 72-77. |
[6] |
XIE Zhengjun,FAN Tian,XIE Jianbo. Numerical analysis on thermal compression of #br#
sample used in a thermal simulation testing machine[J]. PHYSICS EXAMINATION AND TESTING, 2021, 39(5): 9-. |
|
|
|
|