连铸坯低倍检验工艺发展现状及展望

doi:10.13228/j.boyuan.issn1005-4006.20210099

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (698 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract Macrostructure etching of continuous casting billet is one of the important parts of quality control in steel companies. For a long time, compared with the rapid development of automatic metallurgical analysis and products testing process, the value of automatic macrostructure etching process has been underestimated. With acid etching as the testing method, by comparing the different processing of sample preparation, acid etching and imaging, the development of the macrostructure etching process of continuous casting billet in domestic steel companies is reviewed and the future of automatic macrostructure etching process is discussed.

Key words： macrostructure etching continuous casting billet sample preparation hot-acid etching electrolytic etching automation

Received: 19 August 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	MA Fei-yue

Cite this article:

MA Fei-yue. Development and prosperity of macrostructure etching process of continuous casting billet[J]. CONTINUOUS CASTING, 2022, 41(1): 9-13.

URL:

http://www.chinamet.cn/Jweb_lz/EN/10.13228/j.boyuan.issn1005-4006.20210099 OR http://www.chinamet.cn/Jweb_lz/EN/Y2022/V41/I1/9

[1]	师昌绪,李恒德,周廉. 材料科学与工程手册 [M]. 北京:化学工业出版社,2004.
[2]	杨恩蛟,姜敏,侯泽旺,等. 连铸板坯凝固末端大压下改善铸坯内部质量[J].中国冶金,2020, 30(5):23.
[3]	毛敬华,帅勇,谢贵强,等. 连铸特厚板坯内部质量控制的关键技术[J].钢铁,2019,54(8):64.
[4]	郑伟栋,唐志军,郝强,等. 铸坯酸蚀检验法在板坯生产中的应用[J].连铸,2011 (2):44.
[5]	周滨新,张康晖,马建超,等. 70钢小方坯芯部质量优化[J].中国冶金,2021,31(1):42.
[6]	陈亮,宋波,陈天明,等. 45钢连铸大方坯中心疏松与缩孔控制[J].钢铁,2018,53(8):49.
[7]	董大西,王谦,李国栋,等. 含硫易切削钢连铸坯低倍裂纹的成因及控制[J].中国冶金,2013, 23(6):30.
[8]	Da S G, Ghosh S, Chowdhury S G, et al. Investigation of sub-surface cracks in continuous cast billets[J].Engineering Failure Analysis, 2003, 10(3):363.
[9]	Eskin D G, Zuidema J, Savran V I, et al. Structure formation and macrosegregation under different process conditions during DC casting[J].Materials Science and Engineering A, 2004, 384(1/2):232.
[10]	程海芬. 低倍检验在铸坯质量控制中的应用[J].天津冶金,2006(5):44.
[11]	杨劲松,陶金明. 低倍检验在铸坯质量控制中的应用[C]//第八届全国连铸学术会议论文集. 海口:中国金属学会连铸分会,2007.
[12]	张永藏. 低倍检验在铸坯质量控制中的应用[J].河北冶金,2006 (5):49.
[13]	贾建平. 降低连铸坯内部缺陷技术的研究与应用[J].冶金设备,2015(4):69.
[14]	巴虹,万书伟. 连铸坯低倍酸蚀方法及分析[J].物理测试,2010,28(1):59.
[15]	许庆太,张楠,傅强. 连铸坯凝固组织和缺陷的冷酸蚀法宏观检验[J].炼钢,2003,19(5):26.
[16]	李靖,喻承欢,李凤喜,等. 冷蚀检验在连铸坯质量控制中的应用实践[J].炼钢,2003,19(2):13.
[17]	佚名. 大截面钢的低倍电解腐蚀法[J].机械工程师,1974,52(2):21.
[18]	何志明,范立强,彭勃,等. 连铸板坯低倍组织检验的三种方法对比试验[J].世界钢铁,2014 (6):15.
[19]	许庆太,王文仲. 连铸坯低倍检验和缺陷图谱[M].北京:中国标准出版社,2009.
[20]	许庆太,李吉东,孙中强. 枝晶腐蚀低倍检验在连铸生产中的应用[J].物理测试,2011,29(6):22.
[21]	何志明,张斌. 枝晶腐蚀低倍检验技术在连铸生产质量控制中的应用[J].宝钢技术,2014(6):25.
[22]	杨撷光,许庆太,马宁. 枝晶腐蚀低倍检验技术在连铸生产中的应用[J].连铸,2020 (3):22.
[23]	傅文耀,李作鑫,刘广. 钢坯低倍检测试样加工专用设备龙门铣磨床的研制[J].物理测试,2002,20(3):37.
[24]	周立富. 试样加工技术的创新与发展[J].物理测试,2011, 29(增刊1):109.
[25]	魏振广,王万征. 圆盘锯床高效率高精度锯切的新技术[J].制造技术与机床,2008(8):145.
[26]	王克杰,王洪亮,黄港明,等. 洁净钢检测新技术—钢坯镜面加工及全端面检测[J].理化检验(物理分册),2015,51(12):839.
[27]	郭长升,周立民,刘国栋,等. 大型钢坯低倍试样加工与缺陷检测的新装备、新技术[J].连铸,2016 (2):43.
[28]	彭勃,李春阳. 全自动电解腐蚀技术在连铸坯低倍检验中的应用[J].理化检验(物理分册),2015,51(12):858.
[29]	周志超,崔全法,徐鑫. 迁钢全自动低倍检测评定系统的开发与应用[C]//2014年全国压力加工设备节能降耗及技术创新研讨会论文集. 北京:中国金属学会,2014.
[30]	周志超. 扫描技术在连铸坯低倍检验中的应用[J].现代测量与实验室管理,2016(5):8.
[31]	贾永坡. 基于深度学习的板坯低倍质量评级系统[C]//第十一届中国钢铁年会议论文集. 北京:中国金属学会,2017.
[32]	苏群. 低倍酸洗自动化系统的应用[J].甘肃冶金,2019,41(2):107.