10B21微合金钢生产工艺全流程洁净度分析

doi:10.13228/j.boyuan.issn1005-4006.20210150

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (3461 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to explore the factors affecting the production stability of 10B21 steel, improve the quality of steel and meet the needs of customers, the inclusions of clean steel in the whole process were sampled and analyzed. The results show that there are mainly seven types of inclusions in each station of the whole process, namely CaO-Al₂O₃-MgO-CaS-TiN, CaO-Al₂O₃-MgO-CaS, Al₂O₃, MnS, MnS-Al₂O₃, Al₂O₃-TiN and MnS-TiN. Except that the type of sample inclusions in converter station is relatively complex, the inclusions in other stations are mainly CaS-Al₂O₃-MgO-CaO-TiN. The oxygen and nitrogen content fluctuates greatly in different furnace times, especially the control of the oxygen content at the end of the converter is unstable, the inclusions change greatly in the LF refining process, and the size generated after soft blowing operation is 80-100 μm, the main component of which is CaO-Al₂O₃-MgO-CaS-TiN. That is, with calcium oxide and alumina as the nucleation center, magnesium oxide is accompanied outside and wrapped by calcium sulfide and titanium nitride. The inclusions of this component begin to form after LF refining calcium feeding line. Due to the low fluidity of refining slag, poor coverage effect on liquid steel, secondary oxidation is easy to occur, resulting in the obvious aggregation and growth of inclusions in the soft blowing stage.

Key words： 10B21 steel whole process inclusion clean steel quality of steel

Received: 22 December 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	JIAO Kui-ming
	ZHANG Ya-bing
	ZHAO Li
	ZUO Xiao-tan
	WANG Dong-xing
	CHEN Yong-feng

Cite this article:

JIAO Kui-ming,ZHANG Ya-bing,ZHAO Li等. Cleanliness analysis of the whole process of 10B21 microalloyed steel production process[J]. CONTINUOUS CASTING, 2022, 41(5): 69-75.

URL:

http://www.chinamet.cn/Jweb_lz/EN/10.13228/j.boyuan.issn1005-4006.20210150 OR http://www.chinamet.cn/Jweb_lz/EN/Y2022/V41/I5/69

[1]	张立峰. 钢中非金属夹杂物几个需要深入研究的课题[J].炼钢,2016,32(4): 1.
[2]	许国方,张雪良,杨树峰,等.20CrMnTi齿轮钢冶炼全流程的夹杂物分析[J].中国冶金,2020,30(11):23.
[3]	张立峰,李燕龙,任英.钢中非金属夹杂物的相关基础研究(Ⅱ)——夹杂物检测方法及脱氧热力学基础[J].钢铁,2013,48(12):1.
[4]	李成斌,刘君,蒋鹏. 车轴钢EA1N全流程夹杂物演变分析及工艺优化[J]. 炼钢,2021,37(1): 73.
[5]	孙江波,刘旋,翟晓毅,等. 10B21冷镦钢线材表面翘皮缺陷成因分析[J]. 连铸,2018 (5): 39.
[6]	帅习元,桂美文,郑云锋,等. 含硼冷镦钢硼的行为研究[J]. 中国冶金,2011,21(2): 24.
[7]	刘伟建.硼的固溶和析出行为对低碳钢性能影响的研究[D]. 北京:北京科技大学,2015.
[8]	马煜林.超超临界发电用CB2钢的微观组织调控及其力学性能研究[D]. 沈阳:东北大学,2018.
[9]	阮士朋.高品质含硼冷镦钢的组织和性能调控[D]. 北京:北京科技大学,2020.
[10]	刘珍童,杨文,任英,等. 铝脱氧钢钙处理效果影响因素分析[J]. 钢铁,2020,55(3):29.
[11]	贾毅, 刘春阳,韩少伟,等. 铝镇静钢氮含量控制分析[J]. 中国冶金,2021,31(3): 116.
[12]	赵家七,蔡小锋,马建超,等. 铝镇静冷镦钢CaS结瘤机理及改进[J]. 钢铁,2021,56(9): 80.
[13]	刘军,宋朝琦,刘杰,等. H08A焊丝钢夹杂物演变规律分析[J]. 中国冶金,2021,31(3): 44.
[14]	李明,王新成,段加恒,等. 轴承钢中D类夹杂物的形成与控制[J]. 工程科学学报,2018,40(增刊1): 31.
[15]	谌智勇,王文义,储焰平,等. 包钢U75V重轨钢夹杂物演变规律分析[J]. 连铸,2020(5): 57.
[16]	王康,刘剑辉,杨树峰,等. GCr15轴承钢EAF-LF-VD-CC流程非金属夹杂物的演变[J]. 钢铁,2020,55(2): 48.
[17]	赵东伟,包燕平,王敏,等. GCr15轴承钢中TiN(C)析出行为热力学分析和研究[J]. 特殊钢,2012,33(5):7.
[18]	左小坦,陈永峰,陶群南,等.高合金钢中氮含量控制分析[J].工业加热,2019,48(4):13.
[19]	吕迺冰,高航,刘珂,等. 冷却强度对超高硫中碳钢方坯凝固过程MnS生长的影响[J]. 钢铁,2022,57(6): 50.
[20]	王昆鹏,王郢,徐建飞,等. 轴承钢二次精炼过程夹杂物演变规律[J]. 钢铁,2022,57(6): 42.
[21]	温瀚,周海忱,罗衍昭,等. RH加钛时机和纯循环时间对IF钢洁净度影响[J]. 中国冶金,2022,32(9): 45.
[22]	祝航航,王敏,姚骋,等. 六流T型中间包夹杂物去除行为的数值模拟[J]. 中国冶金,2022,32(8): 89.