Practice and process research of Q235B on beam blank caster |
NING Ying-yi |
Fujian Luoyuan Minguang Iron and Steel Co., Ltd., Fuzhou 350000,Fujian,China |
|
|
Abstract In order to provide high quality casting billet for section steel and reduce the occurrence of quality defects such as web crack and center loose, the technological conditions in the production process of Q235B were studied, and the mechanism of web crack and center loose of casting billet was mastered. By controlling the composition and purity of molten steel, optimizing the mold cooling and secondary cooling process, optimizing the slag protection process and the water outlet insertion depth, the casting billet can achieve uniform cooling during the solidification process, reduce the surface temperature drop of the casting billet, effectively eliminate the web cracks on the surface of the casting billet, and control the center porosity level of the casting billet below 1.0.
|
Received: 07 November 2022
|
|
|
|
[1] |
龚殿尧, 高志宇, 徐建忠, 等. 小型H型钢超快冷“内并外扩”的有限元模拟[J]. 钢铁, 2022, 57(1): 102.
|
[2] |
郭年琴, 郭晟, 文铁琦. H型钢万能轧机轧辊调整装置运动学动力学分析[J]. 钢铁, 2015, 50(3): 91.
|
[3] |
王克锋,宋介中,李明贤,等. SS400热轧H型钢翼缘开裂成因及控制措施[J]. 钢铁, 2011, 46(9): 96.
|
[4] |
石雷, 张丽娜, 肖克勇, 等. 热轧H型钢翼缘斜度控制方法及措施[J]. 中国冶金, 2021, 31(4): 74.
|
[5] |
赵培林, 韩文习, 杨志杰, 等. 夹杂物对海工用H型钢冲击韧性影响及分析[J]. 中国冶金, 2020, 30(2): 74.
|
[6] |
汪杰, 吴保桥, 张建, 等. Nb-V、Nb-Ti对重型热轧H型钢强韧性的影响[J]. 中国冶金, 2020, 30(11): 47.
|
[7] |
刘崇,胡春林,吴坚,等.铌微合金化异型坯高温热塑性的研究[J].河北冶金,2021(7):26.
|
[8] |
陈伟,于兴旺,王嘉琦,等. 异型连铸坯结晶器内表面纵裂萌生区域[J]. 钢铁, 2017, 52(3): 36.
|
[9] |
徐宇, 张峻纲, 林小祥, 等. 单点非平衡异型坯连铸配水优化的数值模拟[J]. 中国冶金, 2022, 32(4): 77.
|
[10] |
邓爱军,蒲雪峰,左小坦,等.H型钢V形开裂的缺陷研究与优化[J].钢铁,2019,54(8): 161.
|
[11] |
董鹏莉,尚海霞,王华.铸坯及板卷典型质量缺陷成因与控制技术[J]. 中国冶金,2017,27(6):7.
|
[12] |
蔡开科. 连铸坯质量控制[M]. 北京:冶金工业出版社,2010.
|
[13] |
杨春政. 高效低成本洁净钢生产实践探索[J].钢铁,2021,56(8):20.
|
[14] |
杨丽,柴锋,罗小兵,等.连铸结晶器内板坯传热凝固行为建模和模拟[J].连铸,2019(4):68.
|
[15] |
陈伟,和保民,郭高翔,等.Q235B连铸二冷配水分析[J].铸造技术,2019,40(2):213.
|
[16] |
李殿明, 邵明天, 杨宪礼, 等. 连铸结晶器保护渣应用技术[M]. 北京:冶金工业出版社, 2008.
|
[17] |
翟俊, 李欢, 陈法涛, 等. 保护渣对430不锈钢铸坯边部凹陷缺陷的影响[J]. 中国冶金, 2022, 32(5): 102.
|
[18] |
赵烁, 李祖树, 朱雨逸, 等. 低碳热轧板卷的表面黑线和翘皮缺陷形成机制[J]. 中国冶金, 2021, 31(4): 37.
|
[19] |
毛文文, 路博勋, 郭银涛, 等. 中碳高铝钢表面缺陷研究及控制[J]. 中国冶金, 2021, 31(3): 111.
|
[20] |
李四军, 彭永香, 李萍, 等. 超薄大断面异型坯结晶器非对称流场和温度场的优化[J]. 连铸, 2021(6): 9.
|
[21] |
王晓晨,孙齐松,邸全康,等.薄腹板近终形异形坯连铸温度场数值模拟[J].钢铁,2013,48(12):36.
|
[22] |
张建伟,苏旺,崔衡,等. PIV测速技术分析异形坯连铸结晶器流场[J].连铸,2019(1):54.
|
[23] |
刘颜彬, 唐海燕, 王凯民,等. 水口结构对板坯结晶器液面流动行为的影响[J]. 连铸, 2022(3): 1.
|
[24] |
武鸿杰, 徐宇, 储成阳, 等. 吹气情况下异型坯结晶器水口结构的物理模拟[J]. 连铸, 2021(3): 45.
|
[25] |
陈正阳, 杨树峰, 谢锦丽, 等. 钛合金异形薄壁壳体铸造工艺数值模拟及优化[J]. 中国冶金, 2022, 32(10): 105.
|
[26] |
常朋飞,俞学成,孙亮,等.板坯连铸机全保护浇注工艺优化[J].河北冶金,2021(12):51.
|
[27] |
石树东,胡显堂,张虎成,等.薄板坯连铸保护浇注工艺研究[J].河北冶金,2021(09):39.
|
[28] |
章印, 姜敏, 王新华. Q345D钢精炼过程夹杂物生成及演变行为[J]. 钢铁, 2022, 57(2): 63.
|
[29] |
赵紫玉. 连铸工艺参数调整对连铸坯中心偏析的影响[J]. 中国金属通报,2020(2):27.
|
[30] |
梁军,孙彪. 异形坯表面纵裂纹产生原因及控制措施[J].安徽冶金科技职业学院学报,2021,31(3):47.
|
[31] |
韩延申, 张江山, 邹雷雷, 等. 喷嘴喷淋距离对连铸小方坯二冷均匀性的影响[J]. 工程科学学报, 2020, 42(6): 739.
|
[32] |
钱志友, 汪德富, 邓俊棕,等. 厚板坯角部凹陷裂纹的控制措施[J]. 连铸, 2022(5): 76.
|
[33] |
刘涛, 陈永峰, 王东兴, 等. 含硼钢铸坯表面裂纹缺陷控制[J]. 连铸, 2022(5): 62.
|
[34] |
赵阳.提高铸坯表面温度的节能工艺技术[J].河北冶金,2020(12):54.
|
[35] |
王勇, 杨树峰, 李京社, 等. 精冲钢连铸坯角部横裂纹产生原因及控制措施[J]. 连铸, 2022(1): 49.
|
[36] |
公斌. 微合金化近终型异形坯R角纵裂纹控制与应用[J]. 连铸, 2022(1): 62.
|
[37] |
李超,任素波,胡正才,等.连铸结晶器内坯壳安全凝固的研究[J].重型机械,2020(1):33.
|
[38] |
李伟, 谈正军, 程锦君, 等. 基于二冷优化的高拉速方坯质量改善及实践[J]. 连铸, 2022(2): 95.
|
[39] |
杨鑫,张媛媛,何志军,等.基于电脉冲技术抑制连铸水口结瘤堵塞的研究[J].钢铁,2021,56(4):52.
|
[40] |
牛亮,赵俊学,仇圣桃,等.偏心M-EMS作用下连铸圆坯流动-传热模拟[J].钢铁,2020,55(9):49.
|
[41] |
马樊,刘青,张江山,等.喷嘴射流特征对连铸二冷区蒸汽膜穿透行为的影响[J].钢铁,2022,57(10):101.
|
[42] |
刘喜锚,史伟宁.连铸二冷系统喷嘴堵塞物来源分析和控制措施[J].中国冶金,2022,32(9):73.
|
[43] |
王亚涛,朱小勇,阎建武.板坯连铸机二次冷却水分配策略分析[J].连铸,2022(1):67.
|
[44] |
吴晨辉,李阳,谢鑫,等.板坯连铸过程凝固传热数值计算与工艺优化[J].中国冶金,2022,32(3):92.
|
[45] |
潘文峰,蔡兆镇,王少波,等.连铸板坯二冷高温区传热均匀性研究与优化[J].中国冶金,2021,31(8):23.
|
[46] |
何宇明.连铸结晶器保护渣功能发挥和稳定质量的系统思维[J].连铸,2019(2):14.
|
[47] |
钱志友,汪德富,邓俊棕,等.厚板坯角部凹陷裂纹的控制措施[J].连铸,2022(5):76.
|
[48] |
袁志鹏,朱立光,王杏娟,等.高拉速薄板坯连铸保护渣剪切变稀性质[J].钢铁,2022,57(12):97.
|
[49] |
韩秀丽,刘盈盈,刘磊,等.含钛型连铸保护渣性能及应用研究进展[J].钢铁,2022,57(10):10.
|
[50] |
刘长伟,邹卓明.机器人自动加保护渣技术在宁波钢铁的应用[J].连铸,2022(3):71.
|
[51] |
周秋月, 朱坦华, 张立峰, 等. 非稳态浇铸对结晶器卷渣定量影响的大涡模拟[J]. 钢铁, 2022, 57(4): 68.
|
[52] |
东滨, 张立峰, 陈天明, 等. 连铸坯宏观与半宏观偏析行为表征[J]. 连铸, 2021(4): 31.
|
[1] |
SONG Hong-wei, WANG Dong-xing, REN Yi, WANG Wu-lei, YANG Wei-yong, WANG Chun-mei. Analysis and improvement of prestressed high-strength steel PSB930[J]. CONTINUOUS CASTING, 2023, 42(2): 63-69. |
[2] |
LIN Peng, ZHANG Hong-cai, ZUO Hui, XU Zheng-zhou, ZHAI Wan-li. Analysis and improvement of surface defects of peritectic steel 15CrMoG billet[J]. CONTINUOUS CASTING, 2023, 42(1): 61-65. |
[3] |
YE Dexin, HE Jiannan, ZENG Lingyu. Analysis and improvement of inner wall defects of 35 steel parts[J]. PHYSICS EXAMINATION AND TESTING, 2023, 41(1): 31-34. |
[4] |
ZHAO Xianjiu1,2,ZHANG Jieyu2,3,LI Chuanjun2,3. Analysis of formation mechanism about Ca-Mg-Al spineltype inclusions in cold thin rolling sheet[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 664-671. |
[5] |
KANG Yong-lin, ZHU Guo-ming, JIANG Min, WANG Guo-lian, LIU Peng-tao, XU Hai-wei, XIE Cui-hong, WEI Yun-fei, SHEN Kai-zhao, LIU Yang. Slab continuous casting by big roll heavy reduction and extra thick plate rolled by low compression ratio[J]. Iron and Steel, 2022, 57(7): 95-105. |
[6] |
ZHANG Xueling,LI Maolin. nalysis of unqualified causes of generator yoke Q345C heavy and wide plate[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(6): 41-. |
|
|
|
|