Analysis of causes for deformation of copper tubein rectangular mold |
HAN Lun-jie1, CAO Xue-qian3, XIE Yi-kui2,4, WANG Qian1 |
1. Technology Center, Heilongjiang Jianlong Iron and Steel Co.,Ltd., Shuangyashan 155126, Heilongjiang,China; 2. Technology Department, East China Branch of CISRI, Huaian 223007, Jiangsu,China; 3. Steelmaking Engineering Technology Institute, MCC Capital Engineering and Research Incorporation Limited, Beijing 100176,China; 4. Material Science and Engineering,Shanghai Univeristy School, Shanghai 200444,China |
|
|
Abstract To control the deformation of rectangular crystallizer copper tube cavity in the casting process, reference is provided for optimizing copper tube design.The maximum deflection of crystallizer copper tube was calculated by the uniform load formula of simply supported beam, the thermal deformation was calculated by combining temperature gradient and thermal expansion coefficient and the changes of inner wall size and taper of copper tube under different water pressures were analyzed. The temperature field and deformation distribution in the mold were simulated by MSC Software. The analysis results show that the cooling water pressure is the main cause of copper tube deformation, the largest deformation position is in the center of the copper tube cavity and maximum deformation value 1.76 mm. The taper of the copper tube of the crystallizer increases in the upper part and decreases in the lower part. The simulation results show that the plane area of the copper tube cavity is prone to thermal stress and deformation. The deformation in the middle area is larger, and the deformation in the quarter is 72% of that in the center. Cooling water pressure and deformation is proportional to the linear relationship, and under the same pressure conditions, the copper tube wall thickness decreased 4 mm, deformation increased by 35%.
|
Received: 06 September 2022
|
|
|
|
[1] |
周晨阳, 黄军, 张亚竹, 等. 大方坯连铸结晶器水口优化模拟探究[J]. 连铸, 2023(1): 97.
|
[2] |
GUPTA V K, JHA P K, JAIN P K. A novel approach to predict the inclusion removal in a billet caster mold with the use of electromagnetic stirrer[J]. Journal of Manufacturing Processes,2022,83:27.
|
[3] |
金友林,赵振南,张峻纲,等.圆坯连铸结晶器流场模拟研究[J].安徽工业大学学报(自然科学版),2022,39(3):250.
|
[4] |
刘淼, 刘中秋, 吴颖东,等. 吹氩连铸结晶器液面波动行为的时频分析[J]. 中国冶金, 2022, 32(7): 35.
|
[5] |
李丽,杜一哲,汪勤政,等.Q345钢连铸坯压缩状态下的高温力学性能[J].中国冶金,2021,31(4):32.
|
[6] |
韩毅华,刘少寒,朱立光.软接触电磁连铸结晶器保护渣冶金行为的研究进展[J].河北冶金,2021(5):1.
|
[7] |
王林杰,孔令种,冯亮花,等.高拉速方坯连铸结晶器钢渣界面行为特征[J].连铸,2021(4):11.
|
[8] |
谢长川,李富帅,钱亮,等.高拉速小方坯铸机关键技术的研发及应用[J].炼钢,2020,36(2):59.
|
[9] |
王泽鹏,肖鹏程,朱立光,等. 方坯连铸结晶器铜管温度场分析[J]. 钢铁, 2018, 53(3): 38.
|
[10] |
邵楠男, 邹富康, 仲红刚, 等. PMO和冷却速率对5CrNiMoV热作模具钢凝固组织的影响[J]. 中国冶金, 2021, 31(10): 23.
|
[11] |
王皓, 王国连, 马硕,等. MCCR产线低碳钢高拉速技术研究与应用[J]. 中国冶金, 2022, 32(12): 88.
|
[12] |
杨昌霖, 高琦, 姚成功, 等. 板坯连铸结晶器铜板水槽的优化设计[J]. 中国冶金, 2021, 31(3): 101.
|
[13] |
吴豪, 蔡兆镇, 牛振宇, 等. 薄板坯连铸结晶器铜板热/力行为[J]. 中国冶金, 2021, 31(12): 79.
|
[14] |
陶红标,吕晓军,席常锁,等.薄板坯连铸结晶器锥度设计技术研究及应用[J].钢铁,2012,47(1):28.
|
[15] |
陈阳,钟光,姚军,等. 双流板坯结晶器锥度动态保持技术的开发与应用[J]. 钢铁, 2014, 49(10): 34.
|
[16] |
赵晶,甄新刚,朱志远,等. 倒角连铸坯角部纵向裂纹形成机制及控制[J]. 钢铁, 2015, 50(7): 43.
|
[17] |
江中块,李俊杰,张森森,等.板坯连铸结晶器铜板冷却水槽结构优化[J].材料与冶金学报,2019,18(2):101.
|
[18] |
刘增勋,张朝阳,肖鹏程,等.冷却工艺对高速连铸结晶器传热的影响[J].钢铁,2021,56(5):41.
|
[19] |
林雪莉. 连铸机结晶器振动装置动态性能分析研究[D]. 赣州:江西理工大学,2010.
|
[20] |
郭士萌,王亚平,李占君,等.连铸结晶器铜管异常结垢原因及改进[J].河北冶金,2023(1):59.
|
[21] |
蔡开科. 连铸结晶器[M]. 北京:冶金工业出版社,2008.
|
[22] |
姚海明,杨杰,李梦英.薄板坯连铸结晶器铜板内腔形状研究[J].炼钢,2018,34(5):64.
|
[23] |
朱苗勇. 高拉速连铸过程传输行为特征及关键技术探析[J]. 钢铁, 2021, 56(7): 1.
|
[24] |
张慧,吴夜明,徐李军,等. 唐钢新型薄板坯连铸结晶器的设计和使用效果[J]. 钢铁, 2007, 42(5): 19.
|
[25] |
肖红,李爱武,欧阳红林,等.结晶器电磁搅拌器的内腔磁场和端部漏磁的数值模拟[J].中国冶金,2013,23(12):43.
|
[26] |
谢鑫,吴国荣,吴晨辉,等.连铸管式结晶器变形的数值仿真与优化[J].中国冶金,2022,32(1):77.
|
[27] |
ZENG J H,GAN M J,YAN X B,et al. Mathematical modeling of heat transfer and deformation of bloom tube mold in continuous casting process[J]. Metallurgical and Materials Transactions,2020,51(1):213.
|
[28] |
刘瑞堂,刘文博,刘锦云. 工程材料力学性能[M]. 哈尔滨:哈尔滨工业大学出版社,2001.
|
[29] |
成大先. 机械设计手册第五版[M]. 北京:机械工业出版社,2007.
|
[30] |
林鹏, 张洪才, 左辉, 等. 包晶钢15CrMoG方坯表面缺陷分析与改进[J]. 连铸, 2023(1): 61.
|
[31] |
眭志松, 康欣蕾, 韩德飞, 等. 220方低碳合金钢铸坯质量提升的实践[J]. 连铸, 2022(5): 108.
|
[32] |
董长征.CSP薄板坯连铸结晶器锥度优化与应用[J].炼钢,2013,29(6):15.
|
[33] |
PENG L, LIANG L,TIE Z P, et al. Combined study on mold taper and corner radius in bloom continuous casting by FEM simulation and trial experiment[J]. Metals and Materials International,2019,25(6):1603.
|
[34] |
方昆凡. 工程材料手册[M]. 北京:北京出版社,2000.
|
[1] |
QIAN Zhi-you, WANG De-fu, DENG Jun-zong, GUO Rui, ZHANG Xiao-di. Control measures for dented cracks at corners of thick slabs[J]. CONTINUOUS CASTING, 2022, 41(5): 76-81. |
[2] |
ZHOU Gan-shui, ZHANG Hai-yang, NING Shu-guang, SUN Jun, CHEN Yang, XIAO Hai-jian. Application of online hot width adjustment in four slab casters at FENGNAN[J]. CONTINUOUS CASTING, 2022, 41(3): 76-82. |
[3] |
WANG Dong-cheng, XU Yang-huan, YU Hua-xin, LIU Hong-min. Method of eliminating deflection interference signal of whole roll embedded flatness meter[J]. Iron and Steel, 2020, 55(10): 56-62. |
[4] |
ZHAO Jing,ZHEN Xin-gang,ZHU Zhi-yuan,WANG Yu-long,ZHANG Hu-cheng,ZHAO Xin-yu. Formation mechanism and control method of longitudinal corner crack on slab with chamfering mold[J]. Iron and Steel, 2015, 50(7): 43-47. |
[5] |
CHEN Yang,, ZHONG Guang, YAO Jun, NING Shu-guang, LI Zhen, XIE Chang-chuan. Development and Application of Two-Strand Slab Continuous Caster Mold Taper Dynamic Balance Technology[J]. Iron and Steel, 2014, 49(10): 34-39. |
[6] |
LI Rong-min,,YANG Li-po,YU Bing-qiang,LIU Hong-min,YU Hua-xin. Effect of Shape Detecting Roll Deflection on Original Waveform Signal of Cold Rolling Strip[J]. Iron and Steel, 2013, 48(5): 41-45. |
|
|
|
|