Cause analysis and preventive measures of steel leakage in slab continuous casting |
ZHAO Bingbing, YUAN Tianxiang, LIU Yanqiang, QIAO Huanshan |
Manufacture Division,Shougang Jingtang Iron and Steel Co., Ltd., Tangshan 063200, Hebei, China |
|
|
Abstract In order to study the causes and laws of breakout in slab continuous casting production, the breakout accidents in slab continuous casting production were statistically analyzed. The causes of breakout were analyzed by collecting the breakout slab morphology and production process parameters on site, and the breakout causes were classified and summarized based on the analysis of breakout accidents in recent five years. The results show that the main causes of breakout are poor performance of mold flux, large fluctuation of liquid level, insufficient functional accuracy of caster equipment and improper operation. In addition, molten steel composition, foreign matter involvement and sticking cold steel can also lead to breakout. The causes of breakout were classified and summarized, which provided theoretical guidance for the formulation of breakout prevention measures.
|
Received: 24 May 2023
|
|
|
|
[1] |
刘宇,徐志强,张冬冬,等.连铸漏钢空间-时序特征与演化规律[J].连铸,2021(4):7.
|
[2] |
高宇,张燕平,张士慧,等.结晶器漏钢预报专家系统的开发与应用[J].河北冶金,2020(1):20.
|
[3] |
段海洋,王旭东,姚曼.基于密度聚类和动态时间弯曲的结晶器黏结漏钢预报方法的开发[J].工程科学学报,2020,42(3):348.
|
[4] |
安守勇,王鹏飞.VUHZ检测控制系统在ESP产线的应用[J].连铸,2022(5):125.
|
[5] |
王万林,颜雄,周乐君,等.高碳钢连铸保护渣的性能[J].连铸,2021(6):48.
|
[6] |
陈寿红,刘林刚,姜东滨,等.大方坯连铸漏钢原因分析及控制研究[J].炼钢,2020,36(5):52.
|
[7] |
林鹏,张洪才,左辉,等.包晶钢15CrMoG方坯表面缺陷分析与改进[J].连铸,2023(1):61.
|
[8] |
陈荣凯,刘坤.马标C12D钢方坯角裂漏钢控制实践研究[J].连铸,2018(6):74.
|
[9] |
蒋文波,文光华,江婧,等.保护渣渣圈形成长大机理及影响因素研究现状[J].连铸,2021(2):7.
|
[10] |
李继,陈守杰,王勇源,等.小板坯粘结漏钢原因分析及控制措施[J].河北冶金,2022,316(4):51.
|
[11] |
杨学雨,郑立允.薄板坯连铸结晶器捞渣操作对漏钢的有效控制[J].连铸,2021(1):70.
|
[12] |
梅宁,王宝动,刘延强,等.包晶钢中间包快换板坯接痕漏钢原因分析[J].连铸,2021(3):40.
|
[13] |
季德静,李春阳,苏家男.SS400钢薄板坯连铸生产典型漏钢原因分析和控制[J].中国冶金,2015,25(1):41.
|
[14] |
杨学雨,郑立允.薄板坯连铸结晶器捞渣操作对漏钢的有效控制[J].连铸,2021(1):70.
|
[15] |
徐伟,赵建平,王帅,等.快换浸入式水口时板间漏钢的原因分析及控制措施[J].连铸,2019(4):6.
|
[16] |
YANG J A, CUI H A, ZHANG J A, et al. Interfacial reaction between high-Al steel and CaO-Al2O3-Based mold fluxes with different CaO/Al2O3 ratios at 1 773 K (1 500 ℃)(article)[J]. Metallurgical and Materials Transactions B, 2019,50(6):2636.
|
[17] |
KIM M, PARK M, KANG Y Y P A. A reaction between high Mn-high Al steel and CaO-SiO2-type molten mold flux: reduction of additive oxide components in mold flux by Al in steel[J]. Metallurgical and Materials Transactions B, 2019,50(5):2077.
|
[18] |
黎江玲.高铝钢连铸保护渣的物理化学研究[D].北京:北京科技大学,2016.
|
[19] |
WANG Q, SUN M, QIU S, et al. Study on mold slag with high Al2O3 content for high aluminum steel[J]. Metallurgical and Materials Transactions B, 2014,45(2):540.
|
[20] |
张磊,张鹏,冯飞,等.板坯卷渣的机理及控制措施[J].山西冶金,2023,46(1):225.
|
[21] |
刘建伟.钢中氢对连铸的影响及预防[J].连铸,2010(4):13.
|
[22] |
刘亮,张炯明,杜晓建,等.氢含量对304不锈钢连铸过程中传热的影响[J].铸造技术,2014,35(7):1516.
|
[1] |
LUO Sen, ZHU Miaoyong. State of art on solidification characteristics and continuous casting process of high manganese steel[J]. Iron and Steel, 2023, 58(9): 39-58. |
[2] |
LIU Chengjun, QI Jie, JIANG Maofa. Design and application of new mold flux for high-Al steel continuous casting[J]. Iron and Steel, 2023, 58(9): 116-126. |
[3] |
ZHENG Yihao1,2,QI Jie1,2,ZHENG Xiang1,2,LIU Chengjun1,2,JIANG Maofa1,2. Dissolution behavior of CeAlO3 in mold fluxes with different w(CaO)/w(Al2O3)[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2023, 35(9): 1092-1099. |
[4] |
WU Xiaoxiao, XI Zaihui, HE Shengping, WANG Qiangqiang, ZHANG Xubin. Exploration of Li2O reduction by mold flux for high quality low carbon steel slab continuous casting[J]. Iron and Steel, 2023, 58(8): 110-119. |
[5] |
SUN Yuqiu, WANG Min, ZHAO Jiaqi, JIANG Luheng, BAO Yanping. Influence of non-uniform corrosion of refractory material in SEN wall on flow-field of bloom[J]. CONTINUOUS CASTING, 2023, 42(6): 25-35. |
[6] |
QI Jie, ZHANG Jianghao, LIU Chengjun. Effect of different flux raw material types on physical and chemical properties of CaO-Al2O3 based mold fluxes[J]. CONTINUOUS CASTING, 2023, 42(6): 49-54. |
|
|
|
|