| Effect of casting speed on solidification structure and carbon segregation of 40CrA bloom |
| SHEN Kunrui1, WANG Chen1, WANG Chao2, ZHOU Wenhao3, YANG Wenzhi3, CHEN Botao3, LIU Qing1 |
1. School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing, Beijing 100083,China;
2. School of Advanced Engineers, University of Science and Technology Beijing, Beijing 100083, China;
3. Xiangtan Iron and Steel Co., Ltd., Hunan Valin, Xiangtan 411101, Hunan,China |
|
|
|
|
Abstract The celluar automation finite element(CAFE) model and solidification heat transfer mathematical model were established to improve the problem of carbon segregation in the current continuous casting conditions of 40CrA bloom. And the influence of casting speed change on the solidification structure and microstructure of the bloom was studied. The simulation results show that, when the casting speed is 0.55 m/min, CET(columnar crystal structure to equiaaxial crystal transformation) starts from 69 mm away from the surface of the casting blank and ends at 122 mm away from the surface of the casting blank. When the casting speed is 0.59 m/min, the density of columnar crystal and equiaxed crystal is best. Combined with the industrial test, the results show that when the casting speed increases from 0.55 m/min to 0.59 m/min, the range of carbon segregation index decreases from 0.15 to 0.10, the fluctuation range decreases by 33.3%, the distribution of carbon content is more uniform, and the quality of billet is obviously improved.
|
|
Received: 13 April 2023
|
|
|
|
| [1] |
左小坦, 陈永峰, 张洪彪, 等. 连铸工艺参数对40Cr圆坯碳偏析的影响[J]. 中国冶金, 2020, 30(6): 97.
|
| [2] |
CHATTERJEE D, MAZUMDAR D, PATIL S P. Physical and mathematical modeling of two-phase flows in a hollow jet nozzle[J]. Metallurgical and Materials Transactions B, 2007, 38(5): 819.
|
| [3] |
AYATA K, MORI T, FUJIMOTO T, et al. Improvement of macrosegregation of ingots and continuously cast bloom and billet by electromagnetic stirring[J]. Transactions of the Iron and Steel Institute of Japan, 1984, 24(11): 931.
|
| [4] |
NURI Y, OHASHI T, HIROMOTO T, et al. Solidification microstructure of ingots and continuously cast slabs treated with rare earth metal[J]. Tetsu-to-Hagane, 1980, 66(6): 618.
|
| [5] |
李道明, 罗衍昭, 王顺玺. 基于元胞自动机有限元法对方坯凝固组织的数值模拟[J]. 钢铁研究学报, 2012, 24(12): 17.
|
| [6] |
孙涛, 岳峰, 郭春, 等. 连铸工艺参数对大圆坯凝固组织影响的数学模拟[J]. 炼钢, 2015, 31(6): 23.
|
| [7] |
温巨文, 朱立光, 张元杰, 等. 基于CAFE法对连铸坯凝固组织模拟及影响因素研究[J]. 铸造技术, 2017, 38(11): 2683.
|
| [8] |
田陆, 包燕平, 黄郁君. 凝固组织对连铸板坯中心偏析的影响[J]. 北京科技大学学报, 2009, 31(增刊1): 164.
|
| [9] |
陈伟, 常新年, 杨改彦, 等. 不同拉速对薄板坯凝固过程及组织的影响[J]. 炼钢, 2022, 38(1): 56.
|
| [10] |
李颇, 范宇静, 张程, 等. 拉速波动对GCr15轴承钢250 mm×280 mm连铸坯内部质量的影响[J]. 特殊钢, 2017, 38(5): 22.
|
| [11] |
叶玉奎, 姚骋, 刘宇, 等. 大方坯轴承钢GCr15凝固传热数值模拟[J]. 连铸, 2020(6): 15.
|
| [12] |
HAN Y S, YAN W, ZHANG J S, et al. Comparison and integration of final electromagnetic stirring and thermal soft reduction on continuous casting billet[J]. Journal of Iron and Steel Research International, 2020, 28(6): 160.
|
| [13] |
王兴宇, 韩延申, 刘青, 等. 末端电磁搅拌对弹簧钢连铸坯内部质量的影响[J]. 钢铁, 2020, 55(5): 59.
|
| [14] |
HAN Y S, YAN W, ZHANG J S, et al. Optimization of thermal soft reduction on continuous-casting billet[J]. ISIJ International, 2020, 60(1): 106.
|
| [15] |
杜肖臣, 刘青, 张江山, 等. 喷淋水量分布对C38 N2钢大方坯冷却效果的影响[J]. 中国冶金, 2022, 32(5): 93.
|
| [16] |
韩延申, 张江山, 邹雷雷, 等. 喷嘴喷淋距离对连铸小方坯二冷均匀性的影响[J]. 工程科学学报, 2020, 42(6): 739.
|
| [17] |
朱定华, 王慧胜, 刘青, 等. 连铸喷嘴冷却检测系统研发与应用[C]//2021年全国炼钢-连铸生产技术会暨连铸学术年会. 柳州: 中国金属学会, 2021: 605.
|
| [18] |
HOU Z, JIANG F, CHENG G. Solidification structure and compactness degree of central equiaxed grain zone in continuous casting billet using cellular automaton-finite element method[J]. ISIJ International, 2012, 52(7): 1301.
|
| [19] |
NASTAC L, STEFANESCU D M. Stochastic modelling of microstructure formation in solidification processes[J]. Modelling and Simulation in Materials Science and Engineering, 1997, 5(4): 391.
|
| [20] |
GANDIN C, DESBIOLLES J, RAPPAZ M, et al. A three-dimensional cellular automation-finite element model for the prediction of solidification grain structures[J]. Metallurgical and Materials Transactions A, 1999, 30(12): 3153.
|
| [21] |
景财良, 许志刚, 王郢, 等. 72A帘线钢小方坯凝固组织的CAFE法模拟[J]. 铸造技术, 2011, 32(6): 849.
|
| [22] |
白雪松, 李曜光, 孙彦辉, 等. C72DA高碳钢小方坯凝固组织模拟[J]. 炼钢, 2020, 36(4):60.
|
| [23] |
KURZ W, GIOVANOLA B, TRIVEDI R. Theory of microstructural development during rapid solidification[J]. Acta Metallurgica, 1986, 34(5): 823.
|
| [24] |
雷洪, 张红伟, 陈宏豫, 等. 铁碳合金凝固过程微观溶质偏析模型分析[J]. 材料与冶金学报, 2011, 10(2): 104.
|
| [25] |
虞觉奇. 二元合金状态图集[M]. 上海: 上海科学技术出版社, 1987.
|
| [26] |
陈家祥. 钢铁冶金学—炼钢部分[M]. 北京: 冶金工业出版社, 2004.
|
| [27] |
李文超. 冶金与材料物理化学[M]. 北京: 冶金工业出版社, 2001.
|
| [28] |
曾杰, 陈伟庆, 曹长法, 等. 轻压下对82B钢矩形坯内部质量的影响[J]. 炼钢, 2015, 31(4): 637.
|
| [29] |
李翔, 白雪松, 孙彦辉. 轴承钢大方坯凝固组织模拟[J]. 工业加热, 2021, 50(2): 27.
|
| [30] |
吕明, 米小雨, 张朝晖, 等. 连铸工艺参数对SWRH82B高碳钢碳偏析的影响[J]. 工程科学学报, 2020, 42(增刊1): 102.
|
| [1] |
KANG Yonglin, ZHU Guoming, CHEN Guijiang, QIN Zhe. Latest development of wide thin strip endless rolling technology in China[J]. Iron and Steel, 2023, 58(7): 1-8. |
| [2] |
SUN Yuqiu, WANG Min, ZHAO Jiaqi, JIANG Luheng, BAO Yanping. Influence of non-uniform corrosion of refractory material in SEN wall on flow-field of bloom[J]. CONTINUOUS CASTING, 2023, 42(6): 25-35. |
| [3] |
LI Xuekai, ZHANG Yanchao, ZHANG Caijun, XIAO Pengcheng, ZHU Liguang. Influence of electromagnetic braking on metallurgical behavior in thin plate crystallization[J]. Iron and Steel, 2023, 58(6): 72-81. |
| [4] |
XIANG Hongxue, HAN Limin, XIA Fangyong, WU Guoping. Development and application of heat flux model of high casting speed billet mould[J]. CONTINUOUS CASTING, 2023, 42(5): 21-27. |
| [5] |
WANG Changjun, LIU Zhongqiu, LI Baokuan. Effect of switching period of SEMS on central equiaxed crystal ratio of thin steel slabs[J]. CONTINUOUS CASTING, 2023, 42(5): 64-70. |
| [6] |
YANG Hong, SONG Yi, XIAO Yan, XIA Songqing, XIAO Xiaodan, XIAO Hong. Effect of electromagnetic rotating stirring of traveling wave magnetic field on molten steel metallurgical behavior in mold of slab casting[J]. CONTINUOUS CASTING, 2023, 42(5): 71-79. |
|
|
|
|
2023, Vol. 42 