Discussion about CuO doping on microstructure and properties of Ni 0.4 Zn 0.6 Fe 2 O 4 ferrite
FAN Xiu-feng 1, YAN Yong-wang 2,LIU Su-xia 1, LUO Long 1, LI Xiao-wei 1, HUO Wen-xia 1
1. Analytical and Testing Center, Inner Mongolia University of Science and Technology, Baotou 014010, China;
2. School of Material and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010, China
Ni 0.4-x Cu x Zn 0.6 Fe 2 O 4(x=0, 0.12, 0.20, 0.28) ferrite was prepared by the traditional ball milling method. The microstructure, phase composition and magnetic properties of Ni-Zn ferrite with CuO doping on were investigated by scanning electron microscope (SEM), X-ray diffraction (XRD), comprehensive thermal analysis (TG-DSC) and vibrating sample magnetometer (VSM). The results showed that with the increase of CuO content, the second phase of Ni-Cu-Zn ferrite was formed, and the diffraction peak intensity of Ni-Cu-Zn ferrite gradually increased. It could be seen from the microstructure and energy spectrum that Cu 2+ participated in the reaction of ferrite. The increase of CuO content improved the sintering performance of the sample, and reduced the crystallization temperature of Ni-Cu-Zn ferrite. The hysteresis loop showed soft magnetic properties of Ni 0.4- x Cu x Zn 0.6 Fe 2 O 4 (x=0, 0.12, 0.20, 0.28). When the CuO content x was 0.2, the saturation magnetization (Ms) of ferrite was highest. Meanwhile, the coercive force (H c) was relatively low.
范秀风, 闫永旺, 刘素霞, 罗 龙, 李晓伟, 霍文霞. CuO掺杂Ni0.4Zn0.6Fe2O4铁氧体的组织与性能探讨[J]. 物理测试, 2020, 38(3): 13-.
FAN Xiu-feng, YAN Yong-wang, LIU Su-xia, LUO Long, LI Xiao-wei, HUO Wen-xia. Discussion about CuO doping on microstructure and properties of Ni 0.4 Zn 0.6 Fe 2 O 4 ferrite. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 13-.