Detection of semicoke in pulverized coal by combined coal petrography polarizing microscope and thermogravimetric analyzer |
ZHOU Jun-lan��DU Ping��LEI Ming |
Research Institute�� Iron and SteelShasteel�� Zhangjiagang 215625�� China |
|
|
Abstract The microstructure of pulverized coal was observed by coal petrography microscope. It was found that there were impurities with different structure and morphology from coal. In order to identify the impurities�� the thermogravimetric analysis and polarizing structure analysis of sample were conducted. The reflectance value was measured using coal petrography analyzer and spectrophotometer. The results showed that the DTG curve exhibited two distinctively different peaks�� indicating the presence of impurities. The polarizing structure of impurities was similar to the isotropy of coke. The comparison with semicoke standard sample revealed that the both interference lights were Level-1 red. The average reflectance value of impurities was about 4.6�� which was much higher than the vitrinite reflectance of pulverized coal. The comprehensive characterizations proved that the impurities were semicoke.
|
Received: 09 October 2015
Published: 06 June 2016
|
|
|
|
[1] |
ZHAO Lei,,GONG Zhi-jun,,WU Wen-fei,. Emission rule of HCN and NOx from semi-coke combustion process in fixed-bed[J]. Chinese Journal of Iron and Steel, 2017, 29(5): 352-356. |
[2] |
GONG Zhi-jun,,YANG Biao,,LI Bao-wei,,WU Wen-fei,. NO release characteristic of semi-coke in isothermal combustion process[J]. Chinese Journal of Iron and Steel, 2016, 28(12): 5-8. |
[3] |
HE Xuan-ming, FU Peng-rui, WANG Chun-xia, LIN Hong-tao, WU Shuo, CAO Shi-xin. Combustion Behavior of Low Rank Coal Char Application in Blast Furnace Injection[J]. Chinese Journal of Iron and Steel, 2014, 49(9): 92-97. |
[4] |
. The Research on Optimum Process Conditions of Activated Coke Prepared by Semi-coke Powder for Sintering Flue Gas Desulfurization[J]. Chinese Journal of Iron and Steel, 2010, 22(05): 11-11. |
|
|
|
|