| Cause analysis of cracking of 40CrNiMo steel shaft |
| ZHANG Quan-xin， ZHU Bin， XU Hong-hao， CAO Zheng-kuan |
| Chongqing Iron and Steel Research Institute Co.， Ltd.， Chongqing 400084， China |
|
|
|
Abstract The causes of cracking of 40CrNiMo steel shaft was analyzed and discussed based on chemical composition analysis， hardness testing and metallographic structure inspection as well as fracture morphology observation. Moreover， the improvement measures were proposed. The results showed that the serious segregation of banded structure in the center of the steel shaft was the main reason for the cracking. The upper bainite formed in quenched-tempered heat treatment process further reduced the properties of material， which accelerated the formation and propagation of cracks.
|
|
Received: 20 August 2019
|
|
|
|
| [1] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
| [2] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
| [3] |
FENG Lu-lu1,2,WU Kai-ming1,3,YU Hong-wei4,ZHAO Hua-zhong5. Production status and developing tendency of high strength and toughness steel for hydropower station[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 175-185. |
| [4] |
GAN Gui-ping,YE Jiang,FAN Lei. Effect of tempering treatment on microstructure and low temperature toughness of a low carbon bainite steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 258-264. |
| [5] |
ZHAO Hai-sheng，ZHU Hai-feng. Causes analysis of cold bending cracking of Q195 hot rolled strip[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 36-. |
| [6] |
XIA Bing，CHEN Bin，HOU Zong-bao，ZHAO Zhi-hai. Cause analysis of cold bending cracking of Q235B H-beam steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 45-. |
|
|
|
|
2020, Vol. 38 