Analysis of abnormal fracture in tension of wire rod |
CHENG Ya-nan, CHEN Bin, JIANG Jin, HOU Zong-bao, WANG Yan-yang, QIAN Wen |
Testing Center, Maanshan Iron and Steel Co., Ltd., Ma'anshan 243000, China |
|
|
Abstract In order to investigate the reason why the wire rod sample was broken at the root of fixture during the tensile test, and to avoid the occurrence of this phenomenon which affected the testing results, the simulation test and production application were carried out. The results showed thatthe wire rod sample would be broken at the root of fixturewhen the clamping part of sample did not meet the requirement that the clamping length was at least 3/4 of the fixture length. As a result, the tensile strength would be lower. Moreover, it would affect the measurement of reduction of area and elongation after fracture, resulting in unqualified testing results and invalid data.On the premise of ensuring the coaxiality of upper and lower clamps as well as proper clamping force, the tensile tests were conducted by varying the clamping length of sample.The problem that the wire rod sample was broken at the root of fixture in tensile test was finally solved.
|
Received: 06 June 2019
|
|
|
|
[1] |
XIAO Shao-bin, WANG Wei, LIU Tian-yu, ZHANG Qin, LÜ Zhi-qing. Effects of vacancies and C atoms on mechanical properties of Fe grain boundary[J]. Iron and Steel, 2020, 55(4): 75-81. |
[2] |
. Research on Microstructure and Properties of CMT Welding Joints of Austenitic Stainless Steel[J]. , 2019, 44(6): 0-0. |
[3] |
SHEN Bin-bin. Discussion about the thermoplasticity of vanadium microalloyed steel[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(5): 9-11. |
[4] |
XIAO Juan,YUAN Qin-pan,PAN Gang,MENG Yue-rui. Effect of single-side thinning on the elongation after fracture of Q420B thick plate[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(4): 14-16. |
[5] |
XU Ting-dong,WANG Min-qing,HE Hui-min. Mechanical property-tensil estrain rate curve of metals[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(2): 54-59. |
[6] |
WANG Lin-feng1,2, ZHOU Li-chu1, CHEN Hua-qing2, HU Xian-jun3, . Manufacturing technology,microstructural and mechanical properties of ?5.35 mm-2 100 MPa grade hot galvalume steel wire for bridge cable[J]. Iron and Steel, 2019, 54(2): 90-96. |
|
|
|
|