| Fracture cause analysis of wire rope for automobile crane |
| LI Lushui,LIU Kexiu,LIU Zhaojie,MA Kuo,WANG Lian,FENG Xiaoliang |
| Guangzhou Special Pressure Equipment Inspection and Research Institute, Guangzhou 510663, China |
|
|
|
| Guide |
|
|
Abstract When a automobile crane at a construction site was used for lifting the steel reinforcements, the fracture of wire rope connected to the auxiliary hook occurred. Through macro analysis, dimensional measurement, breaking force tensile test, metallographic analysis, scanning electron microscope morphology observation and energy spectrum analysis, the technical reasons for wire rope fracture were analyzed. The results showed that the outer wire of the automobile crane wire rope had severe wear with local broken wires and cracking. The number of local broken wires had exceeded the scrapping standard in GB/T 5972—2016, resulting in the fracture of wire rope due to insufficient local bearing capacity.
|
|
Received: 15 March 2021
|
|
|
|
|
|
| [1] |
WANG Tao1,2， HU Feng1,2,3， ZHOU Wen1,2,3， YIN Chaochao1,2， KE Rui1,2， WU Kaiming1,2,3 . Effect of impact load on wear resistance of 10Mn steel and analysis of wear resistance mechanism [J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(5): 478-488. |
| [2] |
CHANG Guodong,WU Min. Failure analysis of tube bundle of coal moisture control steam rotary dryer in a coking plant [J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(2): 53-56. |
| [3] |
ZHU Jiao,ZHONG Zhenqian,YU Xueliang,LI Jie. Cause analysis of bolt fracture[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(2): 57-63. |
| [4] |
SHAO Jianping. Cracking analysis of longitudinal beam wing surface of high strength automobile beam steel[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(1): 39-. |
| [5] |
ZHU Jiao,ZHONG Zhenqian,ZHAI Zhanjiang,YU Xueliang. Failure analysis of blade cracking[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(1): 46-. |
| [6] |
LI Chengru1，DENG Xiangtao1，LIANG Liang1,2，LIU Hongyan1,3，WANG Zhaodong1. Study on microstructure, properties and high temperature wear behavior of a novel high temperature wearresistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2021, 33(8): 862-870. |
|
|
|
|
2022, Vol. 40 