Effect of holding time at 850 ℃ on intergranular oxidation layer of 15CrMo steel |
SHI Xuexing,JU Xinhua,YAN Chunlian,WEN Juan |
Technical Research Institute of Shougang Group Co., Ltd., Beijing 100043, China |
|
|
Abstract The effect of holding time at 850 ℃ on intergranular oxidation layer was studied by scanning electron microscope (SEM) and electron probe. The results showed that with the increase of holding time, the oxide scale thickness of the outer layer of 15CrMo steel increased gradually, but the intergranular oxidation depth increased first and then tended to be stable. When the holding time was 30 min, the intergranular oxidation depth was about 13 μm. When the time increased to 120 min, the intergranular oxidation depth was about 17 μm and tended to be stable. The alloying elements including Mn, Cr and Si were enriched obviously in the location of intergranular oxidation. Moreover, the grain boundaries were coarsened and the quantity of oxide points in the grains increased.
|
Received: 24 November 2021
|
|
|
|
[1] |
ZHANG Jie, KONG Ning, WANG Yi-bo, SONG Yu-wei. Quantitative evaluation and analysis on spalling of powdered iron oxide scale for automobile beam steel[J]. Iron and Steel, 2023, 58(1): 125-132. |
[2] |
ZHANG Qi, MI Zhenli, ZHU Rong, WANG Mai, WU Yanxin, LI Lei. EBSD sample preparation and characterization method of oxide scale on the surface of hot-rolled steel strip[J]. PHYSICS EXAMINATION AND TESTING, 2023, 41(1): 21-24. |
[3] |
CAO Guang-ming, SHAN Wen-chao, LIU Xiao-jiang, WANG Chen-yang. High temperature oxidation behavior of Fe-2.2%Si steel in different atmosphere[J]. Iron and Steel, 2022, 57(8): 132-142. |
[4] |
MA Cong,WANG Yongguo,LIU Yang,WU Shengfu,GU Hairong,CUI Lei. Control and improvement of oxide scale on the surface of hotrolled highstrength steel[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(5): 1-. |
[5] |
WANG En-rui, CHEN Zi-gang, LIU Feng-lin, LIU Tian-wu, ZHANG Ming. Oxide scale structure of hot rolled structural steel and its effect on pickling quality[J]. Iron and Steel, 2022, 57(3): 71-78. |
[6] |
ZHAO Li-jie, ZHANG Fang, PENG Jun, CHANG Hong-tao, MING Shou-lu, ZHU Rui-zong. Chemical composition and pore control of porous stainless steel prepared by rolling steel skin[J]. Iron and Steel, 2022, 57(1): 133-142. |
|
|
|
|