Cause analysis of flaw detection unqualified of 4130X continuous casting open cast furnace steel pipe |
ZHANG Xinwen1, SHI Jiakai2, ZHANG Chunxiang1, CHEN Kai1, XUAN Kangle1 |
1. Special Steel Company, Jiangsu Yonggang Group Co., Ltd., Suzhou 215628, China; 2. Product R & D Center, Jiangsu Yonggang Group Co., Ltd., Suzhou 215628, China |
|
|
Abstract It pointed out that the reason for flaw detection unqualified of 4130X steel pipe was the nonmetallic inclusions caused by secondary oxidation of open cast furnace. Take ø500 mm continuous casting blank as the object, several samples were taken from different positions of the casting blank. It was found that the oxygen content, nitrogen content, Al loss and nonmetallic inclusions in the steel in the open casting part were higher than those in other parts, which implied that the secondary oxidation in the open casting part was more serious. In addition, the nearlier to open casting part the quantity and distribution density of inclusions with length more than 5 μm. It is indicated that the effect of secondary oxidation on inclusions more then 5 μm is obviously when open casting.
|
Received: 14 March 2022
|
|
|
|
[1] |
李刚,丁文彬,张朝磊,等. 大容积无缝气瓶用4130X钢ø600 mm连铸圆坯研发[J]. 特殊钢,2022,43(1):45.
|
[2] |
李尚兵,张新文,薛伟江. 高压气瓶用钢4147 ø50 mm连铸圆坯的生产实践[J]. 特殊钢,2006,37(1):48.
|
[3] |
郝国旺,郝国胜. 提升高压气瓶钢质量的工艺改进探索[J]. 机械工程与自动化,2006(6):159.
|
[4] |
武常生,暴志强,朱海鹰.天然气长管拖车气瓶用材料介绍[J].中国化工装备,2008,10(1):124.
|
[5] |
郭萌锋. 大容积钢质无缝气瓶致脆风险的防范措施[J]. 科技视界,2014(31):100.
|
[6] |
练勇,王子砚,刘杰慧. ø559×17拖车气瓶用无缝钢管的开发[J]. 化学工程与装备,2014(1):114.
|
[7] |
蔡开科,程士富. 连续铸钢原理与工艺[M]. 北京:冶金工业出版社,2008.
|
[8] |
董孟宪,杨小青,刘玉爱,等. 37Mn5钢管内壁分层缺陷分析与改进[J].金属加工,2021(2):80.
|
[9] |
袁方明,王新华,李宏,等. 不同浇铸阶段IF钢连铸板坯洁净度[J]. 北京科技大学学报,2005,27(4):436.
|
[10] |
曹磊,王玉民,丁中,等. 开浇第一炉连铸坯夹杂物形成原因与控制措施[J]. 中国冶金,2014,24(2):10.
|
[11] |
崔衡,岳峰,包燕平,等. IF钢连铸头坯洁净度研究[J]. 钢铁,2010,45(3):39.
|
[12] |
付常伟. Q345BHE900MH型钢脆性断口分析及工艺优化[J]. 物理测试,2018,36(5):29.
|
[13] |
李晶. LF精炼技术[M]. 北京:冶金工业出版社,2009.
|
[14] |
郭洛方,王时松,张小伟,等. Al2O3夹杂物碰撞凝聚长大数值模拟新方法[J]. 物理测试,2015,33(4):53.
|
[15] |
杨克枝,常正昇,郭俊波.开浇前中间包充氩对中碳铝镇静钢钢水洁净度的影响研究[J].河南冶金,2021,29(3):12.
|
[16] |
曹晶,杨文,王新华,等. 低碳铝脱氧钢连铸开浇阶段钢中非金属夹杂物的变化[J]. 钢铁,2011,46(6):38.
|
[1] |
JIAO Ao-teng, YANG Shu-feng, LI Jing-she, SONG Jing-ling, LI Heng-hua, ZHANG Fu-jun. Evolution of inclusions in 26CrMo7S steel produced by EAF-LF-VD-CC process[J]. CONTINUOUS CASTING, 2023, 42(2): 28-33. |
[2] |
SONG Bao-min, SHI Shu-guang, LIU Kun-long, LÜ Ming. Formation and evolution of nonmetallic inclusions in 27SiMn steel[J]. CONTINUOUS CASTING, 2023, 42(2): 57-62. |
[3] |
Lei Cao, Li-guang Zhu, Zhi-hong Guo. Research status of inclusions in bearing steel and discussion on non-alloy deoxidation process[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2023, 30(1): 1-20. |
[4] |
CHENG Ri-jin, QI Zhan, ZHANG Hua, LIU Cheng-song, NI Hong-wei. Optimization of refining slag of 20SiMn alloy structural steel[J]. Iron and Steel, 2023, 58(1): 100-107. |
[5] |
ZHANG Yulei1,ZHUO Chao1,HAO Xiaoshuai1,LIU Tian1,SUN Yanhui1,ZHANG Min2. Effect of sulfur content on nonmetallic inclusions of heavy rail steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(8): 799-806. |
[6] |
ZENG Yi-bin, BAO Yan-ping, ZHAO Jia-qi, WANG Min. Formation and evolution of magnesia-alumina spinel in Si-Mn deoxidized 55SiCr spring steel[J]. Iron and Steel, 2022, 57(8): 69-77. |
|
|
|
|