| Analysis of hole defect of 2219 aluminum alloy ring |
| GONG Zhongxing, ZHANG Zheng, WANG Panzhi, XIANG Chunhua |
| Guizhou Aviation Technical Development Co., Ltd., Guiyang 550081, China |
|
|
|
|
Abstract During the inspection of 2219 ring forgings, it was found that there were defects inside, which were about 5 mm from the inner diameter and 80 mm from the end face. The flaw detection showed that the defects were long strips with the length of about 30 mm, and the direction was parallel to the diameter direction of the forgings. In order to analyze the causes of the defects, the macrostructure, microstructure, scanning electron microscopy and energy spectrum analysis of the defective samples were studied in the laboratory. The results showed that the defects of 2219 aluminum alloy ring forging were hole defects, which were caused by the low AlZr input temperature during smelting. It reduced the diffusion rate of elements and increased the segregation of AlZr alloy phase, leading to the formation of hole defects.
|
|
Received: 20 June 2022
|
|
|
|
| [1] |
李学朝. 铝合金材料组织与金相图谱[M].北京:冶金工业出版社,2010.
|
| [2] |
肖亚庆,谢水生,刘静安,等.铝加工实用技术手册[M].北京:冶金工业出版社,2005.
|
| [3] |
林钢,林慧国,赵玉涛. 铝合金应用手册[M]. 北京:机械工业出版社,2006.
|
| [4] |
铝合金镁合金《中国航空材料手册》编辑委员会.中国航空材料手册[M].第3卷.2版.北京:中国标准出版社,2001.
|
| [5] |
张晓清,吴睿,宋体杰. 铝合金锻件线性缺陷分析[J].失效分析与预防,2014,9(4):247.
|
| [6] |
张晓霞. 变形铝合金产品粗大金属间化合物缺陷超声波探伤[J].无损探伤,2011,35(5):46.
|
| [7] |
孙荣滨. 铝合金结构件化合物偏聚缺陷超声波探伤方法[J].轻金属,2009(9):53.
|
| [8] |
谢优华,杨守杰,戴圣龙,等.锆元素在铝合金的应用[J].航空材料学报,2002,22(4):56.
|
| [9] |
Hideo Yoshida, Yoshio Baba.The role of zirconium to improve strength and stress-corrosion resistance of Al-Zn-Mg and Al-Zn-Mg-Cu alloys[J]. Transaction of the Japan Institute of Metals, 1982,23(10):620.
|
| [1] |
ZHANG Xueling,LI Maolin. nalysis of unqualified causes of generator yoke Q345C heavy and wide plate[J]. PHYSICS EXAMINATION AND TESTING, 2022, 40(6): 41-. |
| [2] |
WANG Wei,ZHAO Sixin,GAO Jiaqiang. Hole analysis of Y15 freecutting steel and its precautions[J]. PHYSICS EXAMINATION AND TESTING, 2021, 39(2): 50-. |
| [3] |
SANG Sheng-feng，WEN Yang，LIU Xue-liang，KE Yu-jun，ZHANG Jian-cheng，SUN Jian-shuang. Inspection and treatment of raw material defects in Shougang Jingtang 1420 pickling line-tandem cold mill[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 13-. |
| [4] |
HOU Zhi-peng，ZHANG Shu，ZHANG Peng，YAN Xiao-hong，YANG Mao-sheng. High temperature creep damage behavior of a novel Co-Cr-Mo-Ni alloy[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(7): 683-688. |
| [5] |
LIN Huan, YANG Maosheng, SHU Baipo, LI Jianxin, LUO Zhiqiang. High temperature rotating bending fatigue behavior and damage mechanism of high nitrogen stainless bearing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(5): 475-484. |
| [6] |
YANG Dai-jun，ZHANG Wen-xue，WANG Dao-hu，XU Kun-he，ZHANG Man-man，ZHANG Jing. Analysis of the microstructure and mechanical properties of 9 m diameter 2219 aluminum alloy ring[J]. , 2018, 36(2): 10-16. |
|
|
|
|
2023, Vol. 41 