Cause analysis on upset forging cracking of 35CrMoA round steel |
LI Fengde |
Fujian Sangang Group Co., Ltd., Sanming 365000, China |
|
|
Abstract Aiming at the unqualified batch cracking of upset of 35CrMoA hot-rolled round steel produced by a factory, some detection methods including optical microscope, scanning electron microscope and energy disperse spectroscopy were employed to analyze the reasons for cracking. The results showed that the main reason for upset cracking was the existence of large inclusions in the base metal, which were mainly from the slag in smelting and continuous casting process. By improving the purity of steel, optimizing the LF refining process, increasing the viscosity of the mold slag, and optimizing the flow field in crystallizer, the inclusion content in 35CrMoA round steel could be effectively reduced. Consequently, the qualification rate of upset forging of the round steel was improved.
|
Received: 13 July 2022
|
|
|
|
[1] |
刘勇,冯媛媛,刘鑫,等. 淬火保温时间对35CrMo钢调质性能的影响[J]. 石油和化工设备,2021,24(5):50.
|
[2] |
冯学东,凌有临,李惠,等. 强韧化工艺对35CrMo钢组织与性能的影响[J]. 金属热处理,2018,43(1):78.
|
[3] |
张全新,朱斌,徐鸿昊,等. 40CrNiMo钢轴开裂原因分析[J]. 物理测试,2020,38(2):32.
|
[4] |
齐晓峰. 热轧圆钢热顶锻裂纹原因分析[J]. 中国冶金,2019,29(6):59.
|
[5] |
杜顺林,吴光耀,曹重,等. 中宽带冷弯裂纹成因分析及改进措施[J]. 物理测试,2020,38(6):43.
|
[6] |
罗衍昭,焦会立,庞在刚,等. 热轧工艺对超低碳IF钢卷渣和面翘皮缺陷的影响[J]. 钢铁,2015(5):44.
|
[7] |
刘岩,张聪毅,潘恒沛,等. 某轴承外圈滚道裂纹分析[J]. 物理测试,2021,39(6):44.
|
[8] |
郗雄涛,王志义,王红军. 冷镦钢线材表面微折叠缺陷原因分析及改进措施[J]. 轧钢,2020,37(1):94.
|
[9] |
李亚红,盛春翔,周旭旭,等. 20CrMnTi钢锻件拉伸性能不合格原因分析[J]. 物理测试,2022,40(2):31.
|
[10] |
杜海明,费新刚,张静. 42CrMo锚栓断裂分析[J]. 物理测试,2020,38(1):49.
|
[11] |
李向龙,冯胜强,张志宵. 连铸坯拉速对结晶器卷渣现象的影响[J]. 连铸,2022(2):100.
|
[12] |
薛月凯,田宝生,王杰文,等. 连铸机高拉速下钢液卷渣控制措施[J]. 华北理工大学学报,2020,42(2):14.
|
[1] |
SONG Guangjie, ZHU Haoran, JI Dengping, LIU Bin, FU Jianxun. Analysis of inclusions and carbides in 102Cr17Mo bearing steel billet[J]. Iron and Steel, 2023, 58(8): 157-168. |
[2] |
LIANG Zhanlei,LI Tao,HAN Qiang,XU Tao,BAI Yansong,SUN Zhaoqi. Study on CO2 corrosion resistance of rare earth Ce to 5Cr steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2023, 35(7): 881-888. |
[3] |
WANG Ju, LI Yang, JIANG Zhouhua, SUN Meng, MAO Yunqie, MA Shuai. Inclusion transformation mechanism of AISI 431 stainless steel during production[J]. Iron and Steel, 2023, 58(7): 54-63. |
[4] |
YU Zheng, REN Ying, REN Qiang, ZHANG Lifeng. Effect of magnesium on inclusions and austenite grain in a GCr15 bearing steel[J]. Iron and Steel, 2023, 58(7): 133-143. |
[5] |
MENG Yaoqing1,2,LI Jianli1,2,XU Qi1,2,WANG Kunpeng3. A potential source of forsterite inclusion in Sikilled spring steel 55SiCr[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2023, 35(6): 712-719. |
[6] |
LÜ Ming, LIU Kunlong, GAO Zhizhe, SONG Baomin, ZHANG Zhaohui. Inclusion characteristics and control process optimization of 27SiMn steel[J]. Iron and Steel, 2023, 58(6): 61-71. |
|
|
|
|