Drop hammer tear test and pendulum impact test of pipeline steel |
SHAN Xianfei, LEI Na, ZHAO Naisheng, YANG Yanlong, ZHANG Longhui |
Quality Inspection Department,Beijing Shougang Co., Ltd., Qian′an 064400, China |
|
|
Abstract The performance of drop hammer tear test and pendulum impact test of pipeline steel are two important parameters of materials, which can help determine the safety and reliability of materials or products. Two pipeline steel samples with different specifications and different properties were used to perform drop hammer tear test and Shaabi pendulum impact test at different temperatures. The impact shear section rate and the drop hammer shear area fraction in two test methods were compared. The difference and relationship were studied based on the test results. The results showed that the change laws of impact shear section rate and the drop hammer shear area fraction were basically consistent during the temperature variation for two pipeline steel samples with different specifications and different properties in drop hammer tear test and pendulum impact test.
|
Received: 25 October 2022
|
|
|
|
[1] |
蔺卫平,李娜,王亚龙,等.落锤撕裂试验与摆锤冲击试验剪切面的对比与分析[J].焊管,2014,37(2):44.
|
[2] |
赵晓丽,罗志强,李玲霞.无塑性转变温度落锤试验和落锤撕裂试验方法介绍[J].物理测试,2011,29(6):6.
|
[3] |
陈晓林.X65M 管线钢落锤撕裂试验结果影响因素分析[J].焊管,2021,44(11):58.
|
[4] |
王勇.冲击缺口类型对34CrNi1Mo钢韧脆转变温度的影响[J].物理测试,2021,21(10):37.
|
[5] |
国家市场监督管理总局国家标准化管理委员会.GB/T 229—2020 金属材料夏比摆锤冲击试验方法[S].北京:中国标准出版社,2020.
|
[6] |
郭宏伟,王伟. 管线钢取制样技术对力学性能的影响[J].物理测试,2019,37(2):12.
|
[7] |
申延军. 高强钢冲击功分析和改善[J].物理测试,2022,40(6):33.
|
[8] |
朱姣,钟振前,于学亮,等. 螺栓断裂原因分析[J].物理测试,2022,40(2):57.
|
[9] |
中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会. GB/T 8363—2018 钢材落锤撕裂试验方法[S].北京:中国标准出版社,2018.
|
[10] |
邹鹏. 摆锤冲击吸收能量和断口测量结果的关系[J]. 理化检验(物理分册),2022,58(11):11.
|
[11] |
张峰,孙志鹏,王德宝. 海底管线钢 CTOD 性能探讨[J].物理测试,2021,39(4):10.
|
[1] |
AN Cheng- gang,,NIU Tao,,WU Xin- lang,JIANG Yong- wen,,DAI Xiao- li,. Analysis of DWTT property of thick X70 pipeline steel[J]. , 2018, 30(5): 405-410. |
[2] |
ZHAO Xiao-li,LUO Zhi-qiang,LI Ling-xia. Introduction of Test Method for Nil-Ductility Transition Temperature and Drop Weight Tear Test[J]. Chinese Journal of Iron and Steel, 2011, 29(6): 5-8. |
[3] |
LI Wenzhu;PANG Zaofu;XU Rongjie;WANG Rui;WANG Xiaofeng;SU Guoyang. Microscopical Analysis on Separation Fracture for Pipe Line Steel[J]. Chinese Journal of Iron and Steel, 2007, 25(4): 47-0. |
[4] |
YANG Zheng;CHEN Hongda;ZHAO Xinwei;GUO Wanlin;LUO Jinheng. Delamination Cracks and Fracture Evaluation in DWTT of X70 Pipeline Steel[J]. Iron and Steel, 2006, 41(10): 69-0. |
|
|
|
|