针对迁钢板坯角横裂形成的原因和影响因素等进行了系统的调查研究。结果表明脆性区弯曲矫直和外应力较大是产生角裂的根源,在此基础上采取了控制成分、保证铸机状态、二冷制度和锥度优化等相应的措施,使迁钢板坯的角裂发生率极大降低。
Abstract
Formation mechanism of slab corner cracks was investigated systematically in Qiangang. Temperature measurement of slab corner and high temperature mechanical properties tests shows that the bending and unbending in brittle zone is the main reason for slab corner cracks. Countermeasures were carried out in steel composition control, casting machine maintenances, secondary cooling optimization, and mould taper adjustment, which decreased slab corner cracks obviously.
关键词
板坯 角横裂 高温塑性 二冷水 影响因素
{{custom_keyword}} /
Key words
slab,corner cracks,hot ductility,secondary cooling,influence factors
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] 蔡开科. 连铸坯表面裂纹的控制. 鞍钢技术,2004,第3期.
[2] Hiroyuki Yasunaka, Kiminori Nakayama, Kiyoshi Ebina, et al. Improvement of Transverse Corner Cracks in Continuously Cast Hypoperitectic Slabs. 鉄と鋼, Vol.81(1995), No.9.
[3] Barrie MINTZ. The Influence of Composition on the Hot Ductility of Steels and to the Problem of Transverse Cracking. ISIJ International, Vol. 39 (1999), No. 9, p. 833-855.
[4] H. T. Tsai1, H. Yin, M. Lowry, et al. Analysis of Transverse Corner Cracks on Slabs and Countermeasures. AISTech 2005 Proceedings , Volume II,P.201-208.
[5] Shinzo HARADA, Shigenori TANAKA, Hideyuki MISUMI, et al. A Formation Mechanism of Transverse Cracks on CC Slab Surface. ISIJ International, Vol. 30 (1990), No. 4, p. 310-316.
[6] Toru KATO, Yoshiki ITO, Masayuki KAWAMOTO, et al. Prevention of Slab Surface Transverse Cracking by Microstructure Control. ISIJ International, Vol.43 (2003), No.11, p. 1742–1750.
[7] J.P. Michel and J.J. Jonas. Precipitation Kinetics and Solute Strengthening in High Temperature Austenites Containing Al and N. Acta Metallurgica, 1981, 29:513-526.
[8] 刘阳春.薄板坯连铸连轧流程氮、铝的控制及作用研究.博士学位论文.2007.
[9] W.C.Leslie, Trans., ASM, 46(1054), 1470.
[10] Y. Machara, K. Yasumoto, Y. Sugitani, et al. Effect of carbon on Hot Ductility of As-cast Low Alloy Steels. Trans. ISIJ Int., 1985, 25:1045.
[11] B.Mintz, S. Yue, et al. Hot ductility of steels and its relationship to the problem of transverse cracking during continuous casting. International Materials Reviews, 1991, 36(5):187.
[12] Nicolas Triolet, Kristof Poelmans, Pierre Mabelly, et al. Prevention of corner cracks in slab continuous casting.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}